Method for producing alloyed hot-dipping galvanized steel sheet

A technology of hot-dip galvanized steel sheet and production method, applied in hot-dip galvanizing process, metal material coating process, coating, etc., can solve problems such as deterioration of corrosion resistance, coating powdering and peeling, surface defects, etc., to achieve The effect of excellent corrosion resistance, good welding performance and coating performance

Inactive Publication Date: 2008-09-03
MAANSHAN IRON AND STEEL COMPANY
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to meet these characteristics, some domestic iron and steel enterprises have developed alloyed hot-dip galvanized steel sheets. The production method of alloyed hot-dip galvanized steel sheets is to heat the hot-dip galvanized steel sheets in an alloying furnace at about 500°C after galvanizing. The alloying reaction between the surface pure zinc layer and the steel substrate forms an alloyed coating composed of Fe-Zn compounds, but the corrosion resistance, blackening resistance, and electrical conductivity of the alloyed hot-dip galvanized steel sheet are poor, and in The coating is prone to powdering and peeling during stamping deformation, and the galvanized layer is easily damaged, which not only deteriorates the corrosion resistance, but also easily causes surface defects, affecting the appearance after c

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0026] Example 1:

[0027] A production method of alloyed hot-dip galvanized steel sheet includes a strip steel production process, a strip steel galvanizing process, an alloying process, a leveling process, and a passivation process:

[0028] The strip galvanizing process is as follows: the temperature of the strip steel entering the zinc pot is 470°C, and the temperature of the zinc solution is 460°C; the zinc solution contains the following substances and mass percentages: Al: 0.14%, Pb≤0.003%, Fe: 0.05%, the remaining elements are less than or equal to 0.003%. In the galvanized layer, the δ1 phase of iron is FeZn 8 , The Γ1 phase at the interface of δ1 / steel matrix is ​​Fe 3 Zn 10 .

[0029] The alloying process is: the temperature of the alloying furnace is controlled at 490°C, and the alloying time is controlled at 10-15s;

[0030] The flattening process is: cooling the alloyed strip steel to below 40° C., and sending it to a finishing machine, so that the roughness of the a...

Example Embodiment

[0032] Example 2:

[0033] A production method of alloyed hot-dip galvanized steel sheet includes a strip steel production process, a strip steel galvanizing process, an alloying process, a leveling process, and a passivation process:

[0034] The strip galvanizing process is as follows: the temperature of the strip steel entering the zinc pot is 465°C, and the temperature of the zinc solution is 455°C; the zinc solution contains the following substances and mass percentages: Al: 0.13%, Pb≤0.003%, Fe: 0.04%, the remaining impurity elements are less than or equal to 0.003%. In the galvanized layer, the δ1 phase of iron is FeZn 9 , The Γ1 phase at the interface of δ1 / steel matrix is ​​Fe 3 Zn 10 .

[0035] The alloying process is as follows: the temperature of the alloying furnace is controlled at 500°C, and the alloying time is controlled at 10-15s;

[0036] The flattening process is: cooling the alloyed strip steel to below 40°C, and sending it to a finishing machine, so that the ...

Example Embodiment

[0038] Example 3:

[0039] A production method of alloyed hot-dip galvanized steel sheet includes a strip steel production process, a strip steel galvanizing process, an alloying process, a leveling process, and a passivation process:

[0040] The strip galvanizing process is as follows: the temperature of the strip steel entering the zinc pot is 465°C, the temperature of the zinc solution is 455°C; the zinc solution contains the following substances and mass percentages: Al: 0.12%, Pb≤0.003%, Fe: 0.03%, the remaining impurity elements are less than or equal to 0.003%. In the galvanized layer, the δ1 phase of iron is FeZn 10 , The Γ1 phase at the interface of δ1 / steel matrix is ​​Fe 3 Zn 10 .

[0041] The alloying process is: the temperature of the alloying furnace is controlled at 500°C, and the alloying time is controlled at 10-15s;

[0042] The flattening process is: cooling the alloyed strip steel to below 40°C, and sending it to a finishing machine, so that the roughness of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Roughnessaaaaaaaaaa
Roughnessaaaaaaaaaa
Roughnessaaaaaaaaaa
Login to view more

Abstract

The present invention discloses a production method for an alloyed hot-dip galvanizing steel plate, comprising the processes of strip steel producing, strip steel galvanizing, alloying, leveling and passivating, wherein in the strip steel galvanizing process, the temperature of strip steel entering a galvanized pot is 450 to 470 DEG C, and the temperature of zinc liquid is 455 to 465 DEG C. Compared with current technology, the method can produce a steel plant which not only has good welding property and coating property of a traditional alloyed hot-dip galvanizing steel plate, but also has superior corrosion-resistant property, black -patina-resistant property, conductivity and environment protecting property, and is particularly suitable for manufacturing kinescopes.

Description

technical field [0001] The invention relates to a production method of an alloyed hot-dip galvanized steel sheet, in particular to a production method of an environment-friendly zinc-iron alloyed hot-dip galvanized steel sheet used for a television picture tube. Background technique [0002] The production method of hot-dip galvanized steel sheet has experienced the evolution process of the early Sendzimir process, the improved Sendzimir process and the United States steel process. Affected by the production process, it is difficult for the products produced by the improved Sendzimir process to meet the requirements of alloyed steel plates regardless of their surface quality (including spangle structure) or the range of steel types that can be produced; in addition, the post-treatment section of the Sendzimir process The production of environmentally friendly alloyed hot-dip galvanized steel sheets is generally not considered in the design, so the equipment configuration in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C2/06C23C2/40
Inventor 杨兴亮刘劼赵云龙胡士幸章一樊叶明成
Owner MAANSHAN IRON AND STEEL COMPANY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products