One-step spinning and winding combined manufacturing process for 24-head/position multi-heterogeneous hybrid yarn composite fiber

A composite fiber and manufacturing process technology, applied in fiber processing, spinneret assemblies, textiles and papermaking, etc., can solve the problems of production process growth, spinneret heat reduction, melt flow reduction, etc., and achieve product quality The effect of stably improving, reducing melt degradation, and increasing melt flow

Active Publication Date: 2010-09-08
XUZHOU SILK FIBER TECH
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. Low production efficiency: the compound speed of the two-step method is only about 800m / min;
[0004] 2. High production cost: the two-step method is that two kinds of fibers are spun separately, wound and then compounded in the subsequent process. The production process increases, the equipment investment increases, the floor area is large, the workshop is large, the labor cost is high, and the raw material consumption Large, long production cycle, increased working capital occupation, and low premium product rate;
[0005] 3. Unstable quality: the two-step production process is long, with many control points and many influencing factors, which is not easy to control;
[0006] 4. The product grade is low; the length and weight cannot be fixed
[0007] 5. The production variety is limited: especially the fine-denier silk products whose demand is gradually increasing in the market cannot be produced at all, and the demand for fine silk products is showing a trend of gradually increasing
If the entire production line produces 75dt products, the utilization rate of main equipment is low and the surplus capacity is large, and the cost of production and management per unit product is directly affected due to the decrease in daily output, power consumption, labor costs, equipment depreciation costs, etc.; followed by There is a decrease in the flow rate of the melt, an increase in the residence time of the melt in the conveying pipeline, an increase in the degradation of the melt, and a decrease in the heat brought to the spinneret, which reduces the temperature of the spinneret plate, resulting in floating, End breakage and hole plugging increase, resulting in unstable production, reduced full roll rate, and increased consumption of slices, paper tubes, power, accessories, etc.
It is more difficult to produce products with finer deniers, which affects product quality and production efficiency, and ultimately affects the company's interests

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-step spinning and winding combined manufacturing process for 24-head/position multi-heterogeneous hybrid yarn composite fiber
  • One-step spinning and winding combined manufacturing process for 24-head/position multi-heterogeneous hybrid yarn composite fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0032] Embodiment: A spinning and winding joint manufacturing process of 24 ends / position multi-differential mixed fiber composite fibers in one step is carried out according to the following process steps:

[0033] ①. Material preparation: Put the sliced ​​raw materials into the vibrating screening equipment for screening, screen out the powder and particles with inconsistent particle sizes, and obtain the sliced ​​raw materials that meet the requirements, and then transport the sliced ​​raw materials to the silo for standby;

[0034] ②, crystallization and drying: the slices in the silo are sent to the pre-crystallization bed for crystallization, and then the crystallized slices are transported to the slice drying tower for drying to remove the moisture in the slices;

[0035] ③ Melting and filtering: Send the dried slices into the extruder to heat and melt into a melt, and then transport the melt to a melt filter for filtration to remove impurities in the melt;

[0036] ④ M...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a one-step spinning and winding combined manufacturing process for 24-head / position multi-heterogeneous hybrid yarn composite fiber. The process comprises the steps of material preparation, crystallization and drying, melting and filtering, melt distribution, spinning of pre-oriented yarns and fully-drawn yarns, oiling, pre-meshing of the fully-drawn yarns, drawing and sizing of the fully-drawn yarns, composite meshing and winding (fixed length and fixed weight) in turn. The process fully utilizes and reforms the existing spinning and winding equipment to integrate spinning and winding at one time, and can produce 24 spinning cakes with fixed length and fixed weight at each position simultaneously so as to improve the production efficiency and economic benefit; and the produced multi-heterogeneous hybrid yarn composite fiber has high quality.

Description

technical field [0001] The invention relates to a one-step 24 heads / position multi-different mixed fiber composite fiber spinning and winding combined manufacturing process. Especially the joint manufacturing of multi-differential mixed fiber composite fibers that can complete spinning, web-connected compounding and winding of several different fiber raw materials in one step, and each spinning and winding can produce 24 fixed-length and fixed-weight silk cakes at the same time method. Background technique [0002] Due to production technology reasons, domestic manufacturers generally adopt a two-step method to produce multi-differential mixed fiber composite fibers. The number of spinning and winding heads of this production method is mostly 6 heads / bit, 8 heads / bit, and the most is 12. Head / bit is a common conventional spinning and winding technology, through the separate spinning of pre-oriented yarn (POY) and fully drawn yarn (FDY), winding and then unwinding and net pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D02G3/38D01D1/00D01D1/10D01D4/06D01D5/08D01D5/096D01D4/02D02J1/08
Inventor 孙德荣蒋士成朱建平
Owner XUZHOU SILK FIBER TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products