Manufacturing method of rapidly-degraded environment-friendly corrugated board

A corrugated cardboard, rapid degradation technology, applied in special paper, chemical instruments and methods, paper/cardboard layered products, etc., can solve the problems of poor flame retardancy and low degradation speed of corrugated cardboard, so as to reduce activity and improve The effect of flame retardancy

Pending Publication Date: 2022-04-29
常熟市宏华外贸包装有限责任公司
0 Cites 0 Cited by

AI-Extracted Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a method for manufacturing a rapidly degradable environmentall...
View more

Method used

S2, mixing slurry A and polyurethane, polyvinyl amine are placed in stirring furnace together, at 20-30 degree Celsius normal temperature and 50-100 turn per minute rotating speed and stir 2-3 hour, in the process of stirring, Add ammonium chloride into the stirring furnace every half hour, finally get the mixed slurry B, and store it statically, increase the water solubility of the cardboard itself by adding polyvinylamine and polyurethane, and accelerate the degradation of silicon contained in the cardboard The separation speed is improved, and silicon is dissolved and eliminated by ammonium chloride to increase the speed of cardboard self-degradation;
S2, mixi...
View more

Abstract

The invention provides a manufacturing method of an environment-friendly corrugated board capable of being rapidly degraded, and relates to the technical field of paper product manufacturing. According to the manufacturing method of the rapidly-degraded environment-friendly corrugated board, a degradation raw material group comprises the following raw materials in parts by weight: 5-15 parts of polyurethane, 2-3 parts of polyvinylamine and 10-15 parts of ammonium chloride, and a flame-retardant raw material group comprises the following raw materials in parts by weight: 2-5 parts of aluminum nitrate, 5-10 parts of ammonium chloride, 20-30 parts of pure water, 10-15 parts of silicon monoxide and 10-20 parts of citric acid. In the stirring process, ammonium chloride is added into the stirring furnace every half an hour, the water solubility of the paperboard is improved through the added polyvinylamine and polyurethane, the degradation and separation speed of silicon contained in the paperboard is increased, and the silicon is dissolved and eliminated through the ammonium chloride; the temperature of the high-temperature stirring tank is increased to 120-130 DEG C, stirring is carried out, the obtained flame-retardant liquid is mixed with paperboard raw materials, the activeness of cellulose contained in the paperboard at the high temperature is reduced, and the flame-retardant capacity is improved.

Application Domain

Flexible coversMechanical working/deformation +7

Technology Topic

Corrugated fiberboardAmmonium chloride mixture +9

Examples

  • Experimental program(2)

Example Embodiment

[0027] Embodiment 1:
[0028] The embodiment of the invention provides an environment-friendly corrugated board with rapid degradation, including degradation raw material group, main raw material group and flame retardant raw material group.
[0029] The degradation raw material group includes the following parts by weight: Polyurethane 5-15 parts, polyvinylamine 2-3 parts and ammonium chloride 10-15 parts.
[0030] The weight of polyurethane degradation raw materials includes 10-15 parts of ammonium chloride and less than 2-15 parts of polyethylene.
[0031] The flame retardant raw material group includes the following parts by weight: aluminum nitrate 2-5 parts, ammonium chloride 5-10 parts, pure water 20-30 parts, silicon oxide 10-15 parts and citric acid 10-20 parts.
[0032] The adhesive includes the following parts by weight of raw materials: 5-10 parts of hydrogen peroxide, 2-3 parts of defoamer, 30-40 parts of polyvinyl alcohol and 20-30 parts of acrylic acid.
[0033] The adhesive comprises the following preparation steps:
[0034] Firstly, polyvinyl alcohol, acrylic acid and water are added into the mixer, and stirred at 50-70 ℃ and 30-50 rpm for 1-1.5 hours. After stirring evenly, hydrogen peroxide aqueous solution is added, and the reaction is allowed to stand for 30-40 minutes to obtain mixture A. defoamer is added into the mixer, and the adhesive a is obtained after standing for 20-30 minutes.
[0035] The invention relates to a manufacturing method of rapidly degradable environment-friendly corrugated board, which comprises the following preparation steps:
[0036] S1. Firstly, put the corn straw into the pulverizer, crush the corn straw to 5-10 mesh powder at the speed of 100-150 rpm, and then put it into the high-temperature pulper together with alkali, sodium hydroxide, hydrochloric acid and steamer water. After beating at 80-100 ℃ for 1-2 hours, get the mixed slurry a;
[0037] S2. Put the mixed slurry a together with polyurethane and polyvinylamine in the mixing furnace and stir it at room temperature of 20-30 ℃ and rotating speed of 50-100 rpm for 2-3 hours. During the mixing process, ammonium chloride is added into the mixing furnace every half an hour. Finally, the mixed slurry B is obtained and stored statically. The water solubility of the paperboard itself is improved by adding polyvinylamine and polyurethane, and the degradation and separation speed of silicon contained in the paperboard is accelerated, The silicon was dissolved and eliminated by ammonium chloride to improve the degradation rate of paperboard itself;
[0038] S3. Add silicon oxide, aluminum nitrate and pure water into the high-temperature mixing tank, stir and mix at 100-120 ℃ and 30-50 rpm for 30-50 minutes. After mixing, add citric acid into the high-temperature mixing tank, stir at 50-80 ℃ for 20-30 minutes, and then add ammonium chloride. After raising the problem of the high-temperature mixing tank to 120-130 ℃, stand for 1-1.5 hours. After cooling to room temperature, get mixture a, In step S3, when silicon oxide, aluminum nitrate and pure water are stirred in the high-temperature mixing tank, the temperature inside the high-temperature mixing tank is reduced by 10-15 ° C every 10 minutes to obtain the flame retardant liquid, which is mixed with the paperboard raw materials to reduce the activity of the cellulose contained in the paperboard at high temperature and improve the flame retardant capacity;
[0039] S4. Put the mixed liquid a and mixed slurry B together in the drying room and dry them at 120-150 ℃ for 1-2 hours, so that the water content of paperboard slurry a after mixed liquid a and mixed slurry B is 20-30%;
[0040] S5. Place the paperboard slurry a in a hot press and press it into a 15-20mm thick plate blank a and a cylindrical folding texture blank a at 80-90 ℃, place it in a dry room at room temperature for static storage, and wait to cool to room temperature;
[0041] S6. Add a group of grain blanks a between two groups of plate blanks a, and pour adhesive a into the contact surface between grain blank a and platform blank A. after adhesive a cools and condenses, the finished corrugated board is finally obtained.

Example Embodiment

[0042] Embodiment 2:
[0043] The embodiment of the invention provides a rapid degradation environmental protection corrugated board, which comprises a degradation raw material group, a main raw material group and a flame retardant raw material group.
[0044] The degradation raw material group includes the following parts by weight: Polyurethane 8-20 parts, polyvinylamine 5-8 parts and ammonium chloride 5-10 parts.
[0045] The degradation raw material group includes the following parts by weight: 10-15 parts of polyurethane, 4-8 parts of polyvinylamine and 2-5 parts of ammonium chloride.
[0046] The flame retardant raw material group includes the following parts by weight: 2-5 parts of aluminum nitrate, 5-10 parts of ammonium chloride, 15-20 parts of pure water, 15-20 parts of silicon oxide and 10-15 parts of citric acid.
[0047] The adhesive includes the following parts by weight of raw materials: 4-8 parts of hydrogen peroxide, 3-5 parts of defoamer, 20-30 parts of polyvinyl alcohol and 15-20 parts of acrylic acid.
[0048] The adhesive comprises the following preparation steps:
[0049] Firstly, polyvinyl alcohol, acrylic acid and water are added into the mixer, and stirred at 50-70 ℃ and 30-50 rpm for 1-1.5 hours. After stirring evenly, hydrogen peroxide aqueous solution is added, and the reaction is allowed to stand for 30-40 minutes to obtain mixture A. defoamer is added into the mixer, and the adhesive a is obtained after standing for 20-30 minutes.
[0050] The invention relates to a manufacturing method of rapidly degradable environment-friendly corrugated board, which comprises the following preparation steps:
[0051] S1. Firstly, put the corn straw into the pulverizer, crush the corn straw to 5-10 mesh powder at the speed of 100-150 rpm, and then put it into the high-temperature pulper together with alkali, sodium hydroxide, hydrochloric acid and steamer water. After beating at 80-100 ℃ for 1-2 hours, get the mixed slurry a;
[0052] S2. Put the mixed slurry a together with polyurethane and polyvinylamine in the mixing furnace and stir it at room temperature of 20-30 ℃ and rotating speed of 50-100 rpm for 2-3 hours. During the mixing process, ammonium chloride is added into the mixing furnace every half an hour. Finally, the mixed slurry B is obtained and stored statically. The water solubility of the paperboard itself is improved by adding polyvinylamine and polyurethane, and the degradation and separation speed of silicon contained in the paperboard is accelerated, The silicon is dissolved and eliminated by ammonium chloride to improve the degradation speed of paperboard itself;
[0053] S3. Add silicon oxide, aluminum nitrate and pure water into the high-temperature mixing tank, stir and mix at 100-120 ℃ and 30-50 rpm for 30-50 minutes. After mixing, add citric acid into the high-temperature mixing tank, stir at 50-80 ℃ for 20-30 minutes, and then add ammonium chloride. After raising the problem of the high-temperature mixing tank to 120-130 ℃, stand for 1-1.5 hours. After cooling to room temperature, get mixture a, In step S3, when silicon oxide, aluminum nitrate and pure water are stirred in the high-temperature mixing tank, the temperature inside the high-temperature mixing tank is reduced by 10-15 ° C every 10 minutes to obtain the flame retardant liquid, which is mixed with the paperboard raw materials to reduce the activity of the cellulose contained in the paperboard at high temperature and improve the flame retardant capacity;
[0054] S4. Put the mixed liquid a and mixed slurry B together in the drying room and dry them at 120-150 ℃ for 1-2 hours, so that the water content of paperboard slurry a after mixed liquid a and mixed slurry B is 20-30%;
[0055]S5. Place the paperboard slurry a in a hot press and press it into a 15-20mm thick plate blank a and a cylindrical folding texture blank a at 80-90 ℃, place it in a dry room at room temperature for static storage, and wait to cool to room temperature;
[0056] S6. Add a group of grain blanks a between two groups of plate blanks a, and pour adhesive a into the contact surface between grain blank a and platform blank A. after adhesive a cools and condenses, the finished corrugated board is finally obtained.

PUM

no PUM

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.

Similar technology patents

Insulin receptor partial agonists

ActiveUS20170107268A1lower riskreduce activity
Owner:MERCK SHARP & DOHME LLC

Genetic Or Pharmacological Reduction Of Perk Enhances Cortical- And Hippocampus-Dependent Cognitive Function

ActiveUS20180265873A1improve cognitive functionreduce activity
Owner:CARMEL HAIFA UNIV ECONOMIC

Modifying n-glycosylation of plant proteins using gdp-4-dehydro-6-deoxy-d-mannose reductase (RMD)

InactiveUS20190225978A1reduce fucose contentreduce activity
Owner:GENOPOLE +1

Protease-resistant modified seb and vaccine containing the same

InactiveUS20100166793A1sufficient reactivityreduce activity
Owner:CHEMO SERO THERAPEUTIC RES INST

Oil-control, acne-removal and skin-care composition and preparation method thereof

PendingCN114376928AReduce activityreduce hypersecretion
Owner:广州一一生物技术有限公司

Classification and recommendation of technical efficacy words

  • Reduce activity
  • Improve flame retardant ability

Methods for providing safe local anesthesia

InactiveUS20020114835A1reduce activityimprove indexing
Owner:PURDUE PHARMA LP

Materials and methods for treatment of inflammatory and cell proliferation disorders

InactiveUS20050272650A1reduce activityreduce proliferation and tumor growth
Owner:UNIV OF SOUTH FLORIDA

System and method for using bit errors from memory to alter memory command stream

InactiveUS20080072116A1reduce activityincrease memory scrub rate
Owner:IBM CORP

Compositions and methods for treatment of cancer

InactiveUS7285382B2reduce activity
Owner:GENENTECH INC

Glycogen synthase kinase-3 inhibitors

InactiveUS20060069066A1efficiently usereduce activity
Owner:TEL AVIV UNIV FUTURE TECH DEVMENT

Five-membered ring phosphite compound, and preparation method and application thereof

PendingCN111217855AImprove flame retardant abilityImprove battery safety
Owner:EVERGRANDE NEW ENERGY TECH SHENZHEN CO LTD

Mantle emulsion fire retardant for organic fibre material and synthetic method thereof

InactiveCN1490458AImprove flame retardant abilityStrong water resistance
Owner:东莞市山力高分子材料科研有限公司

Aerogel-filled three-dimensional spacer fabric and preparation method thereof

PendingCN112553750AGood combinationImprove flame retardant ability
Owner:ZHEJIANG SCI-TECH UNIV

Composite fireproof cable

ActiveCN110364299AGood cooling performanceImprove flame retardant ability
Owner:ANHUI STAR CABLE

Flame-retarded expandable polystyrene copolymer

InactiveCN104045760AImprove heat resistanceImprove flame retardant ability
Owner:ZHEJIANG QUZHOU WANNENGDA SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products