Multiple proportional layered composite manufactured amide paper of aramid fiber

A kind of aramid paper, multi-proportion technology, applied in the direction of papermaking, paper machine, layered products, etc., can solve the problems of low elongation at break, poor mechanical properties, affecting the use of aramid paper, etc., to achieve surface smoothness and uniformity , the effect of good interface bonding state

Inactive Publication Date: 2009-10-28
SHAANXI UNIV OF SCI & TECH
View PDF12 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Para-aramid paper products have good dimensional stability and insulation performance under high temperature and high humidity conditions, and are suitable for the preparation of printed circuit board substrates. However, due to the low elongation at break of para-aramid and its molecular Structural symmetry and orientation are high, and the mechanical properties of paper are poor, which affects the use of aramid paper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multiple proportional layered composite manufactured amide paper of aramid fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1, at first with aramid fibril and length is 8mm, the aramid chopped fiber that fineness is 7 deniers namely polym-phenylene isophthalamide fiber is respectively dispersed in water and loosened into slurry, made Mass concentration is 1% aramid fibrid slurry and mass concentration is 8% aramid fibrid slurry; then by mass percentage, 30% aramid fibrid slurry and 70% chopped fiber The slurry is mixed, and the core layer 2 is formed on the Internet by the common papermaking method; then 40% of the aramid precipitated fiber slurry and 60% of the chopped fiber slurry are mixed according to the mass percentage, and the ordinary papermaking method is used on the Internet. Surface layer 1 and bottom layer 3 are formed; the formed core layer 2, surface layer 1 and bottom layer 3 are compounded from top to bottom according to the order of surface layer 1, core layer 2 and bottom layer 3 respectively, wherein Surface layer 1 and bottom layer 3 account for 67% of the weig...

Embodiment 2

[0021] Embodiment 2, at first aramid fibrid and length are 12mm, and fineness is the aramid short-cut fiber of 3 deniers, namely polym-phenylene isophthalamide fiber, is respectively dispersed in water and loosened into slurry, and made Mass concentration is that 1.3% aramid fibrid slurry and mass concentration are 6% aramid fibrid pulp; then by mass percentage, 45% aramid fibrid pulp and 55% chopped fiber The slurry is mixed, and the core layer 2 is formed on the Internet by the ordinary papermaking method; then 60% of the aramid precipitated fiber slurry and 40% of the chopped fiber slurry are mixed according to the mass percentage, and the ordinary papermaking method is used on the Internet. Surface layer 1 and bottom layer 3 are formed; the formed core layer 2, surface layer 1 and bottom layer 3 are compounded from top to bottom according to the order of surface layer 1, core layer 2 and bottom layer 3 respectively, wherein The surface layer 1 and the bottom layer 3 accoun...

Embodiment 3

[0022] Embodiment 3, at first with aramid fibril and length is 4mm, the aramid chopped fiber that fineness is 10 deniers namely polym-phenylene isophthalamide fiber is respectively dispersed in water and loosened into slurry, made Mass concentration is that 1.2% aramid fiber fibrid slurry and mass concentration are 2% aramid fibrid fiber slurry; then by mass percentage, 20% aramid fibrid fiber slurry and 80% chopped fiber The slurry is mixed, and the core layer 2 is formed on the Internet by the common papermaking method; then 50% of the aramid precipitated fiber slurry and 50% of the chopped fiber slurry are mixed according to the mass percentage, and the ordinary papermaking method is used on the Internet Surface layer 1 and bottom layer 3 are formed; the formed core layer 2, surface layer 1 and bottom layer 3 are compounded from top to bottom according to the order of surface layer 1, core layer 2 and bottom layer 3 respectively, wherein Surface layer 1 and bottom layer 3 a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a multi-ratio layered composite paper-making aramid fiber amide paper and a preparation method thereof, comprising the following steps: separately dispersing and dissolving the aramid precipitated fiber and chopped fiber required for the surface layer, the bottom layer and the core layer in water into Slurry: Mix the aramid chopped fiber and precipitated fiber slurry required for the core layer, surface layer, and bottom layer separately, and form them on the Internet with ordinary papermaking methods; Composite sequentially down; pressing and drying; high temperature calendering molding. The invention can effectively improve the forming evenness of the paper sheet; change the structure of fiber distribution in the paper, wet forming compound makes each layer blend into one, fully utilizes the respective bonding, insulating and reinforcing advantages of different aramid fibers, and effectively Improve the mechanical properties such as tensile strength and tear strength of paper, improve the insulation performance and surface smoothness of paper.

Description

technical field [0001] The invention relates to meta-aramid fiber papermaking technology, belongs to the technical field of special synthetic fiber paper manufacturing, and in particular relates to a multi-ratio layered compound papermaking aramid fiber amide paper and a preparation method thereof. Background technique [0002] Aramid paper is a kind of high-temperature-resistant synthetic fiber paper. It is usually mixed with polyaramid chopped fibers and fibrids on a paper machine to make paper, and then made into aramid paper after hot pressing. Because of its excellent mechanical properties, insulation properties, temperature resistance, chemical resistance, etc., and light weight, it can be used as sheet insulation materials, heat insulation materials, packaging materials, honeycomb materials, filter materials for structural materials, motors, etc. It is widely used in aerospace, electronics, transportation and other industries. It can also be used as a laminate reinfor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H27/30B32B29/00D21H13/26D21H15/10D21G1/00
Inventor 张素风张美云
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com