Preparation method of natural red brillinance zeolite as rubber reinforcing additive

A technology of hematilite and additives, which is applied in the field of preparation of natural hematite as a rubber reinforcing additive, to achieve good reinforcing performance, lower production costs, strong competitiveness and promotion and application value

Inactive Publication Date: 2006-01-11
GUILIN UNIVERSITY OF TECHNOLOGY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And natural hematilite has not yet been reported as rubber reinforcing additive and preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Using the natural staphilite ore of Guangxi resources as raw material, the raw ore is washed, crushed and processed to 80-120 mesh; with 60 grams of staphite, 5 grams of zinc oxide, 2 grams of stearic acid, 2.3 grams of sulfur, and 0.8 grams of accelerator gram, 100 grams of rubber, put the natural rubber on the plastic refining machine for initial refining, then add zinc oxide, accelerator, sulfur, and other additives in turn and mix well, then add hematite several times, and mix the rubber until the rubber After the upper and lower surfaces are relatively smooth, take the glue, place it on a clean glass plate, cut it into 22.5×10 (mm) thin slices, take it to a plate vulcanizing machine for vulcanization, and then preheat it with soapy water Put the cut film into the finished mold, pressurize and vulcanize, control the vulcanization temperature within the range of 140°C, and vulcanize for 20 minutes. After the vulcanization is completed, take the glue, cut the vulcanize...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strength at breakaaaaaaaaaa
hardnessaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

A process for preparing the reinforcing agent of rubber from redglow zeolite includes such steps as washing, pulverizing, proportionally mixing it with zinc oxide, stearic acid sulfur, promoter and rubber, neutralizing, adding said zeolite several times, rubber milling and sulfurizing.

Description

technical field [0001] The invention relates to a preparation method of natural hephtilite as a rubber reinforcing additive. Background technique [0002] Stellerite is a mineral species in the pyroxene family, its chemical composition (weight percent): SiO 2 58.76、Al 2 o 3 14.13, CaO8.80, K 2 O0.11, Na 2 O0.18, Fe 2 o 3 0.44, H 2 o + 16.87, H 2 o - 1.25, its chemical formula is (K 0.017 Na 0.042 Ca 1.73 ) 1.189 [Al 1.997 Si 7. 5i 7.05018 ]6.75H 2 O. Natural stilbene is a hydrous alkali metal or alkaline earth metal aluminosilicate mineral, a framework silicate composed of silicon-oxygen tetrahedrons and aluminum-oxygen tetrahedrons. The oxygen atom in the aluminum oxygen tetrahedron has a valency and is not saturated, and the entire aluminum oxygen tetrahedron is negatively charged, and the nearby positively charged cations such as K + 、Na + , Ca 2+ , Mg 2+ Such as alkali metal or alkaline earth metal ions to compensate for the balance. With the func...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08K3/34C08L21/00
Inventor 陈南春崔天顺
Owner GUILIN UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com