Efficient modifying method for wollastonite powder

A wollastonite powder and modification technology, applied in chemical instruments and methods, inorganic pigment treatment, dyed low molecular organic compound treatment and other directions, can solve the problems of cumbersome process, long time consumption, etc., and achieve simple process, simple process and wear value. reduced effect

Inactive Publication Date: 2009-08-26
SHANXI TAIHUA TRADE
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the traditional method, the surface coating of natural wollastonite mineral powder mostly adopts a wet process. After coating, it needs to go through processes such as filtering, washing, drying, and breaking up. The modified mineral powder, as a filler, still needs to add water to prepare a certain concentration of slurry after it enters the paper mill, and it can be added to the wood pulp fiber after being gradually diluted.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1 (theoretical coating rate of calcium carbonate is 10%)

[0022] Prepare dry powder compound A first: take 500g and process it into Jilin Lishu county wollastonite powder A of 400 meshes, add 107.07g of industrial sodium carbonate E with a content of 99%, and then add 8g of dry powder compound C composed of cationic flocculant and bentonite , the cationic flocculant in the dry powder compound C is polyaluminum chloride, the addition amount is 0.8g, and the bentonite is 7.2g, all of which are put into the mixer, and the material is discharged after stirring for 3 minutes;

[0023] Then prepare dry powder compound B: get 500g and process it into 400 mesh Jilin Lishu county wollastonite powder B, add 112.12g of calcium chloride anhydrous F with a content of 99%, then add 2.45g of ethylenediaminetetraacetic acid disodium and The dry powder compound D composed of aluminum chloride, the ratio of the amount of disodium edetate and aluminum chloride is 3:10, all of ...

Embodiment 2

[0026] Embodiment 2 (theoretical coating rate of calcium carbonate is 20%)

[0027] Prepare dry powder compound A first: take 500g and process it into 600 mesh Qinghai Dulan county wollastonite powder A, add 214.14g of industrial sodium carbonate E with a content of 99%, and then add 12g of dry powder compound C composed of cationic flocculant and bentonite , wherein the cationic flocculant is polyamine-type cationic flocculant CFAM-30, its addition amount is 1.2g, bentonite is 10.8g, and then add 4.90g of dry powder compound D composed of disodium edetate and aluminum chloride , the ratio of the amount of disodium edetate and aluminum chloride is 3:10, all of which are put into the mixer, and the material is discharged after stirring for 3min;

[0028] Then prepare dry powder compound B: take 500g and process it into 600 mesh Qinghai Dulan county wollastonite powder B, add 331.31g of anhydrous calcium nitrate F with a content of 99%, put it all into a mixer, and discharge aft...

Embodiment 3

[0031] Embodiment 3 (theoretical coating rate of magnesium carbonate is 30%)

[0032] Prepare dry powder compound A first: take 500g and process it into 800 mesh Jiangxi Xinyu wollastonite powder A, add 321.21g of industrial sodium carbonate E with a content of 99%, add 16g of dry powder compound C composed of cationic flocculant and bentonite, in which cationic The flocculant is quaternary ammonium cationic flocculant ST-50, its addition amount is 1.6g, bentonite is 14.4g, and then add 8.75g of dry powder compound D composed of disodium edetate and aluminum chloride, ethylenediaminetetraacetic acid disodium and aluminum chloride The ratio of the amount of disodium amine tetraacetate and aluminum chloride is 3:10, all of it is put into the mixer, and the material is discharged after stirring for 3min;

[0033] Then prepare dry powder compound B: take 500g and process it into 800-mesh Jiangxi Xinyu wollastonite powder B, add 342.71g of anhydrous magnesium chloride F with a cont...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an efficient method for modifying wollastonite powder, in particular to a method for modifying dry powder ingredients and high-efficiency natural wollastonite powder. The modified wollastonite powder is particularly suitable for use as a filler in the plastic and papermaking industries , the problem to be solved is to provide a method for modifying natural wollastonite powder with dry powder ingredients, simple process, high modification efficiency, convenient use and low cost. A and dry powder compound B containing wollastonite powder, add an appropriate amount of water into the slurry mixing tank, then add dry powder compound A (or dry powder compound B), after stirring and fully dissolving, then gradually add the prepared dry powder Compound B (or dry powder compound A) is added and stirred until the slurry is neutral; the present invention can be widely used in industries such as plastics, rubber, papermaking, coating and paint, and has a good market application prospect.

Description

technical field [0001] The invention relates to an efficient method for modifying wollastonite powder, in particular to a method for modifying dry powder ingredients and high-efficiency natural wollastonite powder. The modified wollastonite powder is particularly suitable for use as a filler in the plastic and papermaking industries . Background technique [0002] Mineral powders are widely used in industries such as plastics, rubber, paper, coating and coatings due to their low price and the ability to improve the properties of matrix materials. However, due to the strong tendency of cleavage fracture along the cleavage plane during the crushing process of the mineral crystal, the surface of the mineral powder has a flat cleavage plane and sharp edges and corners. The flat cleavage surface makes the bonding force between the mineral powder and the matrix poor, and the sharp edges and corners are the stress concentration points during the material failure process, which can...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09C1/28C09C3/06C09C3/08
Inventor 王兆华
Owner SHANXI TAIHUA TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com