Fireproof materials for pressed repairing and method for preparing same

A technology of refractory materials and additives, which is applied in the field of refractory materials to achieve the effects of strong bonding ability, dense structure and prolonged service life

Inactive Publication Date: 2005-08-17
WUHAN IRON & STEEL (GROUP) CORP
View PDF2 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the repair material combined with phenolic resin by Sumitomo Corporation of Japan, its main chemical composition is Al 2 o 3 , SiO 2、 , SiC or MgO, SiC, fixed carbon; in China, the General Institute of Metallurgical Construction reported a repair material combined with thermoplastic phenolic resin, the main chemical composition of which is Al 2 o 3 , SiO 2 , Fe 2 o 3 、K 2 O+Na 2 O, TiO 2 ; Luoyang Institute of Refractory Materials reported a repair material combined with two phenolic resins with different properties, and its main chemical composition is Al 2 o 3 ,, SiO 2 , Fe 2 o

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The refractory material used for press-in repair, the components and parts by weight are: 23 parts of bauxite, 33 parts of coke gem, 3 parts of clay, 12 parts of silicon carbide, 3 parts of carbon, 2 parts of dilithium oxide, 2 parts of dilithium oxide 1 part of boron, 20 parts of thermoplastic phenolic resin, 2 parts of silicone resin, 1 part of tar.

[0024] Preparation method, its steps:

[0025] 1) Mix 23 parts of bauxite, 33 parts of coke, 3 parts of clay, 12 parts of silicon carbide, 3 parts of carbon, 2 parts of dilithium oxide, and 1 part of diboron trioxide to achieve uniformity and form increased additive refractory matrix;

[0026] 2) Heat, stir and mix 20 parts of thermoplastic phenolic resin, 2 parts of silicone resin and 1 part of tar at 80°C to form an organic binder;

[0027] 3) Stir and mix the prepared organic binder with the additive-added refractory matrix mixture, make it uniform, and then pack it for use.

Embodiment 2

[0029] The refractory material used for press-in repair, the components and parts by weight are: 67 parts of coke gemstone, 3 parts of clay, 3 parts of silicon carbide, 1 part of carbon, 1 part of dilithium oxide, 2 parts of diboron trioxide, thermoplastic 20 parts of phenolic resin, 2.9 parts of silicone resin, 0.1 part of tar.

[0030] Preparation method, its steps:

[0031] 1) Stir and mix 67 parts of the above-mentioned burnt gemstones, 3 parts of clay, 3 parts of silicon carbide, 1 part of carbon, 1 part of dilithium oxide, and 2 parts of diboron trioxide to form a refractory matrix with additives ;

[0032] 2) Heat, stir and mix 20 parts of thermoplastic phenolic resin, 2.9 parts of silicone resin and 0.1 part of tar at 110°C to form an organic binder;

[0033] 3) Stir and mix the prepared organic binder with the additive-added refractory matrix mixture, make it uniform, and then pack it for use.

Embodiment 3

[0035] The refractory material used for press-in repair, the components and parts by weight are: 38 parts of corundum, 20 parts of coke gem, 3 parts of clay, 12 parts of silicon carbide, 3 parts of dilithium oxide, 1 part of diboron trioxide, thermoplastic phenolic 21.4 parts of resin, 1.5 parts of silicone resin, 0.1 part of tar.

[0036] Preparation method, its steps:

[0037] 1) Stir and mix the above-mentioned 38 parts of corundum, 20 parts of coke gem, 3 parts of clay, 12 parts of silicon carbide, 3 parts of dilithium oxide, and 1 part of diboron trioxide to form a refractory matrix with additives added;

[0038] 2) Heat and stir 21.4 parts of thermoplastic phenolic resin, 1.5 parts of silicone resin, and 0.1 part of tar at 180°C to form an organic binder;

[0039] 3) Stir and mix the prepared organic binder with the additive-added refractory matrix mixture, make it uniform, and then pack it for use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to refractory material for pressing repair and its preparation process. The refractory material for pressing repair consists of organic binding agent in 3-35 weight portions, refractory material base in 20-80 weight portions and additive in 1-10 weight portions. The preparation process includes the following steps: preparing refractory material base with two or more of high alumina bauxite, bauxite, corundum, clay, SiC and carbon; adding additive; adding organic silicon resin, tar and thermoplastic phenolic resin, mixing homogeneously through stirring and heating at 60-200 deg.c to obtain the organic binding agent; mixing the refractory material base with additive and the organic binding agent; and packing.

Description

technical field [0001] The invention belongs to refractory materials, in particular to a refractory material for press-in repair and a preparation method. Background technique [0002] At present, when using the press-in method to repair equipment such as blast furnaces, RH vacuum furnaces, and mixed iron furnaces, there are mainly two types of refractory materials used, namely, water-based bonding materials and materials using phenolic resin as a bonding agent. [0003] The water-based binding material is mainly composed of water glass, cement and phosphate, and its main chemical composition is Al 2 o 3、 , Fe 2 o 3 、K 2 O+Na 2 O, SiC, the binder is aluminum dihydrogen phosphate, such as: Patent No. 01133640.4 of the published patent for repairing refractories for converters, the main components are sintered magnesia, dolomite, sodium metasilicate, sodium hexametaphosphate ; Patent No. is the patent of 01106497.8, also discloses the repairing refractory material that i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/10C04B35/66
Inventor 徐国涛张洪雷刘国明王悦李安平秦殷
Owner WUHAN IRON & STEEL (GROUP) CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap