Environmental-friendly aqueous epoxy floor coating

An epoxy floor, green and environmentally friendly technology, applied in the direction of epoxy resin coating, coating, latex paint, etc., can solve the problems of gloss, texture and adhesion, poor coating performance, low VOC content, etc., to achieve the goal of coating Improved membrane resistance to chemicals, stable performance, and reduced volume shrinkage

Inactive Publication Date: 2005-11-30
董善刚 +2
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] There are Type I and Type II waterborne epoxy coatings on the market. For example, the publication number is 1415680, and the patent application titled "A Waterborne Epoxy Resin Coating and Its Preparation Method" relates to a Type II waterborne epoxy coating. Publication No. The 1460698 patent appl

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] Below are embodiments of the present invention:

[0018] Among them, the components and weight percentages are, in component A: UCB water-based epoxy curing agent (EH623W / 80WA): 28; water: 16; Corning defoamer (DEHYDRAN 1620): 0.3; Corning wetting agent (HYDROPALAT 875): 0.3; Rohm and Haas leveling agent (2020): 0.4; Propylene Glycol Methyl Ether: 3; Bayer Iron Yellow Pigment (4920): 5; Changzhou North American Group Phthalocyanine Blue Pigment (BGS1513): 4; Shaanxi Fuhua Precipitated barium sulfate (1250 mesh): 25; Jinan Yuxing titanium dioxide (BA101): 2; Pingdu talc powder (400 mesh): 6; Anhui Yina silicon powder (800 mesh): 10. In component B: UCB water-based aerobic resin (EP147W): 16; UCB water-based epoxy resin (EP384W / 53WAMP): 60; water: 4.

[0019] The specific implementation steps are:

[0020] (1) While stirring, gradually add 16 parts of water and 0.3 parts of Corning wetting agent (HYDROPALAT 875) to 28 parts of UCB water-based epoxy curing agent (EH623W / ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a formulation and the method for preparation of a green environment-friendly water-based epoxy terrace-using coating. The green environment-friendly water-based epoxy terrace-using coating comprises the first and the second component, the constituent and weight ratio of the first component being as the following: water-based epoxy curing agent 28-32, water 10-20, defoamer 0.2-0.5, wetting agent 0.2-0.5, leveling agent 0.2-0.5, consolute agent 1-5, phthalocyanine green 3-6, ferrite yellow 4-6, titanium dioxide 1-3, blanc fixe 20-30, silicon micronized quartz powder 10-15, and talcum powder 5-8; and the constituent and weight ratio of the second component being: water-based epoxy emulsion A 15-25, water-based epoxy emulsion B 20-28, and water 1-6. The first component: the second component is 1.25: 1, homogeneously mixing them. The prepared green environment-friendly water-based epoxy terrace-using coating can ensure the lacquer film having good brightness, adhesive force, strong chemical resistance, nice environmental protection property, and low containing of VOC.

Description

technical field [0001] The invention relates to a green and environment-friendly water-based epoxy floor coating formula and a preparation method thereof. Background technique [0002] At present, traditional industrial floor coatings are basically solvent-based and solvent-free floor coatings. Among them, solvent-based floor coatings contain more organic solvents, while solvent-free floor coatings contain active diluents, which are toxic and pollute the environment. endanger human health. With the gradual improvement of people's awareness of environmental protection, many countries have promulgated environmental protection regulations to limit volatile organic solvents (VOC), so the development of coatings in the direction of water-based has become inevitable. [0003] There are Type I and Type II waterborne epoxy coatings on the market. For example, the publication number is 1415680, and the patent application titled "A Waterborne Epoxy Resin Coating and Its Preparation M...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00
Inventor 董善刚刘永屏
Owner 董善刚
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap