Electrode slurry mixing process

An electrode slurry and mixer technology, applied in mixers, mixers with rotating containers, chemical instruments and methods, etc., can solve the problems of long mixing time and sufficient mixing of electrode slurries, so as to improve the discharge of large currents. performance, improve labor efficiency, and overcome the effect of high current performance

Inactive Publication Date: 2008-11-26
BYD CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the shortcomings of the prior art that the mixing time is long and the electrode slurry cannot be fully mixed, and to provide an electrode slurry mixing method that has a short mixing time and can fully mix the electrode slurry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrode slurry mixing process
  • Electrode slurry mixing process
  • Electrode slurry mixing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] This example is used to illustrate the electrode slurry mixing method provided by the present invention.

[0025] Put 10 kg of lithium cobalt oxide powder into figure 1 In the four ball milling tanks of the planetary ball mill shown, each tank contains 2.5 kg, and 12 agate balls with a diameter of 20 mm, 200 with a diameter of 10 mm and 1800 with a diameter of 6 mm are placed in each tank , Grinding for 60 minutes at a rotation speed of 250 rpm and a revolution speed of 350 rpm to obtain a refined and homogenized lithium cobalt oxide powder.

[0026] Then the resulting refined and homogenized lithium cobalt oxide powder and 0.5 kg of acetylene black, 4.0 kg of N-methylpyrrolidone (NMP), and 0.5 kg of polytetrafluoroethylene (PVDF) are equally divided into four parts and put into four ball mills mixing in a tank, and then continue grinding for 120 minutes at an autorotation speed of 280 rpm and a revolution speed of 360 rpm to obtain the electrode slurry S1.

Embodiment 2

[0028] This example is used to illustrate the electrode slurry mixing method provided by the present invention.

[0029] 8.5 kilograms of spherical nickel hydroxide powder are evenly loaded into such as figure 1 In the four ball milling jars of the planetary ball mill shown, put 10 agate balls with a diameter of 20 mm, 150 agate balls with a diameter of 10 mm, and 1200 agate balls with a diameter of 6 mm in each ball mill at 250 rpm The rotation speed and the revolution speed of 350 rev / min were ground for 70 minutes to obtain refined and homogenized spherical nickel hydroxide powder.

[0030] Then the spherical nickel hydroxide powder of gained refinement and homogenization is mixed with 75 grams of titanium dioxide, 200 grams of carbon black, 100 grams of polytetrafluoroethylene, 5 grams of hydroxypropyl methylcellulose and 1 kilogram of deionized water respectively in Mix in a ball mill jar, and then continue to grind for 140 minutes at an autorotation speed of 280 rpm and...

Embodiment 3

[0032] This example is used to illustrate the electrode slurry mixing method provided by the present invention.

[0033] Load 0.6 kg of hydroxymethyl cellulose, 1.5 kg of styrene-butadiene rubber (SBR) latex, 2.8 kg of graphite and 3.8 kg of water into the figure 1 430 grams of zinc oxide, 1.5 kilograms of titanium dioxide, 3.5 kilograms of carbon black, 2.0 kilograms of polytetrafluoroethylene, 100 grams of hydroxypropyl methylcellulose and 2 kilograms of The ion levels are put into the other two ball milling jars of the ball mill, and 30 agate balls with a diameter of 20 mm, 300 agate balls with a diameter of 10 mm, and 2800 agate balls with a diameter of 6 mm are placed in each ball mill, and the ball mills are respectively covered. Grinding at the rotation speed of 150 rev / min, the revolution speed of 200 rev / min behind the can cover plate for 0.5 hour, obtain the negative electrode slurry of refinement and homogenization, wherein the negative electrode slurry containing g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The electrode slurry mixing process is to mix materials constituting electrode slurry in a planetary ball mill. The electrode slurry mixing process can produce electrode slurry capable of raising the great current discharge performance, capacity and cycle performance of cell, and can shorten the electrode slurry mixing time and raise production efficiency greatly.

Description

technical field [0001] The invention relates to a material mixing method, in particular to a mixing method of electrode slurry. Background technique [0002] At present, the mixing of battery electrode slurry is mainly carried out in conventional magnetic stirrer, mechanical stirrer and other mixing equipment with only a single mechanical stirring method, including the binder, solvent, conductive agent and active material required in the electrode slurry Powder, etc. are simply mechanically stirred and mixed to make a slurry. Obviously, this simple mechanical stirring cannot achieve sufficient mixing of the slurry, so that the uniformity of the slurry cannot be guaranteed, resulting in poor high-current discharge performance, low capacity and poor cycle performance of the resulting battery. Moreover, it takes a long time to mix the slurry in this way, usually more than 6 hours. [0003] At present, there is a planetary ball mill on the market. The structure of the ball mil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B02C17/08B01F9/00
Inventor 王建军渠冰杜显忠李亚宾
Owner BYD CO LTD