Method for processing high-performance polyethylene twisting threads for waving netting or binding a steel rope
A high-performance, stitching technology, which is applied in melt spinning, textiles and papermaking, and adding pigments to spinning liquid, can solve the problems of difficult to meet the requirements of the aquaculture industry, poor safety and comprehensive performance, and achieve twist and turn. Good structural stability, improved safety, and good impact resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0008] Example 1: The process flow of high-performance polyethylene twisted yarn processing for blue woven net clothing or seam cable with a diameter of Ω2.03mm includes mixing process, drawing process, separation process, doubling yarn forming process, combined yarn forming process Process steps of stranding process and forming line:
[0009] The mixing process is operated in accordance with the following requirements: the mixer for cleaning and coloring, the corresponding color of Deshen 43003 blue pigment and turpentine additive is selected according to the color of the polyethylene monofilament, and the HDPE 5000S resin (melt index is 0.9) g / 10min), Deshen 43003 blue pigment and turpentine are sieved to remove impurities in the raw materials, to ensure normal wire drawing and reduce the rate of broken ends of the finished wire; use AWH-15 (AW) electronic balance to weigh and screen The treated pigment (addition is 0.03% of the weight of the resin) and turpentine (addition is ...
Embodiment 2
[0024] Example 2: Fruit green diameter Ω2.36mm woven net clothing or sewing cable with high-performance polyethylene twisting process process includes mixing process, drawing process, separation process, silk yarn forming process, and yarn forming process Process steps of stranding process and forming line:
[0025] The mixing process is operated in accordance with the following requirements: the mixer for cleaning and coloring, the corresponding color of Deshen 43003 fruit green pigment and turpentine additives are selected according to the color of the polyethylene monofilament as blue, and the HDPE 5000S resin (melt index is 0.9) g / 10min), Deshen 43003 blue pigment and turpentine are sieved to remove impurities in the raw materials, to ensure normal wire drawing and reduce the rate of broken ends of the finished wire; use AWH-15 (AW) electronic balance to weigh and screen The treated pigment (addition is 0.03% of the weight of the resin) and turpentine (addition is 0.3% of the...
Embodiment 3
[0031] Example 3: Blue diameter Ω2.64mm woven net clothing or stitched cable with high-performance polyethylene twisting process includes mixing process, drawing process, separation process, combined yarn forming process, combined yarn forming process Strand process and stranding process.
[0032] The mixing process is operated according to the following requirements: the mixing process is carried out according to the mixing process in Example 1, and the drawing material is obtained.
[0033] The wire drawing process is operated in accordance with the following requirements: the wire drawing is performed according to the wire drawing process in Example 1, which obtains a monofilament tow bobbin for wire separation.
[0034] The filament separation process is operated in accordance with the following requirements: the filament is separated according to the filament separation process in Example 1, and the bobbin obtained after the filament separation is used for processing single yarn...
PUM
Property | Measurement | Unit |
---|---|---|
melt flow index | aaaaa | aaaaa |
melt flow index | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com