Orthopaedic Implant Fixation Using an In-situ Formed Anchor

Abstract

An orthopaedic implant fixation using a surgically created bone cavity as a mold for forming an anchor from an in-situ hardenable material. An in-situ formed anchor of the present invention is especially useful for attaching an implant to osteoporotic cancellous bone. The injectable nature of the in-situ formed anchor allows implants to be adapted to minimally invasive surgical techniques. The present invention can be adapted to numerous implants or implant system components to include fasteners, pins, nails, intramedullary nails, and suture anchors. Applications include bone fracture fixation, bone fracture prevention, and soft-tissue repair.

Description

CROSS-REFERENCE TO RELATED APPLICATIONS[0001]This application claims the priority of U.S. Provisional Patent Application Ser. No. 60 / 336,557 filed Nov. 1, 2001.FIELD OF THE INVENTION[0002]The present invention generally relates to orthopaedic implants and, more particularly, to fixation of orthopaedic implants to bone.BACKGROUND OF THE INVENTION[0003]Bone structures are typically comprised of two types of bone, cortical bone and cancellous bone. Cortical bone can be characterized as a rigid and dense material, whereas cancellous bone can be characterized as a structured material with a high degree of visible porosity. Cortical bone and cancellous bone combine to form structures that are strong and lightweight. However, strength can be compromised by osteoporosis, a metabolic disease characterized by a decrease in bone mass. It is estimated that osteoporosis affects approximately 15-20 million people in the United States. Although osteoporosis can affect persons of all ages and both ...

AI Technical Summary

Benefits of technology

"The present invention is about improving the fixation of implants to bone, especially in cases of osteoporotic bone. It involves using a surgically created bone cavity as a mold to form an anchor from an in-situ hardenable material. The invention has several advantages, including the ability to use low pressures to fill a large bone cavity, the use of a wide range of in-situ hardenable materials, and the potential for simpler and low-pressure injection systems. The invention can be applied to various implants and can be used in bone fracture fixation, prevention, and soft-tissue repair."

Problems solved by technology

However, strength can be compromised by osteoporosis, a metabolic disease characterized by a decrease in bone mass.

Osteoporosis leads to skeletal fractures under light to moderate trauma and, in its advanced state, can lead to fractures under normal physiologic loading conditions.

Whether treating a fracture associated with osteoporosis or another disorder of the musculoskeletal system, implant attachment to weakened osteoporotic bone can be problematic.

Inadequate attachment of an orthopaedic implant to osteoporotic bone can result in less effective, or ineffective implant fixation.

Tightening bone screws is generally subjective and the appropriate fixation is especially difficult to judge when securing a bone screw to osteoporotic cancellous bone.

Over-tightening can lead to stripping of bone and inadequate fixation, while under-tightening can also lead to inadequate fixation.

These time consuming repair techniques have experienced some success; however, the necessity for repair emphasizes the potential ineffectiveness of screw thread purchase in osteoporotic bone.

Also, bone screws can occasionally loosen, losing their effectiveness.

Further, loose bone screws can ultimately back-out and migrate to an undesirable position or location.

Foremost, the addition of apertures to a screw thread substantially weakens the bone screw.

Another disadvantage is the potential for uneven distribution of bone cement within cancellous bone, caused in part by bone pore regions not directly adjacent to apertures receiving a disproportionate amount of the injected cement.

In addition, extruding directly into bone can require relatively high pressures depending on the bone characteristics and the viscosity of the injectable material.