Chlorinated rubber coating modified by acroleic acid and method for preparing same

A chlorinated rubber and acrylic technology, applied in rubber derivative coatings, wax coatings, epoxy resin coatings, etc., can solve the problems of discoloration and chalking, the coating is prone to pitting corrosion, the coating is peeled off, etc., and the cost performance is achieved. High, excellent physical and mechanical properties, simple process effect

Inactive Publication Date: 2010-07-28
TIANJIN BO XING ENG SCI & TECH LIMITED COMPANY OF CNPC +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The surface of the steel structure in the existing marine corrosive environment is coated with synthetic resin coatings. The disadvantages are that the salt spray resistance and light aging resistance are not good, and the coating is prone to pitting and discoloration. For internal and external peeling, the artificial accelerated salt spray test of the synthetic resin coating is generally 500h, and the artificial accelerated light aging test is generally 600h

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The invention discloses a method for producing an acrylic modified chlorinated rubber paint. In a stainless steel bucket, by 1 part by weight of chlorinated rubber, the chlorinated rubber of 1 part by weight, the chlorinated paraffin of 0.005 parts by weight, the epoxy resin of 0.008 parts by weight, the xylene of 0.05 parts by weight, the xylene of 0.01 parts by weight part of heavy aromatic hydrocarbon solvent, stirred evenly at a low speed at normal temperature, and after high-speed dispersion for 5 hours, added 0.005 parts by weight of fluorocarbon modified acrylic resin, 0.006 parts by weight of titanium dioxide, 0.01 parts by weight of talcum powder, 0.005 parts by weight of organoclay, after dispersing for 0.5h, grind it with a sand mill, and then add 0.005 parts by weight of acrylic resin under low-speed stirring, and disperse it evenly to make acrylic modified chlorinated rubber coating. The coating has the characteristics of single-component packaging and dryi...

Embodiment 2

[0014] The invention discloses a method for producing an acrylic modified chlorinated rubber paint. In a stainless steel bucket, by 1 part by weight of chlorinated rubber, the chlorinated rubber of 1 part by weight, the chlorinated paraffin of 1.03 parts by weight, the epoxy resin of 0.5 parts by weight, the xylene of 3.0 parts by weight, the xylene of 1.5 parts by weight 5 parts of heavy aromatic hydrocarbon solvent, stirred evenly at low speed at normal temperature, and after high-speed dispersion for 7 hours, added 0.045 parts by weight of fluorocarbon modified acrylic resin, 0.5 parts by weight of titanium dioxide, 0.8 parts by weight of talcum powder, 0.05 parts by weight of organoclay, after dispersing for 0.5h, grind it with a sand mill, and then add 0.4 parts by weight of acrylic resin under low-speed stirring, and disperse it evenly to make acrylic modified chlorinated rubber coating. The coating has the characteristics of single-component packaging and drying at room...

Embodiment 3

[0016] The invention discloses a method for producing an acrylic modified chlorinated rubber paint. In a stainless steel bucket, by 1 part by weight of chlorinated rubber, the chlorinated rubber of 1 part by weight, the chlorinated paraffin of 0.5 parts by weight, the epoxy resin of 0.08 parts by weight, the xylene of 2 parts by weight, the xylene of 0.9 parts by weight 4 parts of heavy aromatic hydrocarbon solvent, stirred evenly at low speed at normal temperature, and dispersed at high speed for 6 hours, then added 0.04 parts by weight of fluorocarbon modified acrylic resin, 0.06 parts by weight of titanium dioxide, 0.1 parts by weight of talcum powder, 0.04 parts by weight of organoclay, after dispersing for 0.5 hours, grind it with a sand mill, and then add 0.2 parts by weight of acrylic resin under low-speed stirring, and disperse it evenly to make acrylic modified chlorinated rubber coating. The coating has the characteristics of single-component packaging and drying at ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to acrylic acid modified chlorinated rubber coating and a method for preparing the same. The coating consists of: 1 weight portion of chlorinated rubber, 0.05 to 0.4 weight portion of acrylic acid resin, 0.005 to 1.03 weight portions of chlorinated paraffin, 0.08 to 0.5 weight portion of epoxy resin, 0.05 to 3.0 weight portions of dimethylbenzene, 0.01 to 1.5 weight portionsof heavy aromatic solvent, 0.005 to 0.045 weight portion of fluoro-carbon modified acrylic acid resin, 0.006 to 0.5 weight portion of titanium white powder, 0.01 to 0.8 weigh portion of talcum powder, and 0.005 to 0.05 weight portion of organoclay. The coating has the characteristics of single composition packing and drying film formation under normal temperature. A paint film of the coating has excellent physical property, chemical resistance, salt spray resistance and anti-photoaging property, and can be used for the protection and coating of the surfaces of steel structures under the environment of marine corrosion.

Description

technical field [0001] The invention relates to an acrylic modified chlorinated rubber coating used for protecting and coating the surface of a steel structure in a marine corrosion environment and a preparation method thereof. Background technique [0002] The surface of the steel structure in the existing marine corrosive environment is coated with synthetic resin coatings. The disadvantages are that the salt spray resistance and light aging resistance are not good, and the coating is prone to pitting and discoloration. For internal and external peeling, the artificial accelerated salt spray test of the synthetic resin coating is generally 500h, and the artificial accelerated light aging test is generally 600h. Contents of the invention [0003] The purpose of the present invention is to provide a kind of acrylic acid modified with simple manufacturing method, single-component packaging, and film-forming characteristics of normal temperature drying, and its coating film ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D115/02C09D133/00C09D163/00C09D191/06
Inventor 贺江张丽萍解蓓蓓郭晓军梁国珍李小朋黄骁卓
Owner TIANJIN BO XING ENG SCI & TECH LIMITED COMPANY OF CNPC