Method for preparing special-purpose active carbon for removing mercury and products thereof
A manufacturing method, activated carbon technology, applied in chemical instruments and methods, other chemical processes, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0016] Example 1:
[0017] A manufacturing method of special activated carbon for mercury removal, which comprises the following steps: using 75% anthracite, 18% bituminous coal and 7% MgSO by weight percentage 4 , Mix and make powder, and then use the prepared mixed powder, according to the weight percentage, use powder 65%, pitch 5%, coal tar 27% and water 3% to mix well, and then press into strips After drying, carbonization, activation, crushing / sieving, take the finished product and soak it with more than 90% concentrated sulfuric acid for 8 hours. After the sulfuric acid is washed and recovered, the pH is adjusted to 8 with NaOH, and finally dried and then sieved. to make.
[0018] The carbonization conditions in the carbonization step are that the temperature of the end of the carbonization furnace is controlled at 280-300°C, the temperature rise rate is 3-10°C / min, and the amount of feed is that the volume occupied in the furnace is 4%-10 of the total space of the furnace ...
Example Embodiment
[0019] Example 2:
[0020] A manufacturing method of special activated carbon for mercury removal, which includes the following steps: using 70% anthracite, 25% bituminous coal, 5% MgO or MgSO by weight percentage 4 Or 2% MgO and 3% MgSO 4 , Mix and make powder, and then use the prepared mixed powder, according to the weight percentage, use powder 60%, pitch 7%, coal tar 30% and water 3% to mix well, and then press into strips After drying, carbonization, activation, and crushing / sieving, take the finished product and soak it with more than 90% concentrated sulfuric acid for 10 hours. After the sulfuric acid is washed and recovered, the pH is adjusted to 6 with KOH, and finally dried and then sieved. to make.
[0021] Other conditions are the same as in Example 1.
Example Embodiment
[0022] Example 3:
[0023] A manufacturing method of activated carbon special for mercury removal, which comprises the following steps: according to weight percentage, 80% anthracite, 16% bituminous coal and 4% MgO are mixed to make powder, and then the prepared mixed powder is used according to weight percentage , Use powder 60%, pitch 7%, coal tar 30% and water 3% to mix thoroughly and evenly, and then press into a strip, and then after drying, carbonization, activation, crushing / screening, take it on the sieve The finished product is soaked in more than 90% concentrated sulfuric acid for 8 hours. After the sulfuric acid is washed and recovered, the pH is adjusted to 7 with NaOH, and finally dried and sieved.
[0024] Other conditions are the same as in Example 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap