Improved type slag splashing furnace protecting material and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of slag splashing to protect the furnace and furnace charge, which is applied in the manufacture of converters, sustainable waste treatment, solid waste management, etc., can solve problems such as furnace temperature drop, achieve the effects of increasing service life, reducing production costs, and protecting the environment
Inactive Publication Date: 2008-06-18
PANZHIHUA SHUNTENG GRP METALLURGY MATERIAL
View PDF1 Cites 29 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Since each slag splash takes about 6-8 minutes, it will cause adverse effects such as a drop in furnace temperature, which is obviously in
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0024] The mass percentage of MgO in the slag-splashing furnace charge is 66.3%, the total mass percentage of C is 9.6%, and the mass percentage of TiO2 is 2.5%.
[0025] The specific ratio is 8-5mm waste magnesia carbon brick 20%, 5-3mm waste magnesia carbon brick 10%, 3-0mm waste magnesia carbon brick 26%, 0-1mm high titanium slag 8%, 0-1mm titanium corundum 4 %, metal magnesium powder 0.9%, metal Al powder 1.4%, ferrosilicon 8%, <0.088mm fused magnesia 17.5%.
[0026] First weigh according to the above ratio, then mix the granules for one minute, then add 1 / 3 of the binder (caustic soda and water glass solution), mix for 1 minute, add fine powder and mix for another 3 minutes, then add the rest 2 / 3 of the binder, continue to mix for 3 minutes before discharging, compacted by a compactor and then compressed into a 40×40×50mm agglomerate for use.
Embodiment 2
[0028] The slag-splashing furnace charge MgO mass percentage content is 60.2%, the C mass percentage content is 15.1% and the TiO2 mass percentage content is 5.5%.
[0029] The specific ratio is 8-5mm waste magnesia carbon brick 25%, 5-3mm waste magnesia carbon brick 20%, 3-0mm waste magnesia carbon brick 30%, 0-1mm high titanium slag 12%, <88um titanium concentrate 4% , metal magnesium powder 0.5%, metal Al powder 2%, 0-1mm ferrosilicon alloy 6.5%.
[0030] First weigh according to the above ratio, then mix the granules for 2 minutes, add 1 / 3 of the binder (caustic soda and water glass solution), mix for 3 minutes, add fine powder, and mix for 3 minutes, add the remaining 2 / 3 3, continue to mix for 3 minutes before discharging, compacted by a compactor and then compressed into a 40 × 40 × 50mm agglomerate for use.
[0031] The performance comparison with the original product after testing and use is as follows:
[0032] Item Comparative Example Example 1 Example 2
[0033]...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides modified slag splashing maintenance material which can be used in multiple furnaces and a preparation method thereof. The invention is characterized in that the maintenance material comprises waste magnesium carbon bricks, complex deoxidizer (metal magnesium powder, metal aluminum powder and ferrosilicon alloy), raw materials containing TiO2, etc. The mass percentage is: 30 percent to 75 percent of MgO, 3 percent to 20 percent of total C, 2 percent to 10 percent of Al2O3, 1 percent to 10 percent of TiO2, 0.3 percent to 5 percent of Mg, 1 percent to 12 percent of Al, and the residue is SiO2. The complex deoxidizer amount obviously improves the reduction of the furnace temperature on FeO and improves the yield rate of the converter steelmaking. Specifically, nitrogen that is blown in when TiO2 and splashing slag are introduced helps to form the nitrogen titanium compound with high melting point, which improves the viscosity of the slag, enhances the adhesion force of the splashing slag material to MgO-C bricks of lining bricks of the converter and improves the maintenance effect. And the bonding strength of the splashing slag layer with the converter lining bricks is improved because of the join of TiO2. The obvious effect of the splashing slag maintenance technology is obtained that one time of the slag splashing can support 3 to 5 converters rather than just one before.
Description
technical field [0001] The invention relates to an improved slag-splashing furnace charge and its preparation method, in particular to a compound deoxidizer and TiO-containing 2 A slag-splashing furnace protection material prepared from raw materials that can be used repeatedly and a preparation method thereof belongs to the field of steel-making slag-splashing furnace protection technology and refractory materials. Background technique [0002] Furnace protection by slag splashing is an effective furnace protection technology for converters. Slag splashing is to leave part of the final slag after the converter is tapped, and adjust the viscosity and magnesium oxide content of the slag to an appropriate range by adding protection materials. Inject high-velocity nitrogen to spray the slag onto the furnace lining for cooling. Solidified to form a solid slag layer, as a consumable refractory layer, the slag layer reduces the mechanical erosion and physical and chemical erosion...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more