High speed cigarette mouth building hot melt adhesive and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A cigarette overlap and hot melt adhesive technology, which is applied in the directions of adhesives, adhesive types, mineral oil hydrocarbon copolymer adhesives, etc. Quality, easy to store and transport, quick-drying effect
Inactive Publication Date: 2009-09-23
SHANGHAI JENTAI NANO SCI & TECH CO LTD
View PDF0 Cites 30 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0010] Aiming at the deficiencies of the prior art, the present invention overcomes the problems of poor adhesion of conventional cigarette adhes...
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] Component ratio (wt%) of high-speed cigarette lap glue:
[0033] EVA (MI=150, VA=28%) 30
[0034] Hydrogenated C5 petroleum resin 28.7
[0035] Polyethylene wax 40
[0036] Silica 1
[0037] Antioxidant 1010 0.3
[0038] To prepare a high-speed cigarette lap glue, the above data is used as the formula, the hot melt glue is prepared by melt blending, and the various components are fully mixed and evenly mixed by heating and stirring in a reactor. First, add antioxidant and tackifying resin at 160°C, melt evenly, add EVA resin, and stir evenly; finally add viscosity modifier and silicon dioxide, melt evenly, and discharge after maintaining pressure and pumping air.
Embodiment 2
[0040] Component ratio (wt%) of high-speed cigarette lap glue:
[0041] EVA (MI=150, VA=28%) 30
[0042] Hydrogenated carbon nine petroleum resin 29.7
[0043] Polyethylene wax 35
[0044] Silica 5
[0045] Antioxidant BHT 0.3
[0046]To prepare a high-speed cigarette lap glue, the above data is used as the formula, the hot melt glue is prepared by melt blending, and the various components are fully mixed and evenly mixed by heating and stirring in a reactor. First, add antioxidant and tackifying resin at 160°C, add EVA resin after melting evenly, and stir evenly; finally add viscosity modifier and silicon dioxide, melt evenly, and discharge after maintaining pressure and pumping air.
Embodiment 3
[0048] Component ratio (wt%) of high-speed cigarette lap glue:
[0049] EVA (MI=150, VA=20%) 30
[0050] Hydrogenated rosin 34.7
[0051] Polyethylene wax 30
[0052] Silica 5
[0053] Antioxidant 1010 0.3
[0054] To prepare a high-speed cigarette lap glue, the above data is used as the formula, the hot melt glue is prepared by melt blending, and the various components are fully mixed and evenly mixed by heating and stirring in a reactor. First, add antioxidant and tackifying resin at 150°C, melt evenly, add EVA resin, and stir evenly; finally add viscosity modifier and silica, melt evenly, and discharge after maintaining pressure and pumping air.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
Global softening point
aaaaa
aaaaa
Login to view more
Abstract
The invention belongs to the technical field of novel cigarette materials, in particular relates to a high speed cigarette mouth building hot melt adhesive and a preparation method thereof. The cigarette mouth building hot melt adhesive is prepared from ethylene-vinyl acetate copolymer, tackifying resin, nanometer silicon dioxide and antioxidant, and includes the following components according to percentage by weight: 25 to 35 percentages of ethylene-vinyl acetate copolymer, 35 to 45 percentages of tackifying resin, 20 to 40 percentages of viscosity modifier, 5 to 10 percentages of nanometer silicon dioxide and 0.1 to 0.5 percentage of antioxidant, wherein the components are heated and melted by a reaction kettle and are sequentially added and uniformly stirred. The cigarette adhesive prepared by the method has strong quick-drying performance, the ring and ball softening point nearly ranges from 95 to 105 DEG C, the softening range is from 5 to 8 DEG C, the operation of adhesion can be accomplished in 5 seconds, and the cigarette adhesive has the characteristics of no solvent, no absorption of moisture, corrosion resistance, aging resistance, and the like; the flowability and the wetting quality of the adhesive can be controlled by changing the parameters of wax, the method is suitable for the preparation of different cigarettes, and the adhesive and the method have good value of market popularization and application.
Description
technical field [0001] The invention belongs to the technical field of new cigarette materials, and in particular relates to a high-speed cigarette lapping hot melt adhesive and a preparation method thereof. Background technique [0002] Cigarette lap glue is used for the bonding of cigarette paper in cigarette production. The bonding effect is completed in the high-speed cigarette process. The adhesive should be soaked into the cigarette paper, and the paper and paper can be firmly bonded after curing. In actual production, due to differences in production environments and raw materials, the specific requirements for lapping glue are not the same. However, the lap glue must at least meet the following quality requirements: it should be colorless, non-toxic, odor-free, and non-irritating; it should have strong initial adhesion, fast bonding speed, appropriate viscosity, relatively Good fluidity and wettability; the bonded joint must be firm, with certain moisture-proof, moi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more