Mixed polytetrafluoroethylene powder, polytetrafluoroethylene porous shaped body, methods for producing those, polytetrafluoroethylene porous foam shaped body, and product for high-frequency signal tr

A technology of polytetrafluoroethylene powder and polytetrafluoroethylene, which is applied in the field of high-frequency signal transmission products, can solve the problems of inability to obtain a molded body, burrs on the surface of insulating materials, etc.

Active Publication Date: 2006-10-04
DAIKIN IND LTD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no description about the production method of expanded polytetrafluoroethylene, a molded body cannot actually be obtained, and burrs are formed on the surface of the insulating material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mixed polytetrafluoroethylene powder, polytetrafluoroethylene porous shaped body, methods for producing those, polytetrafluoroethylene porous foam shaped body, and product for high-frequency signal tr

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0225] Spread 1kg of PTFE resin molding powder (TFE homopolymer, SSG 2.155, the maximum endothermic peak temperature at one time is 340°C) on a stainless steel tray to a thickness of 20mm, and burn it in an electric furnace at 380°C for 5 hours , to obtain PTFE resin block.

[0226] The obtained mass of PTFE resin was pulverized to an average particle diameter of 50 μm using a pulverizer to obtain a pulverized powder (hereinafter referred to as a gelled powder).

[0227] 160g of the obtained gelled powder (secondary maximum endothermic peak temperature is 327°C), 640g

[0228] PTFE resin fine powder (SSG 2.160, a maximum endothermic peak temperature of 339° C.) and 136 g of an extrusion aid (trade name: ISOPAR G, manufactured by Exxon Shell) were charged into a 5 L polyethylene bottle and mixed by rotating for 10 minutes. Continue to place it in polyethylene bottle for 2 hours to make it mature at 25° C., obtain 800 g of mixed powder (PTFE resin fine powder: gelled powder=77:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

Disclosed is a polytetrafluoroethylene porous shaped body characterized in that it has a specific gravity of 0.9-2.0 and the aspect ratio of pores formed inside the shaped body is not less than 1 and not more than 3.

Description

technical field [0001] The present invention relates to mixed polytetrafluoroethylene powder and polytetrafluoroethylene porous molded body, their production method, polytetrafluoroethylene porous foam molded body and products for high-frequency signal transmission. Background technique [0002] In order to increase the transmission speed of high-frequency signal transmission products such as coaxial cables, LAN cables, and printed circuit boards, and reduce dielectric loss, insulating materials with a dielectric constant (ε) as low as possible are selected. As the resin constituting the insulating material, fluorine-containing resin is preferably used because it has a low dielectric constant and a low dielectric loss tangent (tan δ), which not only contributes to the reduction of dielectric loss, but also is excellent in heat resistance and the like. [0003] It is known that in order to lower the dielectric constant of an insulating material, it is effective to disperse a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J9/24C08J9/04C08J9/26C08J3/16H01B3/44
CPCC08J2327/18C08J9/24H01B3/445Y10T428/249953
Inventor 泽田又彦吉本洋之笠井俊二田头修二
Owner DAIKIN IND LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap