In-situ synthesis method for preparing tin-carbon/core-shell nano-particle fully filled carbon nano-tube composite anode material

A carbon nanotube composite and nanoparticle technology, which is applied in electrode manufacturing, battery electrodes, electrical components, etc., can solve problems such as uneven distribution, low filling efficiency, and low product structure purity, and achieve improved volume specific capacity and weight The effect of specific capacity

Inactive Publication Date: 2010-12-29
SHANGHAI UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the diameter of carbon nanotubes has a nanoscale size, and the length can reach more than microns, the filling material obtained by this method of filling nanoparticles from the openings at both ends of carbon nanotubes by using capillary action is in the cavity of carbon nanotubes. The distribution is very uneven and the filling efficiency is not high. Many of the target filling materials do not enter the lumen of carbon nanotubes but are loaded on the outer surface of carbon nanotubes, resulting in low structural purity of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • In-situ synthesis method for preparing tin-carbon/core-shell nano-particle fully filled carbon nano-tube composite anode material
  • In-situ synthesis method for preparing tin-carbon/core-shell nano-particle fully filled carbon nano-tube composite anode material
  • In-situ synthesis method for preparing tin-carbon/core-shell nano-particle fully filled carbon nano-tube composite anode material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A porous anodized aluminum film (pore size about 200nm) was placed in 1.0M SnCl 4 Place in the aqueous solution for 3 to 5 hours, then dry in an oven at 70°C for 5 hours, then place the aluminum oxide film in a tube furnace to heat, and feed 200 sccm with a volume percentage of 10% C 2 h 2 and 90%N 2 The mixed gas formed, after passing the mixed gas for 1 hour, began to heat up, heated to 650°C at a heating rate of 3-10°C / min, continued for 3 hours, continued to pass the mixed gas until the tube furnace naturally cooled to room temperature, and then used 6.0M Soak in NaOH aqueous solution for 1 hour to remove the aluminum oxide film, collect the remaining insoluble matter, wash with a large amount of deionized water, and dry the product. The final powder obtained is the product in which Sn@C core-shell nanoparticles are completely filled with carbon nanotubes. This product is in figure 1 Field Emission Scanning Electron Microscope (FESEM) images show that some nanopa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a method for preparing a tin-carbon / core-shell nano-particle fully filled carbon nano-tube composite anode material, which comprises the following steps: a porous anodic aluminaThe invention provides a method for preparing a tin-carbon / core-shell nano-particle fully filled carbon nano-tube composite anode material, which comprises the following steps: a porous anodic aluminafilm is placed in a stannic chloride water solution for soaking, is dried and then is subjected to chemical vapor deposition and reduction reaction in mixed gas of C2H2 and N2 at high temperature to film is placed in a stannic chloride water solution for soaking, is dried and then is subjected to chemical vapor deposition and reduction reaction in mixed gas of C2H2 and N2 at high temperature toobtain the tin-carbon / core-shell nano-particle fully filled carbon nano-tube composite anode material. The size and morphology of filled particles of the invention are controllable, the filling efficiobtain the tin-carbon / core-shell nano-particle fully filled carbon nano-tube composite anode material. The size and morphology of filled particles of the invention are controllable, the filling efficiency of the method is high, the structural purity of a target product can approach 100 percent, the interference of incomplete filling on the one-to-one correspondence of a structure and performance oency of the method is high, the structural purity of a target product can approach 100 percent, the interference of incomplete filling on the one-to-one correspondence of a structure and performance of the product is avoided, and the reversible lithium-storage capacity of the carbon nano-tube composite anode material with the novel structure can reach more than 700 mAh / g.f the product is avoided, and the reversible lithium-storage capacity of the carbon nano-tube composite anode material with the novel structure can reach more than 700 mAh / g.

Description

technical field [0001] The invention relates to a synthesis method for in-situ synthesis of tin-carbon / core-shell nanoparticles fully filled carbon nanotube composite anode materials by chemical vapor deposition, and belongs to the technical field of chemical vapor deposition preparation of new composite materials and application of lithium-ion battery anode materials. Background technique [0002] Due to the advantages of large specific energy, high working voltage, small self-discharge, long cycle life, no memory, no pollution and environmental protection, lithium-ion batteries have gradually replaced traditional nickel-metal hydride and lead-acid batteries and are widely used to meet the needs of today's electronic information Mobile power requirements for different mobile electronic devices in different eras. Graphitized carbon materials are now widely used commercially as anode materials, which have excellent performance in multiple charge and discharge cycles, but thei...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/04H01M4/36
CPCY02E60/12Y02E60/10
Inventor 王勇焦正吴明红陆燕许检红何雅琴
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com