Method for preparing cork floor

A technology of cork flooring and cork particles, applied in the field of decorative materials, can solve problems such as poor wear resistance of the sheet, affecting product appearance quality, and bubbling on the surface of the paint film

Active Publication Date: 2009-12-16
广西永明软木有限公司
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method suffers from the low density of the molded cork module, which is prone to air holes, and the cut pieces have poor wear resistance, which affects product quality.
The way of spraying paint is easy to produce uneven thickness of paint film and bubbling phenomenon on the surface of paint film, which also affects the appearance quality of products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of preparation method of cork floor of the present invention, carry out according to following method steps:

[0022] Put the oak bark into a pulverizer for crushing, and then perform cone milling, put the oak bark particles after cone milling into a vibrating sieve for screening, and then conduct steel milling to obtain granules with a particle size of 0.2-0.8mm and a particle density of 100 grams per cubic decimeter.

[0023] Choose oak bark with a length of 1m, a width of 0.6m, and a thickness of 5mm, put it into an iron cauldron and boil it in water at a temperature of about 80-100°C for 3-4 hours to fully soften it. The layer machine is cut into small pieces of patterned fabrics with a thickness of 0.5-1mm; then the small pieces of fabrics are mixed with 15-20 kg of glue according to 70 kg of material, and stirred at a pressure of 200-400 tons / m 2 The lower compact is put into the furnace and heated at 120°C for 4 hours, cooled after being released from the...

Embodiment 2

[0028] Put the oak bark into a pulverizer for crushing, and then perform cone milling, put the oak bark particles after cone milling into a vibrating sieve for screening, and then conduct steel milling to obtain granules with a particle size of 0.2-0.8mm and a particle density of 100 grams per cubic decimeter.

[0029] Choose oak bark with a length of 1.5m, a width of 0.8m, and a thickness of 8mm, put it into an iron cauldron and boil it in water at a temperature of 80-100°C for 3-4 hours, let it fully soften, take it out and dry it with water The splitting machine is cut into small pieces of patterned fabrics with a thickness of 0.5-1mm; then the small pieces of fabrics are mixed with 70 kg of material and 15 kg of glue, and stirred at a pressure of 200 tons / m 2 The compact is lowered, put into the furnace and heated at 120°C for 4 hours, cooled after being released from the furnace, and sliced ​​to obtain a patterned fabric with a thickness of 0.5-1mm.

[0030] Put the abov...

Embodiment 3

[0035] Put the oak bark into a pulverizer for crushing, and then perform cone milling, put the oak bark particles after cone milling into a vibrating sieve for screening, and then conduct steel milling to obtain granules with a particle size of 0.2-0.8mm and a particle density of 100 grams per cubic decimeter.

[0036] Choose oak bark with a length of 1.2m, a width of 0.7m, and a thickness of 7mm, put it into a large iron pot and boil it at a temperature of 80-100°C for 3-4 hours to fully soften it, take it out and dry it with water The splitting machine is cut into small pieces of patterned fabrics with a thickness of 0.5-1mm; then the small pieces of fabrics are mixed with 70 kg of material and 20 kg of glue, and stirred at a pressure of 400 tons / m 2 The compact is lowered, put into the furnace and heated at 120°C for 4 hours, cooled after being released from the furnace, and sliced ​​to obtain a patterned fabric with a thickness of 0.5-1mm.

[0037] Put the above-mentioned...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing cork floor, which comprises the following steps: a, crushing an oak bark into cork granules with the diameter of 0.2 to 0.8 millimeter; b, selecting another oak bark with certain length, boiling and airing the oak bark, splitting the oak bark into small pattern fabrics, mixing and stirring the pattern fabrics and polyurethane glue solution, pressing the mixture into a blank, heating and cooling the blank, and cutting the blank into sheet pattern fabrics; c, mixing and stirring the cork granules and the polyurethane glue solution, pressing the mixture into a blank, heating and cooling the blank, and cutting the blank into sheets to obtain a base material; and d, pressing and compounding the pattern fabrics and the base material gluing solution, and heating, cooling and strickling the mixture to obtain a finished product. The high-pressure density of the cork floor prepared by adopting the method reaches over 600 kilograms, and the surface abrasion resistance thereof reaches over 8,000 turns. The cork floor has the properties of comfort, durability, environmental protection, beauty, sound insulation, heat insulation, moisture resistance, skid resistance, flame retardation, and the like.

Description

technical field [0001] The invention relates to the technical field of decorative materials, in particular to a method for preparing a cork floor. Background technique [0002] The existing method of preparing cork flooring with oak bark as a raw material is generally to select raw materials, crush them, press mold the crushed raw material particles, slice the formed cork modules in a slicer, and paste the sliced ​​sheets on The high-density wood-based board is used as a veneer, and then sanded with emery cloth, and the paint is generally sprayed, and then the buckle groove is made, the inspection is packaged, and the finished product is finished. This method has the low density of the cork module formed by compression molding, which is easy to produce pores, and the cut pieces have poor wear resistance, which affects product quality. The method of spraying paint is easy to produce uneven thickness of paint film and bubbling phenomenon on the surface of paint film, which al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27M3/04B27L11/06B27K7/00B27N3/00B27N3/06B27N1/00B27N1/02
Inventor 陈道隆李志强何永明
Owner 广西永明软木有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com