Fiber-reinforced composite material cement board and preparation method thereof

A fiber reinforced cement and composite material technology, which is applied in the field of fiber reinforced composite cement board manufacturing, can solve the problems of large equipment investment, large water absorption rate of the board, easy deformation, etc. Effect

Active Publication Date: 2009-08-19
广德衡峰新型建材有限公司
View PDF0 Cites 46 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The process of making boards from the above materials is complicated, and the investment in equipment is large. Some boards have high water absorption and are easy to change when used outdoors. Some are expensive and difficult to popularize and apply.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber-reinforced composite material cement board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The preparation method of the fiber-reinforced composite material cement board of the present invention is realized through the following steps:

[0022] First lay the first layer of fiber-reinforced cement-based composite material 1 (the laying thickness is 3mm) in the prepared mold (size 1220×2440×8mm), and then lay the first layer of fiber-reinforced cement-based composite material 1 on the Lay the first layer of fiber mesh cloth 2 (the size is 1200×2400mm), and then lay the second layer of fiber reinforced cement-based composite material 3 (laying thickness is 6mm) on the laid first layer of fiber mesh cloth 2, and then Lay the second layer of fiber mesh cloth 4 (size is 1200 × 2400mm) on the laid second layer of fiber reinforced cement-based composite material 3, and then lay the third layer on the laid second layer of fiber mesh cloth 4. A layer of fiber reinforced cement-based composite material 5 (laying thickness is 3mm), and finally form a plate in the mould; ...

Embodiment 2

[0032] The preparation method of the fiber-reinforced composite material cement board of this embodiment is the same as Embodiment 1 except for the following features:

[0033] The components of the fiber-reinforced cement-based composite materials 1, 3, and 5 are: 33% of cement, 13% of hollow microspheres of 2500 mesh, 39% of quartz sand of 40-70 mesh, 0.5% of concrete water reducing agent, 0.3% of fiber, Water 12.2%, colorant 2%.

[0034] The fiber mesh cloth 2, 4 adopts metal fiber mesh cloth.

[0035] The fibers in the fiber-reinforced cement-based composite materials 1, 3, and 5 are metal fibers.

[0036] The colorant is iron oxide red.

[0037] The cement is 52.5R ordinary cement.

[0038] The vibrating table vibrated the mold with the plate base for 1.5 minutes.

[0039] The temperature inside the autoclave was 110°C.

[0040] The pressure of the autoclave is 0.8MPa.

[0041] The thickness of the second layer of fiber-reinforced cement-based composite material 3 i...

Embodiment 3

[0043] The preparation method of the fiber-reinforced composite material cement board of this embodiment is the same as Embodiment 1 except for the following features:

[0044] The components of the fiber-reinforced cement-based composite materials 1, 3, and 5 are: 31% of cement, 14% of hollow microspheres of 2500 mesh, 39% of quartz sand of 40-70 mesh, 0.55% of concrete water reducing agent, 0.35% of fiber, Water 12.5%, iron oxide yellow 2.6%.

[0045] The fiber mesh cloth 2, 4 adopts glass fiber mesh cloth.

[0046] The fibers in the fiber-reinforced cement-based composite materials 1, 3, and 5 are polymer fibers.

[0047] The coloring agent is iron oxide yellow.

[0048] The vibrating table vibrated the mold with the plate base for 3 minutes.

[0049] The cement is 42.5R sulfoaluminate.

[0050] The temperature in the autoclave was 100°C.

[0051] The pressure of the autoclave is 1.2MPa.

[0052] The thickness of the second layer of fiber-reinforced cement-based compo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a fiber composite material concrete board, which comprises the following steps: laying a first layer of slurry in a mould; laying a first layer of glass fiber grid cloth on the laid first layer of the slurry; laying a second layer of slurry on the laid first layer of the glass grid cloth; laying a second layer of glass fiber grid cloth on the laid second layer of the slurry; laying a third layer of slurry on the laid second layer of the glass fiber grid cloth; vibrating the mould by a vibration device; putting the mould into a steam autoclave; and performing autoclave leaving, demoulding, airing and final treatment to form the concrete board made of the fiber composite material. The invention also discloses a concrete board made of a fiber composite material. The method has the advantages of simple manufacturing process, little capital and equipment input and low cost; and the concrete board made of the fiber composite material has the advantages of low water absorbing rate, high strength, good toughness, high durability, and the like.

Description

technical field [0001] The invention relates to a manufacturing technology of a fiber-reinforced composite material cement board, in particular to a fiber-reinforced composite material cement board and a preparation method thereof. Background technique [0002] Over the past 20 years, there are roughly 7 categories of new fiber-reinforced cement-based composite materials developed and developed at home and abroad (mainly abroad), namely: 1. Metal fiber-reinforced cement-based composite materials; 2. Glass fiber-reinforced cement-based composite materials; 3. Synthetic fiber-reinforced cement-based composite materials; 4. Natural organic fiber-reinforced cement-based composite materials; 5. Carbon fiber-reinforced cement-based composite materials; 6. Hybrid fiber-reinforced cement-based composite materials; 7. High-performance fiber-reinforced cement-based composite materials . The process of making boards from the above materials is complicated, and the investment in equipm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B28B1/52B28B1/087B28B19/00B28B11/24B32B13/02B32B13/14E04C2/26E04C2/30C04B28/00C04B14/06C04B14/38
CPCC04B2111/00612C04B28/02
Inventor 刘谦江明榆刘扬杨君富
Owner 广德衡峰新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com