Continuous casting crystallizer function protection material for industrial pure iron

A continuous casting crystallizer and industrial pure iron technology, applied in the field of metallurgical auxiliary materials, can solve the problems of slow melting speed of protective materials, high binary alkalinity, high carbon content, etc., and achieve improved casting billet quality, high melting stability, Reduce the effect of slag inclusion

Pending Publication Date: 2022-07-22
西峡县西保冶金材料有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the binary alkalinity of the protective material is high, the melting speed of the protective material is slow, the lubricity is poor, and the carbon content is high, so it is not suitable for industrial pure iron continuous casting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Continuous casting crystallizer function protection material for industrial pure iron
  • Continuous casting crystallizer function protection material for industrial pure iron
  • Continuous casting crystallizer function protection material for industrial pure iron

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] To make the objectives, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions of the present invention will be described clearly and completely below with reference to some specific embodiments. Obviously, the described embodiments are some, but not all, embodiments of the present invention. Based on the described embodiments of the present invention, all other embodiments obtained by those of ordinary skill in the art fall within the protection scope of the present invention.

[0025] Various raw materials and their weight percentages of the continuous casting mold function protection material for industrial pure iron in Examples 1-7 of the present invention are shown in Table 1.

[0026] See Table 2 for the chemical composition and the weight percent content of the continuous casting mold functional protection material for industrial pure iron in Examples 1-7 of the present invention.

[0027] The chemical com...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a function protection material for a continuous casting crystallizer for industrial pure iron. The function protection material is prepared from the following raw materials in percentage by weight: 30.0 to 36.0 percent of pre-melting material, 15.0 to 17.0 percent of wollastonite, 9.0 to 12.0 percent of albite powder, 2.0 to 3.0 percent of lithium carbonate, 14.0 to 16.0 percent of fluorite, 2.0 to 3.0 percent of dead burnt magnesia, 3.0 to 5.0 percent of boron glass powder, 2.0 to 4.0 percent of graphite carbon, 2.0 to 4 percent of imported carbon black, 5.0 to 8.0 percent of bauxite and 2.0 to 3.5 percent of binder. According to the casting powder, the heat preservation effect and the melting effect are guaranteed, the problems of recarburization and carburization on the surface of a casting blank are effectively avoided, smooth production is guaranteed, and the surface qualification rate of the casting blank reaches 99% or above.

Description

technical field [0001] The invention relates to the technical field of metallurgical auxiliary materials, in particular to a functional protection material for continuous casting crystallizers for industrial pure iron. Background technique [0002] Continuous casting mold flux, as an important metallurgical auxiliary material to ensure continuous casting, has a significant impact on continuous casting production and slab quality assurance. With the vigorous development of continuous casting technology, the current international continuous casting ratio has exceeded 95%. Industrial pure iron refers to pure iron with an iron content of more than 99% and a carbon content of less than 0.04%, and requires low smelting harmful elements. Industrial pure iron is divided into electrical pure iron (electromagnetic pure iron), raw material pure iron (charge pure iron), and military pure iron. Electric pure iron has good electrical conductivity and good magnetic permeability, and is ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22D11/111
CPCB22D11/111
Inventor 江波范李飞张鹏
Owner 西峡县西保冶金材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products