Conductive resin composition, conductive film comprising the same, and resistive-film switch employing the same

A technology of conductive resin and conductive film is applied in the field of conductive resin composition, conductive film obtained by using the resin composition, and resistive film switch obtained by using the conductive film, and achieves excellent adhesion, The effect of suppressing the increase of the surface resistivity and the decrease of the surface resistivity

Inactive Publication Date: 2008-11-19
NAGASE CHEMTEX CORPORATION
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, a conductive resin composition capable of forming a conductive film having all these properties cannot be provided at present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Conductive resin composition, conductive film comprising the same, and resistive-film switch employing the same
  • Conductive resin composition, conductive film comprising the same, and resistive-film switch employing the same
  • Conductive resin composition, conductive film comprising the same, and resistive-film switch employing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0121] As the aqueous dispersion of a composite of poly(3,4-ethylenedioxythiophene) and polystyrenesulfonic acid, Baytron PH500 manufactured by H.C. Starck (hereinafter referred to as aqueous dispersion (A)) was used. The electrical conductivity of this complex was measured and found to be 0.79 S / cm. In water dispersion (A) 10.4 parts (convert by solid content), add polyester resin aqueous dispersion (manufactured by Nagase Chemtex company, Gabsen ES-210) 3.0 parts (convert by solid content), melamine series cross-linking agent (Sumitomo Chemical production, Sumitex ResinM-3) 1.0 parts (converted by solid content), 20 parts of N-methylformamide, a small amount of surfactant, a small amount of leveling agent, an appropriate amount of water and modified methanol, stirred for 1 hour, Then, it filtered using the 400-mesh SUS sieve, and obtained the coating agent.

Embodiment 2

[0124] Except that the amount of the aqueous dispersion (A) is changed to 10.7 parts (converted by solid content), and the amount of the polyester resin aqueous dispersion is changed to 9.0 parts (converted by solid content), the same operation as in Example 1 , to prepare the coating agent.

Embodiment 3

[0126] As the aqueous dispersion of a complex of poly(3,4-ethylenedioxythiophene) and polystyrenesulfonic acid, Baytron PH510 manufactured by H.C. Starck (hereinafter referred to as aqueous dispersion (B)) was used. The electrical conductivity of this complex was measured and found to be 0.67 S / cm. A coating agent was obtained in the same manner as in Example 1, except that this water dispersion was used and the amount of the melamine-based crosslinking agent was changed to 3.0 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
electrical conductivityaaaaaaaaaa
Login to view more

Abstract

A conductive resin composition which contains a composite of a poly(3,4-dialkoxythiophene) and a polyanion, wherein the composite has a conductivity of 0.30 S / cm or higher. This composition is suitable for use in producing a conductive film comprising a conductive layer made of the composition. The conductive film is suitable for use in a resistive-film switch.

Description

technical field [0001] The present invention relates to a conductive resin composition applicable to a resistive film switch, a conductive film formed using the conductive resin composition, and a resistive film switch using the conductive film. Background technique [0002] The most common example of a resistive film switch is a touch panel. [0003] The touch screen is used for displaying images of display devices such as liquid crystal displays, cathode ray picture tubes, and electroluminescence (EL) displays. The touch screen is a kind of two-dimensional information resistive film switch. The touch screen is designed so that, for example, when any position on the screen is pressed with a finger or the tip of a pen, etc., the gap between the pressed position (conduction part) and the position of an electrode (such as a silver electrode) formed on a predetermined position of the touch screen is used. The resistance value obtained from the distance can be used to calculat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L65/00C08J7/04C08L101/12H01B1/20H01B5/14H01H13/712
CPCH01G11/48C08L101/12H01B1/20C08L65/00Y02E60/13H01H2201/036C08L2666/02C08G75/06C08G61/12
Inventor 森田贵之千种康男宫西恭子
Owner NAGASE CHEMTEX CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap