Inorganic composition

A composite and inorganic technology, which is applied in the field of substrates for disk-shaped information recording media, can solve problems such as smoothness changes and large surface properties, and achieve the effects of improving surface recording density, mechanical strength, and recording density

Inactive Publication Date: 2007-04-11
OHARA
View PDF11 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The crystallized glass produced by this technology can be smoothed at the atomic level by polishing, but the effect of various cleanings in the film formation process as a magnetic film produces a large smoothness in surface properties Sexual changes or problems with tiny bumps

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inorganic composition
  • Inorganic composition
  • Inorganic composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～3

[0133] and

[0134] Table 1 is about the examples (No. 1 to 3) of crystallized glass that is the inorganic composition of the present invention and the previous three types of Li 2 SiO 3 Crystalline-like glass (comparative example 1: disclosed in Japanese Patent Laid-Open No. 62-72547, Comparative Example 2: disclosed in Japanese Patent Laid-Open No. 9-35234, Comparative Example 3: disclosed in Japanese Patent Laid-Open No. Hei 12-302481 Bulletin), and the previous Li 2 O-SiO 2 Amorphousglass (Comparative Example 4), which together show the ratio of its component composition, the nucleation temperature, crystallization temperature, crystal phase, crystallinity, average grain size, hoop bending strength of crystallized glass , The surface roughness Ra (arithmetic average roughness) formed by grinding, the value of the surface roughness change amount and the surface roughness change rate, specific gravity, Young's modulus, and thermal expansion coefficient after the grinding proce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The present invention provides an inorganic composition for use in information recording medium disc substrate and such, having an excellent surface property capable of sufficiently corresponding with a ramp load system for high density recording, a high degree of tolerability to high speed rotation, and high productivity at a low melting point. Specifically, this invention provides an inorganic composition containing one crystalline phase selected from the group consisting of Alpha-quartz (Alpha-SiO 2 ), lithium disilicate (Li 2 Si 2 O 5 ) and lithium monosilicate (Li 2 SiO 3 ), or that contain at least a crystalline phase of lithium monosilicate (Li 2 SiO 3), in which a mean particle diameter of a particle showing a crystalline phase contained in the inorganic composition is 1 mum or less, a ring flexural strength is 300 MPa or more, and a surface roughness (an arithmetic mean roughness) thereof after a polishing process is 10AA or less.

Description

Technical field [0001] The present invention relates to an inorganic composition, which has a small particle diameter, good mechanical strength and excellent surface roughness with little change in the surface roughness of a substrate after surface treatment with acid or alkali, and has good adaptability to other materials Thermal expansion characteristics. In particular, it relates to a substrate for a magnetic recording medium used in various information magnetic recording devices, and particularly relates to a substrate for a disk-shaped information recording medium that has super-smooth surface, cleanability, and high strength among perpendicular magnetic recording media. By. In addition, the "information recording medium" in the present invention refers to a hard disk that can be used as a personal computer, and it can be used for fixed hard disks, mobile hard disks, card-type hard disks, digital video cameras or digital cameras, audio hard disks, and car navigation systems. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C10/04C03C10/14
Inventor 后藤直雪八木俊刚岸孝之
Owner OHARA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap