Nylon 66 compound capable of use for weaving glass-fiber-free shuttle
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A glass fiber shuttle and composition technology, applied in the field of polyamide composition, can solve the problems of poor flow performance, non-antistatic, affecting the quality of textiles, etc., and achieve the effects of high flowability, no glass fiber exposure, and smooth appearance
Inactive Publication Date: 2010-06-30
PINGDINGSHAN HUABANG ENG PLASTIC
View PDF0 Cites 11 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, the textile shuttles are all reinforced and modified with glass fiber, which has poor fluidity. The surface of the injection molded product has glass fiber exposed, which is not antistatic, which seriously affects the quality of the textile.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0036] Take 59g of raw PA66 slices, 18g of PA6 slices, 1g of ultra-high molecular weight polyethylene, 20g of polyethylene grafts, the antioxidant is 1098 and 168 compound, 1098 is 0.1g, 168 is 0.1g, calcium stearate 1.8g, Put all the raw materials into the high mixer and mix for 2 minutes, then feed the mixed raw materials into the twin-screw extruder, the screw machine speed is 260 rpm, the processing temperature is 250 ° C, and extruded to granulate.
Embodiment 2
[0038] Take 55g of raw PA66 slices, 18.8g of PA6 slices, 2g of ultra-high molecular weight polyethylene, 23g of polyethylene grafts, the antioxidant is 1010 and 168 compound, 1010 is 0.1g, 168 is 0.1g, barium stearate 1g, Put all the raw materials into the high mixer and mix for 3 minutes, then feed the mixed raw materials into the twin-screw extruder, the screw machine speed is 200 rpm, the processing temperature is 260°C, and extruded to granulate.
Embodiment 3
[0040] Take 52g of raw PA66 slices, 20g of PA6 slices, 1g of ultra-high molecular weight polyethylene, 25g of polyethylene grafts, the antioxidant is a compound of 1098 and 168, 0.25g of 1098, 0.25g of 168, 1.5g of calcium stearate, Put all the raw materials into the high mixer and mix for 1.5 minutes, then feed the mixed raw materials into the twin-screw extruder, the screw machine speed is 320 rpm, the processing temperature is 250°C, and extruded to granulate.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thermal decomposition temperature
aaaaa
aaaaa
density
aaaaa
aaaaa
melting point
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to the field of polyamide compound, in particular to a nylon 66 compound capable of use for weaving glass-fiber-free shuttles. The nylon 66 compound is prepared with raw materials according to the following mass ratios: 40-67% of nylon 66 slices, 15-30% of nylon 66 slices, 1-5% of ultra-high molecular weight polyethylene, 15-30% of compatilizer, 0.1-0.5% of antioxygen and 1-10% of lubricant. The preparation method of the nylon 66 compound comprises the following steps: 1. weighting the raw materials; 2. putting all the raw materials in a high mixing machine for mixing; and 3. putting the raw material mixture into a double-screw extruder for extrusion and pelleting. In the invention, nylon 66 resin is used as the base material, the ultra-high molecular weight polyethylene is used, and no glass fiber is used. The invention has the advantages of high fluidity, strong impact resistibility, high strength, wearability, stable dimension, smooth and clean appearance, no glass fiber exposure and antistatic performance.
Description
technical field [0001] The invention relates to the field of polyamide compositions, in particular to a nylon 66 composition that can be used for textile non-glass fiber shuttles, and the nylon 66 composition can be used for injection molding textile shuttles. Background technique [0002] Polyamide is commonly known as nylon (Nylon), and its English name is Polyamide (referred to as PA). It is a general term for thermoplastic resins containing repeated amide groups - [NHCO] - in the main molecular chain. Including aliphatic PA, aliphatic-aromatic PA and aromatic PA. Among them, aliphatic PA has many varieties, large output, and wide application. Its name depends on the specific number of carbon atoms in the synthetic monomer. [0003] Nylon is the most important engineering plastic, and its output ranks first among the five general-purpose engineering plastics. Nylon is a polyamide fiber (nylon). It can be made into long or short fibers. [0004] Nylon was developed by an...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more