Greasing agent for improving strength of leather and preparation method thereof

A fatliquoring agent and strength technology, applied in the field of leather strength fatliquoring agent and its preparation, can solve the problems such as the inability to achieve the tear resistance of leather, and achieve good adsorption and adsorption capacity, stable product quality and low cost. Effect

Inactive Publication Date: 2010-09-15
SHANGHAI SINOFRA FINE CHEM
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Chinese patent application No. 88106317 discloses the preparation of fatty acid amido sodium carboxylate composite leather fatliquoring agent, which is mainly composed of fatty acid amido sodium carboxylate compounded with sulfated lard, chlorinated paraffin, ammonium alkylsulfonate Composition, the patent claims that the composite fatliquoring agent has good effect and good filling performance, but it cannot achieve the purpose of obviously improving the tear resistance of leather

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Formula: (parts by weight)

[0025] Polyoxyethylene alkyl phosphate 100

[0026] Fish oil amide 200

[0027] Chlorinated paraffin 50

[0028] Sodium carboxymethyl cellulose 5

[0029] Sodium alkyl sulfonate 100

[0030] Olive Oil PEG 500

[0031] Chlorinated paraffin is 52# chlorinated paraffin;

[0032] The average molecular weight of olive oil polyethylene glycol ester is 2000;

[0033] Sodium alkylsulfonate is sodium dodecylsulfonate.

[0034] Preparation:

[0035] (1) Mix polyoxyethylene alkyl phosphate and fish oil amide evenly at 40°C;

[0036] (2) Mix chlorinated paraffin and olive oil polyethylene glycol ester uniformly at 50°C;

[0037] (3) Add the mixture obtained in step (1) to the mixture obtained in step (2), stir evenly at 50°C, then heat up to 50°C, add sodium carboxymethylcellulose and sodium alkylsulfonate Stir evenly to get the product. Appearance is yellow or white emulsion, pH value is 5.5.

[0038] According to the following process, the...

Embodiment 2

[0045] Formula: (parts by weight)

[0046] Fish oil amide 150

[0047] Chlorinated paraffin 100

[0048] Sodium carboxymethyl cellulose 5

[0049] Sodium alkyl sulfonate 40

[0050] 30# engine oil 450

[0051] Chlorinated paraffin is 52# chlorinated paraffin;

[0052] The sodium alkylsulfonate is a mixture of sodium dodecylsulfonate and sodium octadecylsulfonate with a weight ratio of 1:1.

[0053] The preparation method is:

[0054] (1) Heating fish oil amide to 45°C;

[0055] (2) Mix chlorinated paraffin and 30# engine oil evenly at 55°C;

[0056] (3) Add the mixture obtained in step (1) to the mixture obtained in step (2), stir evenly at 55°C, then heat up to 60°C, add sodium carboxymethylcellulose and sodium alkylsulfonate Stir evenly to get the product. Appearance is yellow or white emulsion, PH 6.0.

[0057] Example two products are tested according to the following process, and the test adopts sheepskin:

[0058] %(W / W)

Weight (g)

chemicals ...

Embodiment 3

[0064] Formula: (parts by weight)

[0065] Polyoxyethylene alkyl phosphate 100

[0066] Fish oil amide 180

[0067] Chlorinated paraffin 50

[0068] Sodium Carboxymethyl Cellulose 1

[0069] Sodium alkyl sulfonate 150

[0070] Olive Oil PEG 500

[0071] 30# engine oil 450

[0072] The average molecular weight of olive oil polyethylene glycol ester is 2000;

[0073] Chlorinated paraffin is 52# chlorinated paraffin;

[0074] The sodium alkylsulfonate is a mixture of sodium dodecylsulfonate and sodium octadecylsulfonate with a weight ratio of 1:1.

[0075] The preparation method is:

[0076] (1) Mix polyoxyethylene alkyl phosphate and fish oil amide evenly at 40°C;

[0077] (2) Mix chlorinated paraffin, olive oil polyethylene glycol ester and 30# engine oil at 55°C;

[0078] (3) Add the mixture obtained in step (1) to the mixture obtained in step (2), stir evenly at 55°C, then heat up to 60°C, add sodium carboxymethylcellulose and sodium alkylsulfonate Stir evenly to g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a greasing agent for improving strength of leather and a preparation method thereof. The greasing agent comprises the following components in part by weight: 0 to 100 parts of polyoxyethylene alkyl phosphate, 150 to 200 parts of fish oil amide, 50 to 100 parts of chlorinated paraffin, 1 to 5 parts of sodium carboxymethylcellulose, 40 to 150 parts of alkyl sodium sulfonate, 0 to 500 parts of olive oil polyethylene glycol ester and 0 to 450 parts of No.30 engine oil. The greasing agent has the advantage of obviously improving the strength of the leather, namely the tear resistance of the leather so that the leather after greasing treatment has smoothness and softness, strong silk feeling, stable quality, low cost and good permeability, absorption and absorption amount.

Description

technical field [0001] The invention relates to a fatliquoring agent for leather strength and its preparation. technical background [0002] With the development of leather technology level, the strength of leather, that is, the tear resistance has become an important index to measure the quality of leather. [0003] In the process of processing natural animal skin into leather, the high-grade leather fatliquoring agent should have the softness and toughness of the leather, the fullness and elasticity of the leather, the smoothness of silk fabric, and not dry and hard with the change of climate and time. performance. [0004] Chinese patent application No. 88106317 discloses the preparation of fatty acid amido sodium carboxylate composite leather fatliquoring agent, which is mainly composed of fatty acid amido sodium carboxylate compounded with sulfated lard, chlorinated paraffin, ammonium alkylsulfonate Composition, the patent claims that the composite fatliquoring agent ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C14C9/02
Inventor 郑善强宋林
Owner SHANGHAI SINOFRA FINE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com