High viscosity modified asphalt for water permeable pavement and preparation method thereof

A technology of permeable pavement and modified asphalt, applied in building components, building insulation materials, buildings, etc., to achieve good dispersion and stability

Inactive Publication Date: 2007-07-04
SHANGHAI QUNKANG ASPHALTUM TECH CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, modified asphalt for water-permeable pavem...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] Take 100 kg of base asphalt with a penetration of 300, heat it to 180°C, add 8 kg of styrene-ethylene / butylene-styrene block copolymer (SEBS), 8 kg of petroleum resin and 2 kg of polyethylene wax in sequence, A powerful mixer was used to stir for 6 hours at a stirring speed of 200 rpm to prepare modified asphalt, and the results are shown in Table 1.

[0015] Index of modified asphalt

[0016] It can be seen from the table that high-performance modified asphalt is prepared, the viscosity at 60 degrees is greater than 20,000 Pa.s, and the PG classification reaches 82-28. High-performance modified asphalt can be used for OGFC, and it can also be used for bridges. Surface pavement, stress absorbing layer and other special occasions.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high viscosity modified asphalt which wherein the asphalt comprises the following constituents (by weight ratio): asphalt 100, styrene-polyethylene / butylene-styrene segmented copolymer 3-12 having an average molecular weight of 30-350 thousand, petroleum resin 5-30 with a softening point of 70-150 deg C, polyethylene wax 1-6 having an average molecular weight of 500-15000 and a softening point of 90-160 deg. By mixing styrene-ethane/butylenes-styrene segmented copolymer, petroleum resin and polyethylene wax into the asphalt, high viscosity, good dispersity and stability can be achieved, the PG classification can reach 82-28. The obtained high-performance modified asphalt can be used for both the general water seeping pavements, and specific sites such as bridge pavement and stress absorption layer.

Description

technical field [0001] The invention relates to the technical field of high-viscosity modified asphalt for water-permeable pavement. Background technique [0002] High-viscosity asphalt refers to asphalt with a viscosity greater than 20,000 Pa.s at 60°C, which is suitable for paving traffic roads and permeable roads. High-viscosity asphalt is currently mainly prepared by adding polymers to petroleum asphalt. Adding polymers to modify petroleum asphalt can significantly improve the high and low temperature performance of asphalt, and provide high temperature anti-rutting and low temperature anti-cracking capabilities of asphalt pavement. However, due to the differences in molecular weight and viscosity between polymers and asphalt, it is difficult to disperse polymer-modified asphalt; at the same time, because most polymers are completely compatible with asphalt, and there is a density difference, resulting in the modification of asphalt systems. The storage stability at hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L95/00E01C7/18C08L53/02C08L57/02C08L23/06
Inventor 黄子章
Owner SHANGHAI QUNKANG ASPHALTUM TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap