Baking-free brick made by the Yellow River mud and production method thereof

A technology for unburned bricks and sediment, which is applied to unburned bricks made of Yellow River sediment and its production field, can solve the problems of corroding cultivated land, occupying land, polluting the air, etc., and achieves convenient production, low cost, and environmental protection. The effect of pollution

Inactive Publication Date: 2008-09-03
李浩
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most fluorogypsum is directly stacked as a solid waste after a little neutralization treatment, but direct stacking not only occupies land, but also fluorogypsum is acidic, corrodes cultivated land, pollutes water sources, and dust will pollute the air, which is harmful to the environment. great damage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The burn-free brick of the present embodiment is made of the raw materials of following weight ratio,

[0023] Yellow River sediment: 60%

[0024] Fluorogypsum powder: 30%

[0025] Cement: 5%

[0026] Aluminum Potassium Sulfate: 3%

[0027] Acrylic powder for construction: 2%.

[0028] The production method is:

[0029] After mixing the Yellow River sediment, fluorine gypsum powder, cement, aluminum potassium sulfate and acrylic rubber powder for construction evenly, add water to make a mud slurry, put the slurry into a mold, and apply a pressure of 550KN on a press to form it. molded, dried, and finished.

[0030] According to the building material test method stipulated in the national standard, with reference to the standard of GB11945-89 autoclaved lime-sand brick and the standard of JC239-77 fly ash brick, the unburned brick physical size, bulk density, water absorption, mechanical properties (anti-burning brick) of the present invention Compression, flexural...

Embodiment 2

[0037] 2. Embodiment 2

[0038] The burn-free brick of the present embodiment is made of the raw materials of following weight ratio,

[0039] Yellow River sediment: 53%

[0040] Fluorogypsum powder: 30%

[0041] Cement: 10%

[0042] Aluminum Potassium Sulfate: 5%

[0043] Acrylic powder for construction: 2%.

[0044] The production method is:

[0045] After mixing the Yellow River sediment, fluorine gypsum powder, cement, aluminum potassium sulfate and acrylic rubber powder for construction evenly, add water to make a mud slurry, put the slurry into a mold, and apply a pressure of 550KN on a press to form it. molded, dried, and finished.

[0046] According to the building material test method stipulated in the national standard, with reference to the standard of GB11945-89 autoclaved lime-sand brick and the standard of JC239-77 fly ash brick, the unburned brick physical size, bulk density, water absorption, mechanical properties (anti-burning brick) of the present inven...

Embodiment 3

[0053] The burn-free brick of the present embodiment is made of the raw materials of following weight ratio,

[0054] Yellow River sediment: 64%

[0055] Fluorogypsum powder: 20%

[0056] Cement: 8%

[0057] Aluminum Potassium Sulfate: 3%

[0058] Acrylic building powder: 5%.

[0059] The production method is:

[0060] After mixing the Yellow River sediment, fluorine gypsum powder, cement, aluminum potassium sulfate and acrylic rubber powder for construction evenly, add water to make a mud slurry, put the slurry into a mold, and apply a pressure of 550KN on a press to form it. molded, dried, and finished.

[0061] According to the building material test method stipulated in the national standard, with reference to the standard of GB11945-89 autoclaved lime-sand brick and the standard of JC239-77 fly ash brick, the unburned brick physical size, bulk density, water absorption, mechanical properties (anti-burning brick) of the present invention Compression, flexural strengt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a burn-free brick and a production method thereof, particularly to a burn-free brick produced with the Yellow River silt and a production method thereof. The burn-free brick is produced by the extrusion of press machines after mixing the raw materials at a weight ratio as follows: 50-70% Yellow River silt; 20-30% fluoride gypsum powder; 5-10% cement; 3-5% aluminum potassium sulfate and 2-5% construction-used acrylic rubber powder. The invention makes full use of waste fluoride gypsum and a large number of Yellow River silt and is energy-saving and emission reducing and can prevent environmental pollution to meet ecological environmental protection requirements. The burn-free bricks have the advantages of low cost, high strength and good comprehensive performance and each performance are much higher than the relevant national standards of bricks for construction. The production method of has advantages of simple process and convenient production.

Description

technical field [0001] The invention relates to a burn-free brick and a production method thereof, in particular to a burn-free brick made from Yellow River silt and a production method thereof. Background technique [0002] At present, clay bricks are mostly used in buildings in our country, but clay bricks will consume a lot of cultivated land, and the country is restricting the use of clay bricks. [0003] The Yellow River has a high sediment content, and a large amount of sediment enters the sea, causing great waste. In recent years, cities along the Yellow River draw water from the Yellow River, and a lot of Yellow River sediment will accumulate on the banks of the Yellow River. Due to the low viscosity of the Yellow River sediment, the strength of the bricks made cannot meet the building requirements, so it is rarely used for brick making. [0004] Fluorogypsum is an industrial waste produced in the production of hydrogen fluoride in fluoride salt plants, and its mai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B14/06C04B22/14
Inventor 李浩赵子萱
Owner 李浩
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com