Production technique of expansion-type transparent fire-retardant coating

A fire-retardant coating and production process technology, applied in the field of coatings, can solve the problems of fire resistance, poor curing and wear resistance, etc.

Inactive Publication Date: 2010-06-23
张力
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, many units have carried out research work, but the obtained products still have the disadvantages of poor fire resistance, curing property and wear resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Raw material name Concentration Parts by weight

[0029] Component A Phosphoric acid 85% 168

[0030] Tigressitol 97

[0031] Formaldehyde 7% 237

[0032] Urea 46% 66

[0033] Triethanolamine 29

[0034] Sodium Hydroxide 10% 1

[0035] Component B Melamine 45

[0036] Formaldehyde 240

[0037] Borax 1

[0038] Component A is mixed with component B in a 1:1 weight ratio.

Embodiment 2

[0040] Raw material name Concentration Weight

[0041] Component A Phosphoric acid 85% 135

[0042] Tigressitol 84

[0043] Formaldehyde 37% 230

[0044] Urea 46% 55

[0045] Triethanolamine 21

[0046] Sodium hydroxide 10% 0.5

[0047] Component B Melamine 35

[0048] Formaldehyde 210

[0049] Borax 1.5

[0050] Component A and component B were mixed in a weight ratio of 1:2.

Embodiment 3

[0052] Raw material name Concentration Weight

[0053] A component Phosphoric acid 85% 150

[0054] Tigressitol 90

[0055] Formaldehyde 37% 234

[0056] Urea 46% 60

[0057] Triethanolamine 25

[0058] Sodium hydroxide 10% 0.8

[0059] Component B Melamine 40

[0060] Formaldehyde 230

[0061] Borax 1.2

[0062] Component A and component B were mixed in a weight ratio of 1:1.5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a production technology of an expansion-type transparent fire-retardant coating, which comprises the following steps: mixing ammonium dihydrogen phosphate, formaldehyde, pentaerythritol, urea, triethanolamine and sodium hydroxide according to a certain proportion to prepare a component A; mixing tripolycyanamide, formaldehyde and borax according to a certain proportion to prepare a component B; and mixing the component A and the component B with the weight portion of 1:1-2 to obtain the expansion-type transparent fire-retardant coating. The invention has the advantages of low product cost and favorable fire resistance.

Description

technical field [0001] The invention belongs to the field of paint, and in particular relates to a production process of an intumescent transparent fireproof paint. technical background [0002] Fireproof coating is a special coating used on the surface of flammable substrates, which can reduce the flammability of the surface of the coated material, retard the rapid spread of fire, and improve the fire resistance limit of the coated material. The fire retardant coating is coated on the surface of the substrate. In addition to its flame retardant effect, it also has anti-rust, waterproof, anti-corrosion, wear-resistant, heat-resistant, coating toughness, colorability, adhesion, easy-drying and a certain gloss, etc. performance. [0003] Combustion is a rapid and violent oxidation reaction with flames. The reaction is very complicated. Three conditions must be met at the same time for the generation and progress of combustion, namely, combustible substances, combustion aids (...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/30C09D5/18
Inventor 张力
Owner 张力
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com