Soaking mud and production method thereof

A production method and a technology for foaming mud, applied in the field of foaming mud, can solve the problems of environmental pollution, waste of related materials, unfavorable environmental protection and energy saving, etc., and achieve the effect of reducing costs and saving resources.

Inactive Publication Date: 2022-05-13
重庆市赛特刚玉有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the production and processing of brown fused alumina, more brown fused alumina dust will be formed. These brown fused alumina dusts are usually discarded directly, which will cause environmental pollution and waste of related materials, which is not conducive to environmental protection and energy saving.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Soaking mud and production method thereof
  • Soaking mud and production method thereof
  • Soaking mud and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Taking Example 1 as an example, a method for producing foam mud comprises the following steps:

[0037] Step 1, mixing materials: a, preparing materials: divide and order materials according to the formula ingredients in Example 1; the tar should be heated in advance, and the heating temperature of the tar is: 35-40°C, the mud mill is heated in advance, and the temperature is set at 60°C;

[0038] b. Mixing materials: Before mixing materials, it is necessary to check whether the scraper on the machine is damaged or the screw has fallen off, and then heat the machine. When the temperature inside the machine reaches the specified temperature, start the motor and wait for the machine to run normally before adding materials; Put it into the machine and stir for 1 to 2 minutes, then add tar, and then stir the machine for 20 to 40 minutes until the mud forms large pieces before releasing the material;

[0039] c. Feeding: put the mixed gun mud into the cleaned iron bucket; ...

Embodiment 4

[0062] In step a in step 2, during the process of pouring the weighed material into the mold cavity of the template, sometimes the material will be spilled outside the mold cavity, at this time, it is necessary to manually remove the spilled material on the template. Sweeping into the mold cavity is cumbersome to operate. Therefore, this embodiment discloses a template. By improving the structure of the template, the material spilled outside the mold cavity can be automatically swept into the mold cavity.

[0063] Basic as attached Figure 1-Figure 3 As shown, a template includes a plate body 1, a mold cavity 8 is provided on the top of the plate body 1, and a ring gear 2 is rotatably connected to the top of the plate body 1. The ring gear 2 is an external gear ring, and the mold cavity 8 is located on the At the central part of the ring 2, the rotation mode of the ring gear 2 is as follows: the top of the plate body 1 is provided with an annular groove, and the ring gear 2 is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of foamed mud, in particular to foamed mud and a production method thereof.The foamed mud is prepared from 20-30 parts of brown fused alumina recycled powder, 10-14 parts of silicon carbide, 10-14 parts of coke nuts, 35-45 parts of alumina and 15-20 parts of tar; the brown fused alumina recovery powder is prepared from the following components in parts by weight: 29 to 31 parts of Al2O3, 38 to 39 parts of SiO2, 16 to 17 parts of K2O, 3 to 4 parts of Fe2O3, 0.5 to 1 part of TiO2, 0.5 to 1 part of MgO, 0.1 to 0.2 part of CaO and 0.5 to 1 part of Na2O. The production method of the steeping mud comprises the steps of mixing, forming, packaging and the like. According to the method, the brown aluminum oxide powder is recycled, the waste of the brown aluminum oxide recycled powder is reduced, and meanwhile, the performance of the mud soaking is improved.

Description

technical field [0001] The invention relates to the field of foam mud, in particular to a foam mud and a production method thereof. Background technique [0002] Brown corundum, commonly known as corundum, is a brown artificial corundum obtained by melting and reducing three raw materials of bauxite, carbon material and iron filings in an electric arc furnace. Brown corundum is the most basic abrasive, and it is widely used because of its good grinding performance, wide application range and low price. During the production and processing of brown fused alumina, more brown fused alumina dust will be formed. These brown fused alumina dusts are usually discarded directly, which will cause environmental pollution and waste of related materials, which is not conducive to environmental protection and energy saving. Contents of the invention [0003] The present invention intends to provide a foam mud and a production method thereof, so as to realize the recycling of brown coru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/66C04B35/10C04B35/622B65B5/00B28B3/02B28B17/00B28C3/00
CPCC04B35/66C04B35/10C04B35/62204B28B3/02B28B17/00B28C3/00B65B5/00C04B2235/3826C04B2235/3418C04B2235/3201C04B2235/3272C04B2235/3232C04B2235/3206C04B2235/3208C04B2235/9669B65B2220/20
Inventor 范豫庆
Owner 重庆市赛特刚玉有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog