Polycarboxylic acid water reducing agent for gypsum and preparation method thereof

A technology of water reducer and polycarboxylic acid, which is applied in the field of polycarboxylate water reducer for gypsum and its preparation, can solve the problems of unfavorable rapid production of gypsum board and cumbersome operation, and achieve the goal of not delaying the solidification of gypsum, low energy consumption, high The effect of water reduction rate

Active Publication Date: 2009-11-04
SHANGHAI SUNRISE POLYMER MATERIAL CO LTD
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process requires the use of dispersants and auxiliary dispersants in the application process, which is cumbersome to operate, and such dispersants have a retarding effect on gypsum, which is not conducive to the rapid production of gypsum boards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polycarboxylic acid water reducing agent for gypsum and preparation method thereof
  • Polycarboxylic acid water reducing agent for gypsum and preparation method thereof
  • Polycarboxylic acid water reducing agent for gypsum and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Add 120g of GE-1 and 120g of deionized water into a 500ml four-necked flask equipped with a stirrer, a thermometer, and a dropping device, and stir to raise the temperature to 80°C. Add dropwise the monomer aqueous solution that is mixed with 17.6g methacrylic acid, 1.6g2-mercaptopropionic acid, 90g deionized water and 10g of potassium persulfate aqueous solution of 10wt% at the same time, drop time is controlled at about 90 minutes, and reaction temperature is controlled at 78 -85°C. After the dropwise addition, the temperature was kept for 45 minutes to complete the polymerization. Add 17.25 g of 28 wt % ammonia water to neutralize to about pH 6.5. The water reducer of the present invention was obtained, which was designated as PG-1.

Embodiment 2

[0033] Add 120g of GE-2 and 120g of deionized water into a 500ml four-necked flask equipped with a stirrer, a thermometer, and a dropping device, and stir to raise the temperature to 80°C. At the same time, 10 g of monomer aqueous solution mixed with 35.6 g of methacrylic acid, 7.6 g of sodium vinyl sulfonate, 1.2 g of mercaptoethanol, 70 g of deionized water and 10 wt % of ammonium persulfate aqueous solution were added dropwise, and the dropping time was controlled at about 90 minutes , the reaction temperature is controlled at 78-85°C. After the dropwise addition, the temperature was kept for 45 minutes to complete the polymerization. Add 13.75 g of 28 wt % ammonia water to neutralize to about pH 6.5. The water reducer of the present invention is obtained, which is denoted as PG-2.

Embodiment 3

[0035]Add 120g of GE-3 and 120g of deionized water into a 500ml four-neck flask equipped with a stirrer, a thermometer, and a dropping device, and stir to raise the temperature to 85°C. Simultaneously add dropwise the monomer aqueous solution mixed with 17.28g methacrylic acid, 0.8g mercaptoacetic acid, 70g deionized water, 7.8g butyl methacrylate and 10g aqueous potassium persulfate solution of 15wt%, and the dropping time is controlled at about 120 minutes , the reaction temperature is controlled at 83-88°C. After the dropwise addition was completed, the insulation was kept for 30 minutes to complete the polymerization. Add 15g of 28wt% ammonia water to neutralize to about pH 6.5. The water reducer of the present invention was obtained, which was designated as PG-3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polycarboxylic acid water reducing agent for gypsum and a preparation method thereof. The water reducing agent is prepared by copolymerizing unsaturated polyoxyalkylene base ether monomers, unsaturated monocarboxylic acid and derivative monomers thereof, and other monomers capable of being copolymerized with those monomers in a radical polymerization system. The gypsum water reducing agent has the advantages of high water-reducing rate, no delayed coagulation and the like, and the preparation method has the advantages of low energy consumption, high efficiency and good repeatability and stability.

Description

technical field [0001] The invention relates to a water reducer and a method for preparing the agent, in particular to a polycarboxylate water reducer for gypsum and a preparation method thereof. Background technique [0002] Gypsum raw materials are divided into natural gypsum and industrial by-product gypsum. With the development of industry and science and technology, according to the characteristics and application methods of gypsum. The use of gypsum can be roughly divided into two categories: the first gypsum is directly used without satin firing, mainly used to adjust cement condensation, nickel smelting, tofu solidification, optical instruments, gypsum casting molds, etc.; Mature gypsum, used in the production of building materials, ceramic models, dental materials, chalk, handicrafts, grinding glass, tofu solidification, etc. Among them, gypsum cementitious material is one of the three traditional cementitious materials. Its raw materials can be natural gypsum an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/26C08G65/48C04B103/30
CPCC04B24/2694C04B2103/302C04B28/14
Inventor 傅乐峰郑柏存冯中军张毅邓最亮
Owner SHANGHAI SUNRISE POLYMER MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com