Method for glazing and sandblasting surface of sander

A technology for glaze and sandware, applied in the field of the formation of surface glaze on sandware, can solve the problem that sandware has no surface glaze coloring method, etc., and achieve the effects of enriching art types, extending market space, and enhancing artistic value

Active Publication Date: 2010-04-28
张宏亮
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problem that the existing sandware has no feasible surface glaze coloring method, the present invention provides a glaze blasting method for the surface of the sandware

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The method of glaze color sandblasting on the surface of sandware, its specific steps are as follows:

[0013] (1) prepare glaze slurry, glaze slurry is made with the raw material of following percentage by weight: feldspar 32%, calcium carbonate 8%, barium carbonate 4%, quartz 15%, cooked talc 4%, calcite 7%, elutriation pure loess 24%, high-temperature ceramic pigment 6%; then add carboxymethyl cellulose of 0.1% (ie external ratio) of the sum of the weight of all the above-mentioned raw materials; put all the glaze slurry raw materials into crushing or grinding equipment and add water, and crush to 100- 200 mesh (100 mesh or 120 mesh or 150 mesh or 180 mesh or 200 mesh), then high-frequency iron removal equipment for high-frequency iron removal, add water and control the amount of water added to make the specific gravity reach 1.5-1.6 g / ml, Finally stale (i.e. placed) for 3 days to make glaze slurry;

[0014] (2) Select the green body with water dried to 10% ~ 15% (1...

Embodiment 2

[0019] The method of glaze color sandblasting on the surface of sandware, its specific steps are as follows:

[0020] (1) prepare glaze slurry, glaze slurry is made with the raw material of following percentage by weight: feldspar 26%, calcium carbonate 6%, barium carbonate 6%, quartz 17%, cooked talc 6%, calcite 6%, elutriation pure loess 28%, high-temperature ceramic pigment 5%; then add carboxymethyl cellulose of 0.1% (ie external ratio) of the sum of the weight of all the above-mentioned raw materials; put all the raw materials of glaze slurry into crushing or grinding equipment and add water, and pulverize to 100- 200 mesh (100 mesh or 120 mesh or 150 mesh or 180 mesh or 200 mesh), then high-frequency iron removal equipment for high-frequency iron removal, add water and control the amount of water added to make the specific gravity reach 1.5-1.6 g / ml, Finally stale (i.e. placed) for 3 days to make glaze slurry;

[0021] (2) Select the green body with water dried to 10% ~...

Embodiment 3

[0025] The method of glaze color sandblasting on the surface of sandware, its specific steps are as follows:

[0026] (1) prepare glaze slurry, glaze slurry is made with the raw material of following percentage by weight: feldspar 34%, calcium carbonate 10%, barium carbonate 5%, quartz 11%, cooked talc 5%, calcite 4%, elutriation pure loess 20%, high-temperature ceramic pigment 11%; then add carboxymethyl cellulose of 0.1% (ie external ratio) of the sum of the weight of all the above-mentioned raw materials; put all the glaze slurry raw materials into crushing or grinding equipment and add water, and crush to 100- 200 mesh (100 mesh or 120 mesh or 150 mesh or 180 mesh or 200 mesh), then high-frequency iron removal equipment for high-frequency iron removal, add water and control the amount of water added to make the specific gravity reach 1.5-1.6 g / ml, Finally stale (i.e. placed) for 3 days to make glaze slurry;

[0027] (2) Select the green body with water dried to 10% ~ 15% ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for forming glazes on the surface of a sander, in particular to a method for glazing and sandblasting the surface of a sander, which solves the problem that the conventional sander has no feasible surface glazing and coloring method. The method comprises the following steps: (1) preparing glaze slurry, which is prepared from the following raw materials in percentage by weight: 26 to 34 percent of feldspar, 6 to 10 percent of calcium carbonate, 4 to 6 percent of barium carbonate, 11 to 17 percent of quartz, 4 to 6 percent of processed talc, 4 to 8 percent of calcite, 20 to 28 percent of elutriated pure loess and 5 to 11 percent of high-temperature ceramic pigment; then adding carboxymethyl cellulose accounting for 0.1 percent of the weight sum of the raw materials into the raw materials; crushing all the glaze slurry raw materials, deironing, then adding water into the raw materials, and controlling the specific gravity value to reach 1.5 to 1.6 grams per milliliter by controlling the added water quantity; (2) spraying the glaze slurry to the surface of a blank evenly by adopting a spraying device to form granular glazes; and (3) firing the blank. The method fills the blank that the sander has no surface glazing and sandblasting method, so the sander originally only having practical value has more artistic appreciation and collection values.

Description

technical field [0001] The invention relates to a method for forming glaze on the surface of a sand ware, in particular to a method for blasting the glaze on the surface of a sand ware. Background technique [0002] Sandware has a long history. According to archaeological discoveries, it has been produced as early as the Qin Dynasty, and it was recorded in the Tang Dynasty. Included in the provincial intangible cultural heritage protection project. Sand ware is loved by the people because of its effect of "stewing meat without changing taste, boiling medicine without change, and cooking without changing color". The color is relatively single, and the artistic value is low, so that the sandware market space is limited. Contents of the invention [0003] In order to solve the problem that there is no feasible surface glaze coloring method for the existing sandware, the present invention provides a glaze blasting method for the surface of the sandware. [0004] The present...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 张宏亮赵洪
Owner 张宏亮
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap