Magnesium base spherical quasicrystal master alloy and preparation method thereof

An intermediate alloy and spherical technology, applied in the field of magnesium-based alloys, can solve problems such as complex control, difficulty in industrial production, and waste of energy consumption, and achieve the effects of simple preparation process, simplified production steps, and improved mechanical properties

Inactive Publication Date: 2010-05-12
HEBEI UNIV OF TECH
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is: provide a magnesium-based spherical quasicrystal master alloy and a preparation method thereof, the magnesium-based spherical quasicrystal master alloy is a Mg-Zn-Y-Mn-Cu spherical quasicrystal master alloy, and its preparation method is The method of preparing magnesium-based spherical quasicrystalline master alloy by controlling the solidification rate. The present invention not only overcomes the defects of the prior art, such as waste of energy consumption, high requirements for production equipment, complex control and difficulty in realizing industrialized production, but also produces Mg -Zn-Y-Mn-Cu spherical quasicrystalline master alloy greatly improves the high temperature mechanical properties of the reinforced magnesium alloy composite.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnesium base spherical quasicrystal master alloy and preparation method thereof
  • Magnesium base spherical quasicrystal master alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The first step is to smelt the raw material melt of magnesium-based spherical quasicrystal master alloy

[0027] Set the heating temperature of the crucible resistance furnace to be 790°C. When the crucible temperature rose to 380°C, add magnesium ingots accounting for 60.5% of the total raw material mass percent and zinc ingots accounting for 35.5% of the total raw material mass percent to the crucible. And start to pass CO with a volume ratio of 100:1 2 / SF 6 The mixed gas is used as a protective gas, and the temperature continues to rise. After the magnesium ingot and the zinc ingot in the crucible are completely melted, add 3.7% yttrium ingot accounting for the mass percentage of the total amount of raw materials, and stir for 1 minute after the yttrium ingot is completely melted. Adding 0.2% electrolytic manganese and 0.1% particle size to 200 mesh copper powder in the Mg-Zn-Y alloy melt of the total amount of raw materials, the raw material of the magnesium-based...

Embodiment 2

[0033] The first step is to smelt the raw material melt of magnesium-based spherical quasicrystal master alloy

[0034] Set the heating temperature of the crucible resistance furnace to be 780°C, and when the crucible temperature rises to 350°C, add magnesium ingots accounting for 65.0% of the total mass percentage of raw materials and zinc ingots accounting for 30.0% of the total mass percentage of raw materials to the crucible, And start to pass CO with a volume ratio of 100:1 2 / SF 6 The mixed gas is used as a protective gas, and the temperature continues to rise. After the magnesium ingot and zinc ingot in the crucible are completely melted, add yttrium ingot accounting for 4.5% of the total mass percentage of raw materials, and stir for 1 minute after the yttrium ingot is completely melted. Adding 0.3% electrolytic manganese and 0.2% particle size to 200 mesh copper powder in the Mg-Zn-Y alloy melt, the raw material of the magnesium-based spherical quasicrystal master al...

Embodiment 3

[0038] The first step is to smelt the raw material melt of magnesium-based spherical quasicrystal master alloy

[0039] Set the heating temperature of the crucible resistance furnace to be 800°C. When the crucible temperature rose to 400°C, add magnesium ingots accounting for 55.0% of the total mass percentage of raw materials and zinc ingots accounting for 40.0% of the total mass percentage of raw materials to the crucible. And start to pass CO with a volume ratio of 100:1 2 / SF 6 The mixed gas is used as a protective gas, and the temperature continues to rise. After the magnesium ingot and the zinc ingot in the crucible are completely melted, add yttrium ingot accounting for 4.6% of the total mass percentage of raw materials, and stir for 2 minutes after the yttrium ingot is completely melted. Adding 0.1% electrolytic manganese and 0.3% particle size to 200 mesh copper powder in the Mg-Zn-Y alloy melt of the total amount of raw materials, the raw material of the magnesium-b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a magnesium base spherical quasicrystal master alloy and a preparation method thereof, relating to magnesium base alloys with zinc as a submaster component. The alloy is Mg-Zn-Y-Mn-Cu quinary magnesium base icosahedral spherical quasicrystal master alloy, comprising the following chemical components: 55.0-65.0% of Mg, 30.0-40.0% of Zn, 2.5-5.5% of Y, 0.10-1.50% of Mn and 0.10-0.50% of Cu, wherein the diameter of the spherical quasicrystal is 2-7mu m and the mean diameter is 6mu m. The volume of the spherical quasicrystal is 35-45% of the total volume of the alloy. The preparation method is characterized by adopting control of the solidification rate, namely pouring the alloy melt into a casting mold capable of controlling the cooling rate, wherein the solidification rate is controlled between 72.2K / s and 88.6K / s. The product of the invention can better improve the mechanical property of the alloy materials while enhancing the magnesium alloy substrate, has simple process, low requirement on equipment and wide raw material sources, is convenient to realize industrialized production and saves resources.

Description

technical field [0001] The technical solution of the invention relates to a magnesium-based alloy with zinc as the secondary main component, specifically a magnesium-based spherical quasicrystal master alloy and a preparation method thereof. Background technique [0002] Compared with the commonly used metal or alloy materials at present, magnesium has the advantages of light weight, high damping performance, strong electromagnetic shielding ability and good heat dissipation, so that magnesium alloy materials have great application potential in national economy and national defense construction; in addition , Magnesium is easy to recycle and reuse, and is a green and environmentally friendly metal that does not pollute the environment. Therefore, research on magnesium alloys has become a hot spot in the field of material research. Although the specific strength (approximately 14-16) and specific fatigue strength of existing magnesium alloys are higher than those of cast alum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C23/04C22C1/02B22D21/04
Inventor 赵维民蔚成全李海鹏王志峰丁俭李永艳黄春瑛史中方
Owner HEBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap