Furniture ABS resin sealing strip

An ABS resin and edge banding technology, applied in furniture parts, home appliances, furniture accessories, etc., can solve the problems of environmental hazards, poor heat resistance, etc., to improve heat resistance, improve heat resistance and service life , Improve the effect of trimming effect

Active Publication Date: 2011-09-14
东莞市华富立装饰建材有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the polyvinyl chloride in this technical formula is used as the main resin material, and its heat resistance is poor. The resin contains chlorine, and its degradation will cause certain harm to the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Furniture ABS resin sealing strip
  • Furniture ABS resin sealing strip
  • Furniture ABS resin sealing strip

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] An ABS resin furniture edge banding is composed of the following raw materials in parts by weight:

[0036] ABS resin 2000 parts

[0037] CCR nano-scale active calcium carbonate 500 parts

[0038] MBS resin 250 parts

[0039] 80 parts of internal lubricant

[0040] 6 parts of octadecyl β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate

[0041] 8 parts of ethyl benzotriazole

[0042] Polyethylene wax 4 parts

[0043] 15 parts of toner;

[0044] Its production steps are:

[0045] A. According to the above formula, ABS resin, CCR nano-scale active calcium carbonate, MBS resin, internal lubricant, β-(3,5-di-tert-butyl-4-hydroxyphenyl) octadecyl propionate, ethyl-phenylpropanoid Triazole, polyethylene wax, and toner are mixed and banburyed in a high-low temperature dispersion mixer to obtain a uniformly stirred mixture;

[0046] B, above-mentioned mixture is put into granulation in twin-screw granulator;

[0047] C. After granulation, extrude the granules in an ABS sp...

Embodiment 2

[0050] An ABS resin furniture edge banding is composed of the following raw materials in parts by weight:

[0051] ABS resin 2500 parts

[0052] CCR nano-scale active calcium carbonate 500 parts

[0053] MBS resin 300 parts

[0054] Internal lubricant 100 parts

[0055] 7 parts of octadecyl β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate

[0056] Benzenetriazole 10 parts

[0057] Polyethylene wax 5 parts

[0058] 20 parts of toner;

[0059] Its production steps are:

[0060] A. According to the above formula, ABS resin, CCR nano-scale active calcium carbonate, MBS resin, internal lubricant, β-(3,5-di-tert-butyl-4-hydroxyphenyl) octadecyl propionate, ethyl-phenylpropanoid Triazole, polyethylene wax, and toner are mixed and banburyed in a high-low temperature dispersion mixer to obtain a uniformly stirred mixture;

[0061] B, above-mentioned mixture is put into granulation in twin-screw granulator;

[0062] C. After granulation, put the granules into an ABS special extr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of composite materials, in particular to a furniture ABS resin sealing strip. The product of the invention comprises the following components in part by weight: 2,000 to 2,500 parts of ABS resins, 500 to 600 parts of CCR nanometer active calcium carbonate, 250 to 300 parts of MBS resin, 80 to 120 parts of internal lubricant, 6 to 8 parts of antioxidant, 8 to 11 parts of ultraviolet absorber, 4 to 6 parts of dispersant and 10-30 parts of pigment. The ABS resin is applied to the furniture sealing strip instead of PVC, effectively improves the heat tolerance and the edge trimming effect of the furniture sealing strip to further improve the heat resistance of furniture and the service life of the furniture; and at the same time, the ABS resin contains no chlorides, so that the degradation of the ABS resin does not produce adverse effect on the environment and the ABS resin sealing strip has the advantages of safety and environmental protection.

Description

Technical field: [0001] The invention relates to the technical field of composite materials, in particular to an ABS resin furniture edge banding. Background technique: [0002] The edge bands commonly used in home decoration are generally divided into log edge bands and traditional polyvinyl chloride (PVC) edge bands. The log edge bands are simple to make, but the cost is expensive. In order to protect forest resources, countries limit the felling of trees, which limits the source of raw wood edge banding; for this reason, people think of using PVC instead of log skin as the main raw material for making edge banding; but the heat resistance of PVC is poor, The chlorine element in PVC has certain harm to the environment and cannot meet the requirements of high-end furniture on heat resistance, environmental protection and safety. [0003] Chinese patent application number: 200810028245.X, patent name: a formula for environmental protection edge banding, the formula contains...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L55/02C08L51/00C08K13/02C08K3/26C08K5/134C08K5/3475A47B95/04
Inventor 谭洪汝谢志昆
Owner 东莞市华富立装饰建材有限公司