Flame-proof tarpaulin paper and preparation method thereof

A technology of flame retardant paper and flame retardant, which is applied in the field of paper manufacturing, can solve the problems of poor moisture resistance of flame retardant paper, and achieve high cost performance.

Inactive Publication Date: 2008-03-12
上海嘉龙纸业有限公司
View PDF0 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the prior art, there is the problem of poor moisture resistance of flame retardant paper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] a. (Paper surface spray impregnated) flame retardant liquid material formula combination:

[0045] 75-125 parts of ammonium sulfate, 10-50 parts of borax, 3-15 parts of urea, 0-5 parts of boric acid, 400-500 parts of water; total: 488-695 parts, solid content: 15-33%, pH=6- 8.9. The flame retardant liquid material can be heated and prepared in the mixing tank next to the production line site, and then the flame retardant liquid material is guided to the paper machine for feeding by pipelines.

[0046] b. (for spraying and impregnating paper surface) colloid liquid material formula combination:

[0047] 10-40 parts of starch, 10-15 parts of commercially available DS-SS830 paper surface sizing agent, 400-500 parts of water, total: 420-555 parts, solid content: 3.8-12%, pH=6-8. The colloid liquid material can also be heated and prepared in the mixing tank next to the production line site, and then the colloid liquid material is guided to the paper machine for feeding by ...

Embodiment 2

[0055] a. (Paper surface spray impregnated) flame retardant liquid material formula combination:

[0056] 100-150 parts of borax, 20-35 parts of phosphoric acid (85%), 3-15 parts of urea, 5 parts of aluminum hydroxide, 400-500 parts of water, total: 528-705 parts, solid content: 20-34%, pH =5~9; control the temperature of the liquid material for spraying at 70~96°C, and control the feeding flow rate at: 250~350kg / h.

[0057] b. (for spraying and impregnating paper surface) colloid liquid material formula combination:

[0058] 10-30 parts of starch, 10-15 parts of commercially available 400DS paper surface sizing agent, 400-500 parts of water, total: 420-545 parts, solid content: 3.8-10%, pH=7-8.5; control spraying The temperature of the liquid material is 60-95°C, and the feeding flow rate is controlled at: 250-350kg / h.

[0059] c. Spray and dipping construction on paper surface:

[0060] On a paper machine with a vehicle speed of 18-50m / min and a door width of 1.8m, straw ...

Embodiment 3

[0064] a. (Paper surface spray impregnated) flame retardant liquid material formula combination:

[0065] 10-25 parts of sodium dihydrogen phosphate, 20-50 parts of urea phosphate, 100-150 parts of borax, 3-15 parts of urea, 400-500 parts of water, total: 533-740 parts, solid content: 21-38%, pH =5~9; control the temperature of the liquid material for spraying at 70~90°C, and control the feeding flow rate at: 1000~1200kg / h.

[0066] b. (for spraying and impregnating paper surface) colloid liquid material formula combination:

[0067] 10-30 parts of starch, 10-15 parts of commercially available DS-SS830 paper surface sizing agent, 400-500 parts of water, total: 420-545 parts, solid content: 3.8-10%, pH=6-8.9; control The temperature of the liquid material for spraying is 60-95°C, and the feeding flow rate is controlled at: 1000-1200kg / h.

[0068] c. Spray and dipping construction on paper surface:

[0069] On a paper machine with a speed of 50-150m / min and a width of 2m, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of paper-making methods, and relates in specific to a non-fiber material that is added into paper pulp, in particular to cooperative utilization of paper impregnation materials in paper-making process. The invention relates to a flame retarding and moistproof paper as a paper cellular core material, as well as a relevant preparation method. The preparation method comprises a combined utilization mode of compounds of flame retardant and glutinous agent with high cost performance. Technical indexes of the paper are as follows: Oxygen index (OI): is more than or equal to 32; water content (percent): 6 to 14; quantitation (g / m2): in 50 to 120 or 130 to 450; transversal ring crush compression index (N is multiplied by m2 / g): anticipated as 2.5 to 5 or is more than or equal to 5. The paper-making method is characterized by impregnating flame retarding and fluid of glutinous agent (also named as sizing agent) on raw paper with a papermaking machine or / and a coating machine, and then, by being dried on a drying cylinder on the machine before being reeled and formed in a one-through way.

Description

technical field [0001] The invention belongs to the technical field of paper making methods, and in particular relates to non-fibrous materials added to pulp, especially the combined use of paper impregnating materials in the paper making process. Background technique [0002] The production and application of flame-retardant paper has a long history. With the development of social demand, the technical requirements for flame-retardant paper are getting higher and higher. Other physical properties are poor, such as: moisture resistance, toxicity, non-smoke, paper strength, etc., especially the moisture resistance is not satisfactory; and these types of flame-retardant paper also have the disadvantages of high production costs. [0003] Paper honeycomb core material is a new type of paper product that has been widely used in recent years. It can be used for cargo pallets in the logistics industry, and can also be used as core materials for interior walls and interior doors. I...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H23/22D21H25/06D21H23/04D21H21/34D21H21/16
Inventor 吴丹国胡永明
Owner 上海嘉龙纸业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com