Baby blue zirconia ceramic preparation and product obtained thereby

A technology of zirconia ceramics and ultra-fine zirconia, which is applied to the preparation method of pink-blue zirconia ceramics and the fields of the obtained products, can solve the problem of not meeting individual needs, restricting the development of colored zirconia ceramics, and maintaining high temperature stability of pigments. Problems such as poor sex, to achieve the effect of bright color

Inactive Publication Date: 2009-07-08
北京晶莱陶瓷制品有限公司
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the very high sintering temperature of special ceramic materials, especially the sintering temperature of zirconia ceramic materials is higher than 1300°C in almost all cases, and most of the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～6

[0012] Ingredients are prepared according to the following table, and after ball milling, drying, sieving, kneading, injection, solvent degreasing, thermal degreasing, firing, rough processing, fine processing, and polishing, a pink-blue zirconia ceramic with bright color and luster is obtained.

[0013] Raw materials and process parameters Example 1 Example 2 Example 3 Example 4 Example 5 Example 6 Zirconia 92.5 92 91.5 93.5 93 92.5 Aluminum oxide 1.5 1.5 1.5 0.5 0.5 0.5 cobalt oxide 1.0 1.5 2.0 0.5 1.0 1.5 silica 4 4 4 3 3 3 Vanadium pentoxide 0.5 0.5 0.5 1.5 1.5 1.5 magnesium oxide 0.5 0.5 0.5 1.0 1.0 1.0 Sintering temperature (℃) 1480 1450 1430 1480 1450 1430 Holding time (min) 180 180 180 180 180 180

[0014] According to the products obtained in the above table, the test results of bending strength (three-point method), fracture toughness (unilateral notch beam ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing powderblue zirconia ceramics and prepared products. The method comprises: adopting superfine zirconia ceramic powder as base powder, adding industrial metal oxide including cobalt oxide, silicon dioxide, alumina, vanadium pentoxide and magnesia, and obtaining the powderblue zirconia ceramic products after weighing, ball milling, drying, sieving, mixing, injection, solvent degreasing, thermal degreasing, sintering, rough machining, finish machining and polishing, wherein the sintering temperature is between 1,430 and 1,480 DEG C, and the temperature preservation time is 180 minutes. The obtained products are bright-colored and stable, and can be widely applied in the fields of zirconia ceramic watches, zirconia ceramic ornamental articles and the like.

Description

technical field [0001] The invention belongs to the field of inorganic non-metallic materials (ceramics), in particular to a preparation method of pink-blue zirconia ceramics applied to watch accessories and jewelry and the prepared product Background technique [0002] With the development of the times, the timing function of watches is gradually being weakened, and the decorative function with clothing is gradually occupying a dominant position. High-performance colored zirconia ceramic watch accessories and jewelry products are characterized by their high hardness, wear resistance and toughness. Good quality, long-lasting color, no damage to the skin, high insulation, no metal and electroplating pollution, etc., are deeply loved by fashionable women. With the continuous enrichment of zirconia ceramic colors, it is bound to affect the development trend of watches and jewelry. However, due to the very high sintering temperature of special ceramic materials, especially the s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/48C04B35/622
Inventor 杨凯周焕忠任永国顾幸勇
Owner 北京晶莱陶瓷制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap