Multifunction sulfur recovery catalyst and its preparing method

A sulfur recovery and catalyst technology, applied in chemical instruments and methods, sulfur preparation/purification, physical/chemical process catalysts, etc., can solve problems such as low activity of organic sulfur hydrolysis, poor poisoning performance, and poor mechanical strength of catalysts

Inactive Publication Date: 2004-07-14
SINOPEC QILU CO
View PDF3 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0024] The object of the present invention is to provide a 2 "Poisoning performance and de-"leakage of O 2 "Protection ability, multi-functional sulfur recovery catalyst with high organosulfur hydrolysis activity and Claus activity and its preparation method are used to overcome and solve common Al 2 o 3 Catalyst resistant to "leaking O 2 "Poor poisoning performance, easy to sulfate poisoning and Al containing iron compounds 2 o 3 The base catalyst has low activity in hydrolysis of organosulfur and TiO 2 Defects and problems such as poor mechanical strength of the catalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] After drying at 120° C. for 4 hours and pulverizing to 180 mesh, 100 g of industrial metatitanic acid dry powder, 100 g of industrial pseudoboehmite aluminum hydroxide dry powder and 6 g of turmeric powder were mixed evenly. According to the 3% metering element iron of finished catalyst weight, take by weighing 24.3g FeSO 4 ·7H 2 O and 6g HNO 3 Dissolve in 70ml distilled water with HNO 3 After adjusting the pH value of the solution to 4-5, add it to the above-mentioned powder and stir, knead with a twin-screw extruder for 0.5h, extrude it with a Φ4.5mm orifice plate, and place it at room temperature for 12h to dry. Dry at 120°C for 2 hours and calcined at 400°C for 4 hours to obtain catalyst sample A. The chemical composition of its active components is: TiO 2 54.2% (m / m), Al 2 o 3 45.8% (m / m).

[0041] FeSO 4 The measured iron-containing compound is 7.8%, and the specific surface area of ​​the sample is measured to be 218m 2 / g, crushing strength 152N / cm, me...

Embodiment 2

[0043] After drying at 120°C for 4 hours, 100 g of industrial metatitanic acid dry powder and 100 g of industrial pseudo-boehmite aluminum hydroxide dry powder were crushed to 180 meshes, and mixed with 6 g of turmeric powder. Weigh 6g concentrated HNO 3 Dissolve in 85ml of distilled water, add to the above powder and stir, knead with a twin-screw extruder for 0.5h, extrude with a Φ4.5mm orifice plate, place at room temperature for 12h to dry, and dry at 120°C for 2h Roast at 400℃×4h to get TiO 2 -Al 2 o 3 Carrier, its chemical composition is: TiO 2 54.2% (m / m), Al 2 o 3 45.8% (m / m); Then measure elemental iron according to 3% of finished catalyst weight, weigh 24.3g FeSO 4 ·7H 2 O was dissolved in 25ml of distilled water, with HNO 3 Adjust the pH value of the solution between 4-5, and dry the above-mentioned TiO with a particle size of 20 mesh to 40 mesh at 120°C 2 -Al 2 o 3 158.4g of the carrier was immersed in it, stirred evenly, left at room temperature for 12...

Embodiment 3

[0045] According to embodiment 2 conditions, prepare clover-shaped and four-leaf clover-shaped catalyst samples B respectively 1 and B 2 , The crushing strength measured is 178N / cm and 191N / cm respectively, and the mechanical strength after the boiling test is 159N / cm and 174N / cm respectively.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Crushing strengthaaaaaaaaaa
Mechanical strengthaaaaaaaaaa
Login to View More

Abstract

The present invention is multifunctional sulfur recovering catalyst with high deoxygenation activity, high organic sulfur hydrolyzing activity and high H2S-SO2 Clausius reaction activity and its preparation process. The catalyst has active components including titania 40-60 wt%, active alumina 35-50 wt% and ferrous compound 5-10 wt%. The catalyst has the advantages of great specific surface area, high mechanical strength, high oxygen leakage poisoning tolerance, high deoxygenation activity, high organic sulfur hydrolyzing activity and high H2S-SO2 Clausius reaction activity. It may be used alone or via matching with common alumina catalyst.

Description

technical field [0001] The invention relates to a sulfur recovery catalyst and a preparation method thereof, in particular to a sulfur recovery catalyst with high deoxygenation 2 activity and higher organosulfur hydrolysis activity and higher H 2 S and SO 2 A multifunctional sulfur recovery catalyst with Claus reaction activity and its preparation method. Background technique [0002] Large amounts of H are produced during oil and gas processing 2 S gas, in order to protect the environment and recover elemental sulfur, the industry generally adopts the Claus process to treat the gas containing H 2 The acid gas of S, its reaction equation is as follows: [0003] <chemistry num="001"> <chem file="02151549_cml001.xml" / > < / chemistry> (1) [0004] <chemistry num="002"> <chem file="02151549_cml002.xml" / > < / chemistry> (2) [0005] <chemistry num="003"> <chem file="02151549_cml003.xml" / >...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01D53/48B01D53/86B01J23/835B01J27/053C01B17/04
Inventor 唐昭峥张文郁胡文宾达建文解秀清郝国阳谭永放
Owner SINOPEC QILU CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products