Blends containing macrocyclic polyester oligomer and high molecular weight polymer

Abstract

The invention provides blends of macrocyclic polyester oligomer (MPO) with high-molecular-weight polymer and polymerization catalyst as friable, one-component, ready-to-polymerize materials with long shelf life. The invention also provides methods for preparation and use of the blend materials. The blends are used, for example, in the production of thermoplastics via low-pressure processes, such as rotational molding and powder coating, without modification of existing equipment. The blends are particularly useful where it is desired to exploit the ability to polymerize and crystallize MPO isothermally, but where the melt viscosity of unfilled MPO is too low for use in existing equipment.

Description

PRIOR APPLICATIONS [0001] This application is a continuation-in-part of U.S. patent application Ser. No. 10 / 408,753, filed on Apr. 7, 2003, which is a continuation of U.S. patent application Ser. No. 10 / 195,853, filed on Jul. 15, 2002, and issued as U.S. Pat. No. 6,639,009, which is a continuation of U.S. patent application Ser. No. 09 / 754,943, filed on Jan. 4, 2001, and issued as U.S. Pat. No. 6,420,047, which is a continuation-in-part of U.S. patent application Ser. No. 09 / 535,132, filed on Mar. 24, 2000, and issued as U.S. Pat. No. 6,369,157, which claims benefit of U.S. Provisional Patent Application No. 60 / 177,727, filed on Jan. 21, 2000, the descriptions of which are incorporated by reference herein in their entirety. This application is related to the commonly-owned U.S. patent application entitled, “Intimate Physical Mixtures Containing Macrocyclic Polyester Oligomer and Filler,” by Takekoshi et al., filed under Attorney Docket No. CYC-051, on even date herewith, the descrip...

AI Technical Summary

Benefits of technology

[0009] The invention provides blends of macrocyclic polyester oligomer (MPO) with high-molecular-weight polymer and polymerization catalyst as friable, one-part, ready-to-polymerize materials with long shelf life. Components manufactured from these blends exhibit improved ductility and toughness.

[0010] Blend materials of the invention are particularly well-suited for use in low-pressure processes such as rotational molding and powder coating, without modification of existing equipment. The presence of the polymer in the blend increases the melt viscosity of the blend without adversely affecting the friability of the blend, without significantly decreasing the rate of polymerization of the blend, and without affecting the ability of the blend to polymerize and crystallize essentially isothermally. Furthermore, the presence of high-molecular-weight polymer in the blend improves the toughness and ductility of the polymerized product.

[0011] This combination of attributes is unexpected, for example, because adding a viscosity-enhancing agent to a polymerization reaction mixture typically reduces its rate of polymerization and may unacceptably reduce the friability of the mixture prior to polymerization.

[0012] The invention provides methods for preparing the blends in order to adequately disperse the components without prematurely initiating polymerization. Blends prepared according to these methods exhibit long shelf lives and may be stored for weeks, months, or even years prior to use in a manufacturing process.

[0020] In yet another aspect, the invention provides a method for polymerizing an MPO, the method including the steps of: (a) providing a blend material that is stable at ambient conditions for at least one week, the blend material including an MPO, a polymerization catalyst, and a polymer; and (b) heating the blend material to polymerize the MPO. The blend material is preferably friable prior to the heating step. This provides improved handling and processibility, for example, in low-pressure processing methods. The method may be implemented as part of a manufacturing process including, for example, a rotational molding process, a powder coating process, a low-pressure molding process, a gas-assist molding process, a short-shot molding process, a co-injection molding process, a reaction-injection molding process, a blow molding process, a thermoforming process, or combinations thereof.

Problems solved by technology

This combination of attributes is unexpected, for example, because adding a viscosity-enhancing agent to a polymerization reaction mixture typically reduces its rate of polymerization and may unacceptably reduce the friability of the mixture prior to polymerization.

Blends prepared according to these methods exhibit long shelf lives and may be stored for weeks, months, or even years prior to use in a manufacturing process.