Preparation method of ceramic-metal composite material

A metal composite material and ceramic technology, which is applied in the field of preparation of ceramic-metal composite materials, can solve the problems of uneven mixing of the matrix and the second phase material, cracks in the composite material, etc., and achieves superior high temperature performance, low thermal conductivity, and comprehensive performance. Good results

Inactive Publication Date: 2007-10-31
SHANDONG IRON & STEEL CO LTD +1
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The powder metallurgy method is relatively simple to operate, but the disadvantage is that the matrix and the second phase material are n

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of ceramic-metal composite material
  • Preparation method of ceramic-metal composite material
  • Preparation method of ceramic-metal composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0078] Example 1 Preparation of Ceramic-Metal Composite Material

[0079] 1), matrix alloy ratio: 2Cr33Ni48WC10MoFe8 nickel-based metal is used as the matrix alloy, according to the composition ratio (weight ratio) in the 2Cr33Ni48WC10MoFe8 nickel-based metal, 2 parts of Cr powder, 33 parts of Ni powder, 48 parts of WC powder, Mo powder 10 parts and 8 parts of Fe powder are mixed evenly to prepare matrix alloy material;

[0080] 2), the preparation of composite ceramic phase particles: according to Ti powder and spherical Al 2 o 3 The particle weight ratio is 1:0.03, adding Ti powder to Al 2 o 3 Add PVB (polyvinyl butyral) alcohol solution binder to the granules, the amount of binder added is 5-10 ml per 100 grams of raw materials, stir and mix, so that the Ti powder is evenly coated on the oxidized The surface of aluminum particles is prepared as Al with a particle size of 0.8 mm and coated with Ti powder. 2 o 3 Composite ceramic phase particles.

[0081] 3), batching ...

Embodiment 2

[0093] Example 2 Preparation of Ceramic-Metal Composite Material

[0094] 1), matrix alloy ratio: 2Cr33Ni48WC10MoFe8 nickel-based metal is used as the matrix alloy, according to the composition ratio (weight ratio) in the 2Cr33Ni48WC10MoFe8 nickel-based metal, 2 parts of Cr powder, 33 parts of Ni powder, 48 parts of WC powder, Mo powder 10 parts and 8 parts of Fe powder are mixed evenly to prepare matrix alloy material;

[0095] 2), the preparation of composite ceramic phase particles: according to Ti powder and spherical Al 2 o 3 The particle weight ratio is 1:0.01, adding Ti powder to Al 2 o 3 Add PVB (polyvinyl butyral) alcohol solution binder to the granules, the amount of binder added is 5 ml per 100 grams of raw materials, stir and mix, so that the Ti powder is evenly coated on the alumina granules Surface, made of Ti powder-coated Al with a particle size of 1.0 mm 2 o 3 Composite ceramic phase particles.

[0096] 3), batching and granulation: According to the vol...

Embodiment 3

[0108] Example 3 Preparation of Ceramic-Metal Composite Material

[0109] 1), matrix alloy ratio: 2Cr33Ni48WC10MoFe8 nickel-based metal is used as the matrix alloy, according to the composition ratio (weight ratio) in the 2Cr33Ni48WC10MoFe8 nickel-based metal, 2 parts of Cr powder, 33 parts of Ni powder, 48 parts of WC powder, Mo powder 10 parts and 8 parts of Fe powder are mixed evenly to prepare matrix alloy material;

[0110] 2), the preparation of composite ceramic phase particles: according to Ti powder and spherical Al 2 o 3 The particle weight ratio is 1:0.05, adding Ti powder to Al 2 o 3 Add PVB (polyvinyl butyral) alcohol solution binder dropwise to the granules, add 10 ml of binder dropwise per 100 grams of raw material, stir and mix, so that the Ti powder is evenly coated on the alumina granules Surface, prepared as Ti powder-coated Al with a particle size of 0.5 mm 2 o 3 Composite ceramic phase particles.

[0111] 3), batching and granulation: According to t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparing method of ceramic-metallic composite material, which comprises the following steps: 1) allocating basal body alloy material; choosing 2Cr33Ni48WC10MoFe8 nickel base metal as basal body alloy; 2) preparing composite ceramic phase particle; choosing Al2O3 particle coating with Ti powder as composite ceramic phase particle; 3) mixing the basal body alloy material and composite ceramic phase particle with volume ratio at 1:0. 15-0. 45; pelleting; 4) press-forming; 5) vacuum-drying; 6) vacuum-clinkering; getting the product. This invention possesses lower ceramic-metallic composite material heat transfer capacity and predominance high temperature property, which is fit for new type material of rolled steel heater block.

Description

technical field [0001] The invention relates to a preparation method of a ceramic-metal composite material, in particular to a preparation method of a ceramic-metal composite material for a steel rolling heating furnace slide block. Background technique [0002] In steel rolling production, slabs are heated in furnaces before rolling. The slider supporting the heated slab is required to be able to withstand the thermal erosion of the furnace gas in the oxidation-sulfurization atmosphere at 1250-1400 °C, and to withstand the high-temperature sliding friction of the heavy slab. [0003] At present, the slider in the steel rolling heating furnace is made of cast 2Cr33Ni48W10Mo superalloy, but its thermal conductivity is high, and it is easy to form a "black belt" on the surface of the billet, which will lead to the uneven structure and product performance of the rolled steel plate, affecting The quality of medium and thick plate products is guaranteed. [0004] In order to so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C29/00C22C1/05B22F3/16
Inventor 刘福田陈启祥杜文华周波李文虎赵正李兆前
Owner SHANDONG IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap