Manufacturing method for raising specific volume of electrode foil in use for aluminium electrolytic capacitor
A technology for aluminum electrolytic capacitors and manufacturing methods, applied in the direction of electrolytic capacitors, capacitor manufacturing, capacitors, etc., can solve the problem of low electrode foil capacity, achieve high product quality, reasonable technology, and increase the effect of specific capacitance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0011] Example one:
[0012] Take the corroded aluminum foil for medium pressure, with a purity of 99.99%, immerse it in pure water above 95 degrees for 6 minutes, then soak it in 0.5% 60 degrees phosphoric acid solution for 5 minutes, then in 1.2% ammonium adipate And 4% boric acid in 85℃ aqueous solution, the applied current density is 50mA / cm 2 , 350V voltage for formation, after 28 minutes of constant voltage, high temperature heat treatment at 450°C for 4 minutes, and then in an aqueous solution of 1.2% ammonium adipate and 4% boric acid at 90°C, the applied current density is 50mA / cm 2 , 350V voltage is formed, and the constant voltage ends after 12 minutes.
Example Embodiment
[0013] Embodiment two:
[0014] Take the corroded aluminum foil for medium pressure with a purity of 99.99%, soak it in pure water above 95 degrees for 6 minutes, then soak it in a 0.1% 40 degree phosphoric acid solution for 1 minute, and then in 0.5% ammonium adipate And 3% boric acid in 60℃ aqueous solution, the applied current density is 50mA / cm 2 , 350V voltage for chemical conversion, constant voltage for 20 minutes, and then through 350 ℃ high temperature heat treatment for 3 minutes, then in 0.5% ammonium adipate and 3% boric acid 60 ℃ aqueous solution, the applied current density is 50mA / cm 2 , 350V voltage is formed, and the constant voltage will end after 10 minutes.
Example Embodiment
[0015] Embodiment three:
[0016] Take the corroded aluminum foil for medium pressure, with a purity of 99.99%, immerse it in pure water above 95 degrees for 6 minutes, then soak in 5% 90 degrees phosphoric acid solution for 10 minutes, and then in 3% ammonium adipate And 10% boric acid 90℃ aqueous solution, the applied current density is 50mA / cm 2 , 350V voltage for chemical conversion, after 30 minutes of constant voltage, heat treatment at 500°C for 5 minutes, then in 3% ammonium adipate and 10% boric acid in an aqueous solution of 90°C, the applied current density is 50mA / cm 2 , 350V voltage for formation, the constant voltage will end after 15 minutes.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap