Binder for magnesium carbonaceous fire-resistant material

A refractory material and binder technology, applied in the direction of asphalt material binder, binder type, aldehyde/ketone condensation polymer binder, etc., can solve the problems of single variety, unsatisfactory quality and high production cost, reaching Stable and reliable quality, obvious economic and social benefits, and the effect of reducing production costs

Inactive Publication Date: 2009-07-22
周惠兴
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the existing domestic refractory binders generally use thermoplastic or thermosetting phenolic resins. Manufacturers generally report that their production costs are high, the variety is single, and the quality is not ideal enough to meet the needs of the production of magnesia carbon-containing refractory materials. Therefore, research It is imperative to develop new binders for magnesia carbon-containing refractories

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A binder for magnesia carbon-containing refractories, which consists of the following materials in proportion by weight:

[0017] 100 parts of phenolic resin or aromatic polyester;

[0018] Coal tar pitch, 30% by weight of phenolic resin or polyamide resin;

[0019] Anthracene oil products of coal tar distillation, 55% by weight of coal tar pitch;

[0020] Alcohol solvent is 25% of the above weight sum.

Embodiment 2

[0022] A binder for magnesia carbon-containing refractories, which consists of the following materials in proportion by weight:

[0023] 100 parts of phenolic resin or aromatic polyester;

[0024] Coal tar pitch, 15% by weight of phenolic resin or polyamide resin;

[0025] Anthracene oil products of coal tar distillation, 50% by weight of coal tar pitch;

[0026] The ester solvent is 17% of the above weight sum.

Embodiment 3

[0028] A binder for magnesia carbon-containing refractories, which consists of the following materials in proportion by weight:

[0029] 100 parts of phenolic resin or aromatic polyester;

[0030] Coal tar pitch, 30% by weight of phenolic resin or polyamide resin;

[0031] Anthracene oil products from coal tar distillation, 60% by weight of coal tar pitch;

[0032] Benzene or tar fraction solvent is 32% of the above weight sum.

[0033] In the above embodiments, the coal tar pitch refers to a special pitch with a beta resin content ≥ 30% and a residual carbon content ≥ 60%.

[0034] The manufacturing method of the binder for magnesia carbon-containing refractories is: after the catalytic polycondensation reaction of phenol and formaldehyde is completed, coal tar pitch and anthracene oil are added, heated and stirred with a pressure of ≧0.4MPa, and the time is controlled at more than 60 minutes, and then Vacuumize and dehydrate by heating to make the water content <7%. When ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a bonding agent used for magnesia carbon-containing refractory materials , which consists of materials with weight proportions as follows: 100 proportions of phenolic resin; aromatic polyester and coal tar pitch with the weight accounting for 15-30% of the weight of the phenolic resin or polyamide resin; coal tar distillation anthracene oil product with the weight accounting for 50-60% of the weight of the coal tar pitch; and solvent with the weight accounting for 17-32% of the weight sum of the four materials. The beneficial effects are as follows: a series of products of the bonding agent used for the magnesia carbon-containing refractory materials are provided, and the production cost is reduced greatly, thus having obvious economic and social benefits. The product quality is stable and reliable, the performance of the bonding agent meets the standard of the existing bonding agent by inspection, and solid content and residual carbon amount are significantly higher than the existing bonding agent of the refractory materials, thus leading the performance indicators of the refractory materials to be improved.

Description

technical field [0001] The invention relates to a binder used in the refractory industry, in particular to a binder for magnesia carbon-containing refractory materials, referred to as LFQ binder. Background technique [0002] At present, the existing domestic refractory binders generally use thermoplastic or thermosetting phenolic resins. Manufacturers generally report that their production costs are high, the variety is single, and the quality is not ideal enough to meet the needs of the production of magnesia carbon-containing refractory materials. Therefore, research It is imperative to develop new binders for magnesia carbon-containing refractories. Contents of the invention [0003] The purpose of the present invention is to provide a binder for magnesia carbon-containing refractories, which greatly reduces production costs, greatly improves product quality, and has stable quality, which can meet the production requirements of magnesia carbon-containing refractories. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J161/10C09J167/00C09J195/00
Inventor 周惠兴
Owner 周惠兴
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products