Aqueous PU velvet resin used for synthetic leather

A velvet resin and synthetic leather technology, which is applied in fiber treatment, textiles and papermaking, etc. It can solve the problem of poor synthetic leather viscosity, stability, hand touch, etc., the bottom layer of synthetic leather dissolves, and the synthetic leather feels bad. problem, to achieve the effect of excellent comprehensive effect, firm bonding and plump hand feeling

Inactive Publication Date: 2010-01-27
JIANGSU BAOZE POLYMER MATERIAL
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 1. The organic solvent contained in the solvent-based cashmere resin will cause the bottom layer of synthetic leather or artificial leather to dissolve, and the treated synthetic leather will not feel good;
[0005] 2. The organic solvent contained in the solvent-based velvet resin not o

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example 1

[0028] 1. Water-based PU velvet resin for synthetic leather is composed of the following raw materials: 100 kg of water-based polyurethane resin (30% solid content), 100 kg of ordinary tap water, 3 kg of low-temperature yangbuck powder, 2 kg of silica velvet powder, and silicone oily 3 kg of refreshing agent, 1 kg of matting powder, 3 kg of water-based polyurethane thickener, 5 kg of silicone defoamer, and 3 kg of silicone leveling agent.

[0029] 2. The preparation method of the water-based PU velvet resin for synthetic leather of the present invention is as follows:

[0030] ① Select 100 kg of water-based polyurethane resin, 2 kg of silica velvet powder, 3 kg of silicone oil slip agent, 1 kg of matting powder, 3 kg of silicone leveling agent, 5 kg of silicone defoamer and 100 kg of water Stir for 3 hours, mix well and set aside;

[0031] ② Grind and filter the mixture obtained in step ①;

[0032] ③ Take the mixture obtained in step ②, add 3 kg of low-temperature y...

Example Embodiment

[0037] Example 2

[0038] 1. Water-based PU velvet-feel resin for synthetic leather is composed of the following raw materials: aliphatic polyurethane emulsion (30% solid content) 100 kg, ordinary tap water 100 kg, low temperature yangbuck powder 8 kg, silica velvet powder 8 kg, silicone oil Slip agent 6 kg, matting powder 8 kg, silicone leveling agent 3 kg, silicone defoaming agent 8 kg, non-ionic polyurethane polymer 4 kg.

[0039] 2. The preparation method of the water-based PU velvet resin for synthetic leather of the present invention is as follows:

[0040] ①Select 100 kg of aliphatic polyurethane emulsion (30% solid content) in proportion, 100 kg of ordinary tap water, 8 kg of silica velvet powder, 6 kg of silicone oil slip agent, 8 kg of matting powder, and 3 kg of silicone leveling agent , 8 kg of organosilicon defoamer, stir for 3 hours, mix well, and set aside;

[0041] ② Grind and filter the mixture obtained in step ①;

[0042] ③Take the mixture obtained in step ②, add 8 k...

Example Embodiment

[0047] Example 3

[0048] 1. Water-based PU velvet resin for synthetic leather is composed of the following raw materials: aliphatic polyurethane dispersion (30% solid content) 80 kg, ordinary tap water 80 kg, low temperature venom powder 4 kg, silica velvet powder 4 kg, organic Silicone oil slip agent 2 kg, matting powder 4 kg, silicone leveling agent 1 kg, silicone defoamer 4 kg, non-ionic polyurethane polymer 2 kg.

[0049] 2. The preparation method of the water-based PU velvet resin for synthetic leather of the present invention is as follows:

[0050] ① Select aliphatic polyurethane dispersion (30% solid content) 80 kg, ordinary tap water 80 kg, silica velvet powder 4 kg, silicone oil slip agent 2 kg, matting powder 4 kg, silicone leveling agent 1 Kg, 4 kg of organosilicon defoamer, stir for 3 hours, mix well and set aside;

[0051] ② Grind and filter the mixture obtained in step ①;

[0052] ③Take the mixture obtained in step ②, add 4 kg of low-temperature mutton flour, and mix w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aqueous PU velvet resin used for synthetic leather, which comprises the following raw materials by weight percent: 40-50% of aqueous polyurethane resin, 40-50% of water, 2-5% of low-temperature sheep bar powder, 2-4% of silicon dioxide velvet powder, 1-3% of organic silicone oil smoothing agent, 1-4% of extinction powder, 0.5-1% of organic silicon flatting agent, 2-5% of organic silicon antifoaming agent and 0.5-2% of aqueous polyurethane thickening agent. The aqueous PU velvet resin used for synthetic leather of the invention takes water as solvent to replace toxic solvent, such as dimethyl fomamide, butanone and the like and has the advantages of being non-combustible, safe and environment-friendly, saving cost and the like. The aqueous PU velvet resin also has the advantages of good film-forming resistance, firm bonding, coating solvent resistance, cold resistance, hydrolysis resistance and heat-proof aging. Products fabricated by using the resin have the characteristics of plump feel, unique velvet effect, strong real leather quality, fine and smooth texture, good air permeability and the like.

Description

Technical field [0001] The invention relates to a velvet-feel resin for synthetic leather, in particular to a synthetic leather water-based PU velvet-feel resin applied to a synthetic leather front process. Background technique [0002] With the continuous improvement of people’s living standards, high-end, safe and environmentally friendly daily-use products have become people’s goals. For example, leather bags, leather shoes and leather clothing are commonly used products. As the world’s awareness of animal protection increases, Animal leather is far from meeting people's needs. Synthetic leather products have gradually become a popular trend in the future. Synthetic leather has been widely used in the production of luggage, clothing, shoes and other products. Among them, the base fabric of PU leather is a canvas PU material with good tensile strength. In addition to being coated on the top of the base fabric, the base fabric can also be included in the middle, so that the exis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/643D06M15/564D06M11/79D06M13/50C08L75/04
Inventor 时云刚
Owner JIANGSU BAOZE POLYMER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap