Phenolic resin additive, phenolic resin with the additive and its prepn process

A technology of phenolic resin and additives, which is applied in the field of phenolic resin additives for wood-based panels and its preparation, can solve the problems of underutilized fenugreek, high price, affecting the curing performance and bonding strength of adhesives, etc. Achieve the effect of reducing the amount of resin, reducing the manufacturing cost, and reducing the content of phenolic resin

Inactive Publication Date: 2007-12-19
BEIJING FORESTRY UNIVERSITY
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the price of general protein is high, and the curing performance and bonding strength of the adhesive are often affected when the amount added is too much, which limits its use.
At present, there is a kind of fenugreek rich in protein a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0013] Example 1

[0014] 1) Prepare a sodium carbonate solution with a concentration of 5%. Add 25kg of fenugreek residue powder to 75kg of sodium carbonate solution, stir and heat to 70-80°C, react for 3-6 hours, cool to 30°C, and obtain a viscosity of 200 -400cP homogeneous fenugreek residue mucilage.

[0015] 2) Mix the obtained fenugreek residue mucus with an alkaline water-soluble phenolic resin with a molar ratio of phenol and formaldehyde of 1:2.1 in a ratio of 30:70 by weight to prepare a phenolic resin adhesive.

[0016] Among them, the performance index of fenugreek residue mucus is as follows:

[0017] Appearance: yellow-brown mucus

[0018] pH: 9-11

[0019] Solid content: 25-30%

[0020] The quality indicators of the adhesive are as follows:

[0021] Solid content 30-40%

[0022] pH 10.0-11.0

[0023] Viscosity (20℃) 150-300mPa·s

[0024] Free formaldehyde content <0.2%

[0025] Free phenol content <0.2%

[0026] Storage period 2-3 months

[0027] The ...

Example Embodiment

[0040] Example 2

[0041] 1) Prepare a sodium carbonate solution with a concentration of 5%, add 25kg of fenugreek residue powder to 75kg of the solution, stir and heat to 70-80°C, react for 3-6 hours, cool down to 30°C, and obtain a solution with a viscosity of 200-400cP Evenly fenugreek residue mucilage.

[0042] 2) The obtained fenugreek residue mucus and the same alkaline water-soluble phenolic resin as in Example 1 were uniformly mixed in a ratio of 50:50 by weight to make a phenolic resin adhesive.

[0043] The adhesive quality index:

[0044] Solid content 30-40%

[0045] pH 9.5-10.5

[0046] Viscosity (20℃) 150-300mPa·s

[0047] Free formaldehyde content <0.2%

[0048] Free phenol content < 0.2%

[0049] Storage period 60-90 days

Example Embodiment

[0061] Experimental example

[0062] Utilize the phenolic resin binder prepared by the phenolic resin of the embodiment of the present invention 1,2 method and comparative example 1 and comparative example 2 method respectively to manufacture seven-layer plywood, adopt following preparation process parameters:

[0063] Veneer: Poplar, thickness 1.6mm;

[0064] Glue adjustment: each glue type is added with flour according to 10% of the total weight, and mixed evenly;

[0065] Glue sizing: gluing on the core board, the amount of gluing is 220~300g / m 2 ;

[0066] Aging: 10-30 minutes;

[0067]Hot pressing: 130°C, 1.5MPa, 70s / mm.

[0068] The performance test results of the seven-layer plywood manufactured by the above process are shown in Table 1, and the bonding strength was measured according to the provisions of GB / T17657-1999 "Test Methods for Physical and Chemical Properties of Wood-based Panels and Decorated Wood-based Panels".

[0069] Table 1 Formaldehyde emission an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The phenolic resin adhesive additive is prepared through mixing 3-25 % concentration sodium carbonate solution in 70-80 weight portions and fenugreek slag powder in 20-30 weight portions, heating to 70-80 deg.c to react for 3-6 hr, cooling to 30 deg.c to obtain fenugreek adhesive with viscosity 200-400 mPa.s as the additive for phenolic resin adhesive. Alkaline water soluble phenolic resin and the fenugreek adhesive in the weight ratio of 50-90 to 10-50 are mixed to obtain the phenolic resin adhesive. The phenolic resin adhesive has low production cost, high adhesion strength and low formaldehyde releasing amount.

Description

technical field [0001] The invention relates to an additive for an adhesive, an adhesive based on an organic polymer compound containing the additive and a preparation method thereof, in particular to an additive for a phenolic resin for a wood-based panel and a preparation method thereof. Background technique [0002] With the rapid development of construction, decoration, packaging and other industries, the output of wood-based panels in my country has increased rapidly, and the adhesives for wood-based panels have also developed rapidly. The types of adhesives used for wood-based panels in my country are roughly the same as those in foreign countries. The commonly used "trialdehyde adhesives" include urea-formaldehyde resins, phenolic resins and melamine-formaldehyde resin adhesives, which occupy a dominant position. Among them, phenolic resin is an excellent and widely used glue type in wood adhesives, and phenolic resin is the preferred adhesive in the production of wea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08K11/00C08L61/06
Inventor 李建章周文瑞任强赵金平王建中陈欣赵强母军
Owner BEIJING FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka