Hydrophober and method for preparing hydrophobic glass by same

A technology of hydrophobic glass and water-repellent agent, which is applied in the field of water-repellent agent and preparation of water-repellent glass, which can solve the problems of short retention time of hydrophobic film and poor water-repellent effect, and achieve excellent water repellency, good moldability, The effect of prolonging the life of art

Active Publication Date: 2010-03-10
ZHENGZHOU HIHO OPTICAL TECH CO LTD
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There have been reports of similar water-repellent agents before, and most of their formulas use hydrophobic substances such as silicone oil (such as methyl silicone oil), or use general hydrophobic surfactants, but their disadvantage is that the retention time of the hydrophobic film is too short , poor water-repellent effect, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Mass percentage composition of water repellent:

[0030] Tridecafluorooctyltrimethoxysilane 1.5%

[0031] Orthoethyl silicate 0.6%

[0032] Lauryltrimethylammonium Chloride 0.1%

[0033] Isopropanol 97.5%

[0034] Acetic acid 0.3%.

[0035] Preparation method of hydrophobic glass:

[0036] (1) To prepare a water-repellent agent, take each component in proportion, mix, first stir for 30 minutes, and then ultrasonically stir for 20 minutes;

[0037] (2) the glass to be treated is cleaned with an ultrasonic cleaning agent, and then dried;

[0038] (3) Spray the water-repellent agent prepared in step (1) on the glass surface treated in step (2) by using a spraying system, and 3 g of water-repellent agent is required for every 1 square meter of glass;

[0039] (4) Dry the glass after spraying the water-repellent agent, the temperature during drying is 80° C., and the drying time is 5 minutes, so that the water-repellent film layer is dried and solidified to obtain the ...

Embodiment 2

[0041] Mass percentage composition of water repellent:

[0042] Tridecafluorooctyltrimethoxysilane 1.1%

[0043] Orthoethyl silicate 0.6%

[0044] Lauryltrimethylammonium Chloride 0.1%

[0045] Isopropanol 98%

[0046] Acetic acid 0.2%.

[0047] Preparation method of hydrophobic glass:

[0048] (1) To prepare water repellent, take each component in proportion, mix, first stir for 50 minutes, then ultrasonically stir for 10 minutes;

[0049] (2) the glass to be treated is cleaned with an ultrasonic cleaning agent, and then dried;

[0050] (3) Spray the water-repellent agent prepared in step (1) evenly on the glass surface treated in step (2) by using a spraying system, and 4g of water-repellent agent is required for every 1 square meter of glass;

[0051] (4) Dry the glass after spraying the water-repellent agent, the temperature during drying is 130° C., and the drying time is 3 minutes, so that the water-repellent film layer is dried and solidified to obtain the finishe...

Embodiment 3

[0053] Mass percentage composition of water repellent:

[0054] Tridecafluorooctyltrimethoxysilane 4%

[0055] Orthoethyl silicate 0.5%

[0056] Lauryltrimethylammonium Chloride 0.2%

[0057] Isopropanol 95%

[0058] Acetic acid 0.3%.

[0059] Preparation method of hydrophobic glass:

[0060] (1) To prepare water repellent, take each component in proportion, mix, first stir for 60 minutes, then ultrasonically stir for 5 minutes;

[0061] (2) the glass to be treated is cleaned with an ultrasonic cleaning agent, and then dried;

[0062] (3) Spray the water-repellent agent prepared in step (1) evenly on the glass surface treated in step (2) by using a spraying system, and 6g of water-repellent agent is required for every 1 square meter of glass;

[0063] (4) Dry the glass after spraying the water-repellent agent, the temperature during drying is 180° C., and the drying time is 1 minute, so that the water-repellent film layer is dried and solidified to obtain the finished pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a hydrophober comprising tridecafluoro octyl trimethoxy silane, ethyl orthosilicate, dodecyltrimethylammonium chloride, isopropanol and ethylic acid. The method for preparing hydrophobic glass comprises the following steps: (1) preparing the hydrophober, taking all the components in a certain proportion, mixing and stiring uniformly; (2) cleaning and drying glass to be processed; (3) spraying the hydrophober prepared in the step (1) on the surface of the glass processed in the step (2); and (4) drying the glass on which the hydrophober is sprayed in the step (3) so thata hydrophobic film layer is dried and solidified to obtain a finished product. The hydrophober has easily obtained components, simple preparation process and good film forming performance and enablesthe service life of a hydrophobic film to be greatly prolonged; in addition, the acid and alkali resistance and the weather resistance of the prepared hydrophobic glass are greatly improved.

Description

technical field [0001] The invention belongs to the technical field of functional glass, and relates to a water-repellent agent and a method for preparing water-repellent glass by using the water-repellent agent. Background technique [0002] Due to the high surface energy of the glass surface, the resulting surface tension is much higher than that of water, so water has wettability to glass. At present, most of the art glass in the construction and home decoration market is directly or reprocessed from float glass, and none of them have water-repellent effect. Therefore, when the surface of the glass is stained with water, a layer of water film will be formed, causing the water droplets to not easily slip off. frequency. Therefore, how to improve the stain resistance of the glass surface, reduce the difficulty and cost of cleaning and maintenance; improve the acid and alkali resistance and weather resistance of the glass, and finally improve and improve the functional val...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C17/30
Inventor 李金钟
Owner ZHENGZHOU HIHO OPTICAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com