A two-photon three-dimensional optical storage material branched pyrimidine derivative and its synthesis method

A technology for optical storage materials and pyrimidine derivatives, which is applied in record carrier materials, optical record carriers, organic chemistry, etc., to achieve high yield, simple synthesis method, and improved storage effect

Inactive Publication Date: 2011-12-14
ANHUI UNIVERSITY
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This makes it possible to make optical discs for three-dimensional information storage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A two-photon three-dimensional optical storage material branched pyrimidine derivative and its synthesis method
  • A two-photon three-dimensional optical storage material branched pyrimidine derivative and its synthesis method
  • A two-photon three-dimensional optical storage material branched pyrimidine derivative and its synthesis method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] Taking R as ethyl as an example, non-limiting examples are described as follows:

[0031] 1. Preparation of intermediate (I)

[0032] Weigh 12g (0.016mol) of thiourea and dissolve it in 100mL of methanol, add 16g (0.016mol) of acetylacetone and 1mL of hydrochloric acid, and let it stand at room temperature for 40-50 hours, the solution turns yellow, and a large amount of bright yellow crystals precipitate out. After filtering and drying, 13.2 g of bright yellow crystals were obtained, with a yield of 75%. That is the intermediate (I) 2-mercapto-4,6-dimethylpyrimidine.

[0033] 2. Preparation of intermediate (II)

[0034] NaOH (4.0 g, 0.1 mol), 100 mL of water and 2-mercapto-4,6-dimethylpyrimidine (14.0 g, 100 mmol) were successively added into a 250 mL round bottom flask, and 9.4 g of 1 was added dropwise under stirring at room temperature, 2-Dibromoethane (0.05mol), continue to stir for 60-80 hours after dripping to obtain a large amount of gray solid, after filteri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A branched pyrimidine derivative of a two-photon three-dimensional optical storage material, characterized in that it has a compound shown in the following chemical formula: in the test, R is selected from ethyl or propyl or butyl or pentyl or hexyl or hydroxyethyl or Hydroxyethylcarboxylate or phenyl. The compound has a large two-photon absorption cross-section and good stability, and is an ideal organic two-photon three-dimensional optical storage material whether it is formulated into a solution or processed into a film.

Description

1. Technical field [0001] The invention relates to an organic two-photon three-dimensional optical storage material and a preparation method thereof, in particular to a kind of multi-branched pyrimidine derivatives of an organic two-photon absorption material that can be used in two-photon three-dimensional optical storage and a synthesis method thereof. 2. Background technology [0002] Organic materials with large two-photon absorption cross-sections have good application prospects in frequency upconversion lasers, optical clipping, photodynamic therapy, frequency upconversion fluorescence microscopy, three-dimensional optical information storage, and three-dimensional micromachining. aroused great interest of researchers. After more than 20 years of development, many two-photon absorbing materials with practical value have been discovered, and two-photon absorbing materials have entered the stage of practical research with practical significance. Among the many applicati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C07D239/38G11B7/244
Inventor 田玉鹏李林杨家祥李胜利张胜义金葆康周虹屏吴杰颖宋继梅孔林
Owner ANHUI UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products