Anti-rust coating composition

An anti-rust coating and composition technology, applied in the direction of coatings, anti-corrosion coatings, polyester coatings, etc., can solve the problems of poor corrosion resistance of anti-rust coatings, unable to meet the requirements of medium and long-term anti-rust, and achieve safe use. Effect

Active Publication Date: 2011-08-10
CHINA NAT OFFSHORE OIL CORP +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing antirust coatings for oil casings have poor corrosion resistance and can only meet the short-term anticorrosion requirements under dry conditions, but cannot meet the medium and long-term antirust requirements under high temperature, humidity and marine climate conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] serial number

[0018] The above anti-rust coating composition for petroleum casing, according to GB / T1771 paint and varnish neutral salt spray resistance test, under the condition of film thickness 25±2um, the test result: 1224h, the coating has no change.

Embodiment 2

[0020] serial number

[0021] 2

[0022] The above anti-rust coating composition for petroleum casing is tested according to GB / T1771 paint and varnish neutral salt spray resistance performance. Under the condition of film thickness of 25±2um, the test result: 1152h, the coating has no change.

Embodiment 3

[0025] The above anti-rust coating composition for petroleum casing is tested according to GB / T1771 paint and varnish neutral salt spray resistance performance. Under the condition of film thickness of 25±2um, the test result: 1080h, the coating has no change.

[0026] The anti-rust coating composition of the present invention can be applied to the outer surface of the oil casing by spraying, and the neutral salt spray resistance time exceeds 1000h without any change in the coating, which can meet the long-term anti-rust requirements of the oil casing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an anti-rust coating composition which is characterized by comprising the following components in percentage by weight: 60-70 percent of film-forming resin, 0.5-1 percent of shrinkage-proof agent, 0.2-2 percent of photo-thermal stabilizing agent and 30-40 percent of solvent, wherein the film-forming resin consists of thermoplastic acrylic resin and alkyd resin; the thermoplastic acrylic resin is selected from one of a copolymer of methyl methacrylate and butyl acrylate, a copolymer of the methyl methacrylate and butyl methacrylate and a copolymer of acrylic ester and styrene; the alkyd resin is selected from one of linseed oil alkyd resin, dewatered castor oil alkyd resin and acrylic modified alkyd resin; the shrinkage-proof agent is organic fluorine modified polyacrylic ester; the photo-thermal stabilizing agent is one of 2-hydroxy-4-n-octyloxy benzophenone which is an ultraviolet ray absorbent and bi-(2,2,6,6-tetramethyl piperidyl) sebacic acid ester which is a hindered amines light stabilizing agent; and the solvent is an environment friendly mixed dimethyl ester solvent.

Description

technical field [0001] The technical field of the invention relates to metal surface anti-corrosion technology, especially the long-term anti-rust technology on the outer surface of petroleum casing, and specifically an anti-rust coating composition. Background technique [0002] Oil casing is an important material for drilling and oil production. In recent years, with the continuous growth of the world's demand for oil energy, the demand and output of oil casing for oil production have also increased year by year. At present, the method commonly used by oil casing manufacturers at home and abroad is to spray anti-rust coating on the outside of the oil casing to avoid corrosion of the oil casing. [0003] The existing antirust coatings for oil casings have poor corrosion resistance and can only meet the short-term anticorrosion requirements under dry conditions, but cannot meet the medium and long-term antirust requirements under high temperature, humidity and marine climate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/04C09D167/08C09D133/06C09D5/08
Inventor 叶学海刘红光张晓波于晓微付春明张春丽霍文敏
Owner CHINA NAT OFFSHORE OIL CORP