Low-temperature thermal insulation paper, preparation method and application thereof

A low-temperature adiabatic and wet process technology, applied in papermaking, textiles and papermaking, synthetic cellulose/non-cellulose material pulp/paper, etc., can solve the problems of affecting product performance, increasing outgassing rate, and high comprehensive cost, reaching Long service life, increased contact thermal resistance, and good profiling

Active Publication Date: 2007-10-24
HANGZHOU FUSHIDA SPECIAL MATERIAL
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the glass filaments of woven glass cloth need to be added with wax or other oils during the fiber drawing process to prevent the fibers from sticking to each other, they need to undergo high-temperature degreasing treatment when used in multi-layer insulation structures. Once there are problems in the treatment process or treatment operations Improperly, the outgassing rate under vacuum will increase and affect the performance of the product, and in actual use, because the fiber diameter is relatively thick, it is easy for the fiber to enter the capillary pores of the human body and make the body itchy, thus bringing troubles to production and operation. There are many uncertain factors and difficulties, and the overall cost is high; while using other papers such as cigarette paper can save the trouble of degreasing, but it is not resistant to high and low temperatures (high temperature is easy to force the paper to age and low temperature is easy to make the paper fat. Brittle), some chemicals added in the paper production process will affect the final vacuum, thus affecting product performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature thermal insulation paper, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Example 1 Preparation of low temperature thermal insulation paper (refer to Figure 1)

[0034] (1) Add 100Kg of 49°SR (fiber diameter 0.1-1.0μm) ultra-fine alkali-free glass fiber into the beater and dilute it to 1.0% with water, add sulfuric acid to adjust the pH value to 2.5, and put it away after the fibers are all dispersed into single strands into the mixing pool;

[0035] (2) Continue to dilute the glass fiber put into the slurry mixing tank to 0.1% with white water, and add sulfuric acid to adjust the pH value to 2.5, and after stirring evenly, use a pump to send the slurry to the slurry storage tank after being treated by a conical slag remover;

[0036] (3) Pump the slurry from the slurry tank to the headbox, dilute it with white water to 0.05% again, and then take it online, after dehydration and pressing, it enters the drying tunnel for drying, and finally after trimming, stick it to the cylinder and coil it into rolls .

[0037] The above-mentioned finishe...

Embodiment 2

[0039] Example 2 Preparation of Low Temperature Thermal Insulation Paper

[0040] (1) Add 40Kg of 49°SR (fiber diameter 0.1-1.0μm) alkali-free glass fiber into the beater, dilute it to 0.5% with water, add sulfuric acid to adjust the pH value to 2.5, and put the fiber into the compound after all the fibers are dispersed into a single fiber pulp pool;

[0041] Take 60Kg of 54°SR alkali-free glass fiber (fiber diameter is 0.1-1.0μm), add it into the beater, dilute it with water to a concentration of 0.5%, add sulfuric acid and adjust the pH value to 2.5, and put it into the compound after all the fibers are dispersed into single fibers. pulp pool;

[0042] (2) Continue to dilute the glass fiber put into the pulp mixing tank to 0.05% with white water, and add sulfuric acid to adjust the pH value to 2.5, and after stirring evenly, use a pump to send the slurry to the slurry storage tank after being treated by a conical slag remover;

[0043] (3) Pump the slurry from the slurry t...

Embodiment 3

[0046] Example 3 Preparation of Low Temperature Thermal Insulation Paper

[0047] (1) Put 40Kg of 49°SR (fiber diameter 0.1-1.0μm) alkali-free glass fiber into the beater and dilute it to 2.0% with water, add sulfuric acid to adjust the pH value to 3.0, and put the fiber into the compound after all the fibers are dispersed into a single fiber pulp pool;

[0048] Take 60Kg of 54°SR alkali-free glass fiber (fiber diameter is 0.1 ~ 1.0μm), add it into the beater, dilute it with water to a concentration of 2.0%, add sulfuric acid and adjust the pH value to 3.0, and put it into the compound after all the fibers are dispersed into single fibers. pulp pool;

[0049](2) Continue to dilute the glass fiber put into the slurry mixing tank to 0.5% with white water, and add sulfuric acid to adjust the pH value to 3.0, and after stirring evenly, use a pump to send the slurry to the slurry storage tank after being processed by a conical slag remover;

[0050] (3) Pump the slurry from the s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention involves a low-temperature insulating paper, and relates to a preparation method of said low-temperature insulating paper and its applications. The invention prepares the low-temperature insulating paper with superfine alkali-free glass fiber and wet paper preparation process; the definite quantity of said low-temperature insulating paper is 10-20 g / m2 and the thickness is 0. 06 - 0. 09 g / m2. The preparation method of said low-temperature insulating paper includes: beating, stirring and scattering the superfine alkali-free glass fiber, and drying after stripping in paper machine, last coiling and preparing the products. The low-temperature insulating paper in the invention can be used for vacuum multi-layer insulation structure of copious cooling liquid accumulating container and complement pipes. The low-temperature insulating paper in the invention has good adiabaticity, the degassing ratio is small in vacuum, the profiling performance is good, and it has long life and wide uses.

Description

(1) Technical field [0001] The invention relates to a low-temperature heat-insulating paper, and also relates to a preparation method and application of the low-temperature heat-insulating paper. (2) Background technology [0002] At present, the insulation materials commonly used in the vacuum multilayer insulation structure of cryogenic liquid storage and transportation containers and their supporting pipelines are glass cloth, and other papers such as cigarette paper are used as substitutes. Since the glass filaments of woven glass cloth need to be added with wax or other oils during the fiber drawing process to prevent the fibers from sticking to each other, they need to undergo high-temperature degreasing treatment when used in multi-layer insulation structures. Once there are problems in the treatment process or treatment operations Improperly, the outgassing rate under vacuum will increase and affect the performance of the product, and in actual use, because the fiber...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H13/40D21H15/02D21H11/02
Inventor 应建明
Owner HANGZHOU FUSHIDA SPECIAL MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com