Sheet laminating preparation method for sisal fiber reinforced polypropylene composite material

A technology of sisal fiber and composite materials, which is applied in fiber processing, textiles and papermaking, etc., to achieve the effect of improving comprehensive performance, strong tensile force and low price

Inactive Publication Date: 2005-02-23
SUN YAT SEN UNIV
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This inventive process is only suitable for the preparation of medium-strength materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-4

[0023] Example 1-4: The raw sisal fibers were cut into 5mm, 20mm and 30mm respectively, and the obtained sisal short fiber raw materials were dried in an oven at 80°C. Stir the PVA aqueous solution with a concentration of 1% (mass percentage) and sisal short fiber raw materials evenly to make a fiber mat, then place it on a hydraulic press to press and shape it, and adjust the temperature of the hydraulic press to 100°C and the pressure to 2MP a . The PVA content in the prepared sisal fiber felt is 2%. Select 5 pieces of sisal fiber felt, sandwich the same amount of PP non-woven fabric in the interlayer, press and form it on a hydraulic press, the forming temperature is 172°C, and the pressure is 5MP a . The mass percent contents of the selected PP are 30%, 40% and 50% respectively.

Embodiment 5-7

[0024] Example 5-7: Cut the raw sisal fiber into 10mm, 20mm and 30mm respectively to obtain the sisal short fiber raw material, soak the sisal short fiber raw material with fluorine-containing waterproofing agent for 1 minute, take it out and dry it in the air, and store it at 80°C After drying, the pretreated sisal short fiber raw material is obtained. Stir the PVA aqueous solution with a concentration of 5% (mass percentage) and PP powder evenly, then pour it into the pretreated sisal short fiber raw material for mixing, lay a felt, and then place it on a hydraulic press to press and shape it, and adjust the temperature of the hydraulic press to 120°C , the pressure is 2MP a . Select 5 pieces of sisal fiber felt to be laminated and place them on a hydraulic press to form them. The forming temperature is 175°C and the pressure is 4MP. a . The mass percent contents of the selected PP are 30% and 50% respectively.

[0025] Table 1 shows the composition and performance data ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The present invention adopts the sisal hemp fiber as fiber raw material, and uses the nonwoven fabric of thermoplastic resin PP, film, powder material and its fiber as resin base body, and adopts the following steps: pretreating sisal hemp fiber and making it into fiber felt, hot-pressing and forming, selecting and using a certain number of fiber felts, delaminating and sand wiching pp nonwoven fabric or film, under the condition of a certain temp. and pressure hot-pressing and forming or mixing PP fiber (PP powder) directly with sisal hemp fibre, making them into fiber felt and then hot-pressing and forming so as to obtain the invented sisal hemp fiber reinforced polypropylene composite material.

Description

technical field [0001] The invention belongs to the preparation method of sisal fiber (SF) / thermoplastic resin matrix composite material. Background technique [0002] In the preparation method of existing sisal fiber / thermoplastic resin-based composite material, the short sisal fiber / low-density polyethylene composite material that people such as Kuruvilla Joseph adopt melt blending and solution blending to make, melt blending The characteristic of the method is that the damage to the sisal fiber is serious, resulting in a decline in the performance of the composite material, while the solution mixing process needs to use a large amount of toxic solvents, causing environmental pollution, and the cost is also high. Joesph et al. also prepared short sisal fiber / polypropylene composites by extrusion molding. The screw of this process seriously damages the sisal fiber, and the high temperature will cause the sisal fiber to decompose. [0003] Zeng Hanmin and Yang Guicheng use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C70/12C08J5/04D06M17/00
Inventor 曾汉民杨桂成梁小波
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com