Single-Component dental composition containing silane coupling agent and acidic group-containing polymerizable monomer

Abstract

The present invention provides a one-component dental adhesive composition which can exhibit excellent adhesion to both materials of a dental ceramics and an organic composite containing an inorganic compound, and is excellent in can-stability. More particularly, the present invention provides a one-component dental adhesive composition comprising 1 to 60 parts by weight of (a) a silane coupling agent, 1.0 to 20.0 parts by weight based on 100 parts by weight of the (a) component of (b) an acidic group-containing polymerizable monomer, and 28 to 99 parts by weight of (c) a volatile organic solvent.

Description

TECHNICAL FIELD[0001]The present invention is a single-component dental adhesive composition which exhibits excellent adhesion to both materials of a dental ceramics and an organic composite containing an inorganic compound (hereinafter, referred to as composite material in some cases), and is excellent in can-stability.BACKGROUND ART[0002]In a restorative dental material, inorganic materials, and composites of inorganic-organic composite materials are used in many cases, a representative of which is a dental porcelain (main component is silicon dioxide), an alumina core, a zirconia core, and a composite. The composite is obtained by mixing an inorganic powder and a resin into a paste. Alternatively, metal materials are also used.[0003]Previously, in adhesion of them, there was a trial to improve adhesion of a surface using a silane coupling agent, and a trial to improve adhesion of a surface using an acidic monomer. The silane coupling agent is known to improve adhesion to a materi...

AI Technical Summary

Benefits of technology

[0036]By using the dental adhesive composition of the present invention, excellent adhesiveness and durability can be exhibited on both materials of a dental ceramics, and an organic composite containing an inorganic compound and, further, can-stability is excellent, and handling is simple. Particularly, adhesion on silica-based, alumina-based and zirconia-based dental materials, and non-noble metals, and inorganic organic composites is excellent.

[0037]As specific utility of the dental adhesive composition of the present invention, the composition is used in adhesion with a resin-based material when any of a dental restoration / a dental restorative material / a dental device is a dental ceramics containing silicon dioxide as a main component, a dental ceramics containing aluminum dioxide and zirconium dioxide as a main component, a resin-based material containing a ceramics or an inorganic filler, or a dental restoration made of a non-metal material, in adhesion between any of a dental restoration / a dental restorative material / a dental device.

[0038]The dental adhesive restorative material is such that a dental restorative material itself is made to have adhesiveness using the technique of the present invention. Specifically, the material is an adhesive composite resin for a facing crown or fracture restoration.

[0039]By using the dental adhesive composition of the present invention, a dentist can simply implement an adhering work without selecting an adherend. In addition, a handling method is entirely the same as that of various adhesive compositions which have been used until now. That is, although the composition is an adhesive composition having essentially entirely new function, since the using method is the same, it is easily accepted by a dentist who is a user, and is advantageous to whole dental therapy.

[0040]Since the dental adhesive composition in the present invention is a one-component adhesive composition, handling is simple. In this regard, previously, since the composition was in a two-component mixed-type merchandise form, a mixing procedure was necessary upon use, a procedure was troublesome, working was time-consuming, and many points were unknown, as whether an appropriate mixing ratio of two components is maintained, and a sufficient mixing procedure has been done or not was unclear, and a technical error was easily generated, causing a loss.

[0041]The present invention can be also used as a primer, and can be also used simultaneously with other adhesive.

Problems solved by technology

However, usually, since the silane coupling agent and the acidic monomer can not be preserved in the same solvent for a long period of time, two kinds of materials must be used by mixing them immediately before use.

However, it is difficult that the silane coupling agent and the acidic monomer coexist, and they must be mixed before use.

However, a silane coupling agent is deteriorated by a phosphonic acid group-containing (meth)acrylate-based monomer, and it is difficult to stably exhibit the adhering effect for a long period of time.

And, it is difficult that the silane coupling agent and the acidic monomer coexist, and they must be mixed before use.

However, this adhesive has no adhesion to a porcelain, and has a primer composition such that two components must be mixed before adhesion.

JP-A No. 2000-248201 discloses a composition which exhibits sufficient adhesion to any of a base metal alloy, a noble alloy, and a ceramics, but when a silane coupling agent and an acidic group-containing polymerizable polymer are used as a single-component composition, a serious defect arises regarding can-stability of the single-component composition.

JP-A No. 2002-265312 discloses the technique of composition which exhibits sufficient adhesion to any of a tooth substance, a base metal alloy, a noble metal alloy, and a ceramics, but when a silane coupling agent and an acidic group-containing polymerizable monomer are used as a single-component composition, a serious defect arises regarding can-stability of the single-component composition.