Waterborne wood paint

A technology of water-based wood paint and water-based dispersion, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of not being generally recognized by users, poor hardness, and poor wear resistance, and achieve a plump and beautiful paint film. Good defoaming, good leveling effect

Active Publication Date: 2010-09-22
广东大中三联科技有限公司
View PDF4 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there are some water-based wood products developed by some manufacturers on the market, but these products are not gen

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The water-based wood lacquer in the present embodiment comprises the following components, and the percentage by weight of each component is: the polyurethane water-based dispersion adopts the product of the American ALBERDINGK company, the model is CUR99, and its content is 81.2%. Nano-silicon carbide is a product of Qinhuangdao Taiji Ring Nano Products Co., Ltd., and its content is 3.2%. Polyethylene water-based wax liquid is the product of Weng Kaier Company, and its content is 2.5%. The film-forming aid is Texanol from Eastman Company of the United States, and its consumption is 5%. Dispersant, leveling agent, wetting agent and defoamer are all products of Tego, Germany. The dosage is 0.4% of dispersant, 0.2% of leveling agent, 0.3% of wetting agent, 0.5% of The agent is Kathon LXE of Rohm and Haas, the dosage is 0.3%, the pH regulator is AMP-95 of Dow, the dosage is 0.1%, the thickener is the product of Aksu, the dosage is 1.2%, and the dosage of water is 5.1% %....

Embodiment 2

[0049] Waterborne wood lacquer in the present embodiment, the difference with embodiment is: the weight percent of each component is:

[0050] Polyurethane aqueous dispersion 88%;

[0051] Water 5.6%;

[0052] Dispersant 0.20%;

[0053] Wetting agent 0.20%;

[0054] Leveling agent 0.10%;

[0055] Defoamer 0.20%;

[0056] Nano silicon carbide 2%;

[0057] Polyethylene water-based wax liquid 1%;

[0058] Fungicide 0.10%;

[0059] Thickener 0.5%;

[0060] Coalescing aid 2%;

[0061] PH regulator 0.10%.

[0062] The preparation method of water-based wood lacquer comprises the following operations in sequence:

[0063]1) Prepare the raw materials according to the set weight percentage, put the dispersant, wetting agent, water and 50% defoamer into the high-speed stirring container, and add the thickener while stirring at high speed, until the thickener is completely dispersed Finally, add nano-silicon carbide and disperse at a high speed until the fineness of the scraper...

Embodiment 3

[0071] Waterborne wood lacquer in the present embodiment, the difference with embodiment is: the weight percent of each component is:

[0072] Polyurethane aqueous dispersion 86%;

[0073] water 5%;

[0074] Dispersant 0.50%;

[0075] Wetting agent 0.50%;

[0076] Leveling agent 0.50%;

[0077] Defoamer 0.50%;

[0078] Nano silicon carbide 3%;

[0079] Polyethylene water-based wax liquid 1%;

[0080] Fungicide 0.30%;

[0081] Thickener 0.60%;

[0082] Coalescing aid 2%;

[0083] PH regulator 0.10%.

[0084] The preparation method of water-based wood lacquer comprises the following operations in sequence:

[0085] 1) Prepare the raw materials according to the set weight percentage, put the dispersant, wetting agent, water and 50% defoamer into the high-speed stirring container, and add the thickener while stirring at high speed, until the thickener is completely dispersed Finally, add nano-silicon carbide and disperse at a high speed until the fineness of the scraper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides waterborne wood paint, which comprises the following components in percentage by weight: 72 to 88 percent of polyurethane waterborne dispersion, 5 to 10 percent of water, 0.20 to 0.80 percent of dispersant, 0.20 to 0.80 percent of wetting agent, 0.10 to 0.60 percent of leveling agent, 0.20 to 0.80 percent of defoamer, 2 to 5 percent of nanometer silicon carbide, 1 to 4 percent of polyethylene waterborne wax liquid, 0.10 to 0.50 percent of fungicide, 0.5 to 3 percent of thickener, 2 to 6 percent of film-forming additive and 0.10 to 0.50 percent of pH regulator. The invention also provides a method for preparing the waterborne wood paint. In contrast to the prior art, the paint has the advantages that paint film hardness and wear resistance are greatly improved, and the wear resistance is close to the level of oil paint, so that the common problem that waterborne paint is difficult to defoam is solved. The paint also has the characteristics of good leveling property, plump attractive paint film, easy construction and the like.

Description

technical field [0001] The invention relates to a water-based paint, in particular to a water-based wood paint which is dried at normal temperature and used on the surface of wooden products, and has high hardness and high wear resistance. Background technique [0002] Environmental protection and energy are two major challenges we face in the 21st century. In order to meet this challenge, the coatings industry is gradually shifting from traditional varieties with high pollution, high energy consumption, and extreme dependence on petroleum industry products to environmentally friendly and resource-saving products such as water-based coatings, radiation-cured coatings, powder coatings, and high-solid content coatings. . The increasingly stringent laws and regulations in various countries have accelerated the pace of replacing solvent-based coatings with water-based coatings. [0003] my country is a major producer of paint in the world, and it is also the largest producer a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/04C09D7/12
Inventor 杨伟平
Owner 广东大中三联科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap