Environment-friendly low-toxicity white-light gluing crystal board and manufacture method thereof

A crystal board, an environment-friendly technology, applied in the field of environmentally friendly low-toxicity white light laminated crystal boards, can solve the problem that it is difficult to achieve the appearance standard of white, transparent, bright and low-toxicity white light laminated thick sheets, and the color of transparent light-colored products is difficult to control , poor transparency and brightness, etc., to achieve the effect of excellent elasticity, good surface smoothness and high transparency

Active Publication Date: 2012-05-02
TIANJIN HONGMAO PLASTICS
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This processing technology has a long production process, is not easy to control, requires a large amount of stabilizer, and takes a long time to heat the material.
The low-toxic PVC laminated thick film produced by this processing technology has poor transparency and brightness, and it is more difficult to control the color of transparent light-colored products. It is difficult to achieve white, transparent and bright low-toxic white laminated sheets that comply with REACH regulations. Thick slice appearance standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly low-toxicity white-light gluing crystal board and manufacture method thereof
  • Environment-friendly low-toxicity white-light gluing crystal board and manufacture method thereof
  • Environment-friendly low-toxicity white-light gluing crystal board and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0078]

[0079] Set the electronic scale according to the above formula and start measuring. After completion, polyvinyl chloride, diisononyl phthalate DINP, liquid barium zinc stabilizer and non-toxic phosphate are discharged into the high mixer in sequence;

[0080] 2) Perform high-speed mixing. After mixing for 120 seconds, add processing aids and pigments in sequence, and the total mixing time is 400 seconds;

[0081] 3) Perform cooling and stirring, discharge the high-speed mixed materials into the mixer for cooling and stirring, and lower the temperature by feeding circulating cooling water into the mixer until the temperature drops below 80°C, and discharge them into the storage tank.

[0082] 4) The material in the storage barrel is conveyed to the planetary extruder through the screw conveyor for plasticization, and the extrusion temperature of the planetary extruder is set at 176°C;

[0083] 5) Filter the plasticized material of the planetary extruder through a fi...

example 2

[0098]

[0099] Set the electronic scale according to the above formula and start measuring. After completion, polyvinyl chloride, diisononyl phthalate DINP, liquid barium zinc stabilizer and non-toxic phosphate are discharged into the high mixer in sequence;

[0100] 2) Perform high-speed mixing. After mixing for 120 seconds, add processing aids and pigments in sequence, and the total mixing time is 420 seconds;

[0101] 3) Perform cooling and stirring, discharge the high-speed mixed materials into the mixer for cooling and stirring, and lower the temperature by feeding circulating cooling water into the mixer until the temperature drops below 80°C, and discharge them into the storage tank.

[0102] 4) The material in the storage barrel is conveyed to the planetary extruder through the screw conveyor for plasticization, and the extrusion temperature of the planetary extruder is set at 178°C;

[0103] 5) Filter the plasticized material of the planetary extruder through a fi...

example 3

[0118]

[0119] Set the electronic scale according to the above formula and start measuring. After completion, polyvinyl chloride, diisononyl phthalate (DINP) and liquid barium zinc stabilizer are discharged into the high mixer in sequence;

[0120] 2) Perform high-speed mixing. After mixing for 120 seconds, add processing aids and pigments in turn. The total mixing time is 450 seconds;

[0121] 3) Perform cooling and stirring, discharge the high-speed mixed materials into the mixer for cooling and stirring, and lower the temperature by feeding circulating cooling water into the mixer until the temperature drops below 80°C, and discharge them into the storage tank.

[0122] 4) The material in the storage barrel is conveyed to the planetary extruder for plasticization through the screw conveyor, and the extrusion temperature of the planetary extruder is set at 175°C;

[0123] 5) Filter the plasticized material of the planetary extruder through a filter, using four-layer stai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacture method of an environment-friendly low-toxicity white-light gluing crystal board. The formula of the crystal board comprises the following components: 100 polrvinyl chloride, 40-60 diisononyl ortho-phthalate, 1.8-2.5 liquid Ba-Zn stabilizer, 0.3-0.6 acrylic acid processing aid, 0.05-0.08 pigment and 0.3-0.6 PHR nontoxic phosphate. The process comprises the following working procedures of automatically metering; mixing at a high speed; stirring by cooling; plasticizing by using a planet extruder; filtering; four-roll calendaring; calendaring and cooling; bait reusing; calendaring and winding; gluing and feeding; gluing, preheating and gluing; gluing, cooling and cutting edge; gluing and winding; and packing and put finished products in storage. The invention accords with the REACH regulatory requirements and has short process flow, less material plasticizing and processing time and high production efficiency. The environment-friendly low-toxicity white-light gluing crystal board has superior elasticity to glass, high surface transparency and brightness, good surface planeness and small water wave; in addition, a single gluing film is approximate to be colorless, has high transparency and has the characteristics of glass.

Description

technical field [0001] The invention belongs to a polyvinyl chloride calendered and laminated crystal plate, in particular to an environmentally friendly low-toxicity white light laminated crystal plate that meets the requirements of REACH regulations, is similar to glass, has small water marks, and can achieve white, transparent and bright appearance effects and its production method. Background technique [0002] Polyvinyl chloride (hereinafter referred to as PVC) resin is a kind of strong polar polymer, and its intermolecular force is large, which leads to higher softening temperature and melting temperature of PVC resin, and generally requires 160-210°C to process. In addition, the substituted chlorine groups contained in the molecular structure of PVC can easily lead to the dehydrochlorination reaction of PVC resin, thereby causing the degradation reaction of PVC. PVC is extremely unstable to heat, and the temperature rise will greatly promote the dehydrochlorination re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08K5/12C08K5/521B29C47/92B29C43/58B29C43/24B29C48/92
Inventor 张明奇苗启军
Owner TIANJIN HONGMAO PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products