Phosphogypsum-based light plastering gypsum for hollow internal mold metal net wall body

A technology for plastering gypsum and metal mesh, applied in the field of building plastering materials, can solve the problems of unstable performance of phosphogypsum, high impurity content, low utilization rate, etc., achieve smooth construction feel, improve comprehensive performance, and reduce comprehensive production. cost effect

Pending Publication Date: 2022-08-05
云南特雅建材科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, phosphogypsum is different from desulfurized gypsum. The performance of phosphogypsum is unstable, especially the high impurity content causes low utilization rate. Therefore, no one has successfully used phosphogypsum to prepare a plaster that can be used to make hollow inner mold metal mesh walls. product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of phosphogypsum-based light plastering gypsum for hollow inner-mold metal mesh wall, in parts by mass, including 100 parts of gypsum high-strength agent, 80 parts of gypsum water-resistant agent, 90 parts of sodium bentonite, and 100 parts of vitrified microbeads , 60 parts of anti-sagging agent, 700 parts of phosphate rock gypsum powder, 8 parts of thixotropic lubricant, 70 parts of hydroxypropyl methylcellulose, 45 parts of anti-cracking enhancer, 25 parts of starch ether, and 30 parts of inorganic toughening agent.

Embodiment 2

[0022] A kind of phosphogypsum-based light plastering gypsum for hollow inner-mold metal mesh wall, which, in parts by mass, comprises 50 parts of gypsum high-strength agent, 100 parts of gypsum water-resistant agent, 60 parts of sodium bentonite, and 50 parts of vitrified microbeads , 50 parts of anti-sagging agent, 500 parts of phosphate rock gypsum powder, 6 parts of thixotropic lubricant, 50 parts of hydroxypropyl methylcellulose, 20 parts of anti-cracking enhancer, 15 parts of starch ether, and 40 parts of inorganic toughening agent.

Embodiment 3

[0024] A kind of phosphogypsum-based light plastering gypsum for hollow inner-mold metal mesh wall, which, in parts by mass, comprises 90 parts of gypsum high-strength agent, 120 parts of gypsum water-resistant agent, 70 parts of sodium bentonite, 50 parts of calcined ceramic particles, 100 parts of anti-sagging agent, 400 parts of phosphate rock gypsum powder, 5 parts of thixotropic lubricant, 40 parts of hydroxypropyl methylcellulose, 30 parts of anti-cracking enhancer, 10 parts of starch ether, and 10 parts of inorganic toughening agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to ardealite-based light plastering gypsum for a hollow internal mold metal net wall body and a preparation method of the ardealite-based light plastering gypsum. Comprising 50 to 450 parts of a gypsum high-strength agent, 50 to 450 parts of a gypsum water-resistant agent, 50 to 120 parts of sodium bentonite, 50 to 250 parts of glass beads or 50 to 200 parts of calcined ceramic particles, 50 to 200 parts of an anti-sagging agent, 200 to 1800 parts of calcined phosphogypsum, 1 to 8 parts of a thixotropic lubricant, 10 to 80 parts of hydroxypropyl methyl cellulose, 5 to 50 parts of an anti-cracking reinforcing agent, 1 to 30 parts of starch ether and 1 to 50 parts of an inorganic flexibilizer. The plastering gypsum base disclosed by the invention has the advantages of light weight, high strength, stable and reliable product and low manufacturing cost, can meet the requirements of different strengths, different sound insulation and heat preservation and different regional climates of building design, effectively reduces the weight of a hollow internal mold metal net wall body due to light weight, and improves the shock resistance and heat preservation of a building.

Description

technical field [0001] The invention relates to the technical field of building plastering materials, in particular to a phosphogypsum-based light plastering plaster for hollow inner-mold metal mesh walls. Background technique [0002] The hollow inner mold metal mesh wall is a wall formed by spraying plastering plaster onto the steel mesh and then smoothing it. It is widely used in the partition walls of airports, schools, hospitals and other high-rise buildings because of its good seismic resistance. The traditional hollow inner mold The metal mesh walls are all prepared by spraying metal mesh with cement mortar, and the weight of the mesh wall per square meter is 120-140 kilograms, which causes the building to weigh too much. For this reason, some manufacturers have begun to try to reduce the amount of cement and use cement plastering gypsum to spray metal mesh. Although this can improve the seismic resistance of the hollow metal mesh partition wall, due to the heavy weig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B111/28C04B111/52
CPCC04B28/14C04B2111/00482C04B2111/28C04B2111/52C04B14/104C04B14/22C04B18/0445C04B24/383C04B2103/65C04B2103/0068C04B2103/0085C04B18/023Y02W30/91
Inventor 周世斌周佳霖
Owner 云南特雅建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products